Comporison Sduty of Microstructure by Metallographicalk on the Polarized Lightand Texture by XRD of CC 5083 and CC 5182 Aluminium Alloy after Cold Rolling and Recrystallization |
CHEN Ming-biao1,2, LI Yong-wei1, TAN Yuan-biao2, MA Min2, WANG Xue-min2, LIU Wen-chang2 |
1. College of Mechanical Engineering, Qinghai University, Xining 810016, China 2. Key Laboratory of Metstable Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China |
|
|
Abstract At present the study of relation between microstructure ,texture and performanceof CC 5083 aluminium alloy after cold tolling and recrystallization processes is still finitude. So that the use of the CC 5083 aluminium alloy be influenced. Be cased into electrical furnace, hot up with unlimited speed followed the furnace hot up to different temperature and annealed 2h respectively, and be casedinto salt-beth furnace, hot up quickly to different temperature and annealed30min respectively for CC 5083 and CC 5182 aluminum alloy after cold roling with 91.5% reduction. The microstructure be watched use metallographic microscope, the texture be inspected by XRD. The start temperature of recrystallization and grain grow up temperature within annealing in the electric furnace of CC 5083aluminum alloy board is 343 ℃, and the shap of grain after grow up with long strip (the innovation point ); The start temperature of recrystallization within annealling in the salt bath furnace of CC 5083 is 343 ℃. The start temperatureand end temperature of recrystallization within annealling of CC 5083 and CC 5182 aluminum alloy is 371 ℃. The grain grow up outstanding of cold rooled CC 5152 aluminum alloy after annealed with 454 ℃ in the electric furnace and salt bath furnace. The start temperature of grain grow up of CC 5083 alluminum alloy annealed in the electric furnace and salt bath furnace respectively is higherthan the start temperature of grain grow up of CC 5182 alluminum alloy annealed in the electric furnace and salt bath furnace respectively. The strat temperature of recrystallization grain grow up is higher than which annealled with other three manner annealing process. The recrystallization temperature of CC 5182 annealed in the salt bath furnace is higher than which annealed in the electric furnace. The recrystallization temperature of the surface layer of CC 5083 and CC 5182 aluminum alloy is higher than the inner layer (the innovation point). Thereis a difference each other of the structure and the texture of the four manner annealing aluminum alloy (the innovation point). There is a little difference at the recrystallization processes course reflectived by the observe results of structure transform and by the examination results of texture transmission.
|
Received: 2014-04-04
Accepted: 2014-07-04
|
|
Corresponding Authors:
CHEN Ming-biao
E-mail: chenmingbiaozyx@126.com
|
|
[1] Li J, Liu W C, Zhai T, et al. Scripta Materialia, 2005, 52(3): 163. [2] Liu W C, Morris J G. Materials Science and Engineering A, 2003, 339(1-2): 183. [3] Liu W C, Yuan H, Huang M J, et al. Materials Science and Engineering A, 2009, 524(1-2): 168. [4] Zhao Y M, Liu W C, Morris J G. Metallurgical and MaterialsTransactions A, 2004 35 (11): 3613. [5] Engler O. Metallurgical and Materials Transactions A, 1999, 30 (6): 1517. [6] Liu W C, Morris J G. Metallurgical and Materials Transactions A, 2005, 36(10): 2829. [7] ZHAO Xin, JING Tian-fu, GAO Yu-wei, et al(赵 新,荆天辅, 高聿为, 等). J. of Iron and Steel Reseach(钢铁研究学报), 2004, 16(6): 69. [8] Liu W C, Radhakrishnan B. Materials Letters, 2010, 64 (16): 1829. [9] Wells M A, Lloyd D J, Samarasekera I V, et al. Metallurgical and Materials Transactions B, 1998, 29 (3): 621. [10] Liu W C, Zhai T, Man C S, et al. Philosophical Magazine, 2004,84(31): 3305-3321. |
[1] |
SUN Wei-ji1, LIU Lang1, 2*, HOU Dong-zhuang3, QIU Hua-fu1, 2, TU Bing-bing4, XIN Jie1. Experimental Study on Physicochemical Properties and Hydration Activity of Modified Magnesium Slag[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3877-3884. |
[2] |
LIU Pan1, 2, 3, DU Mi-fang1*, LI Bin1, LI Jing-bin1, ZENG Lei1, LIU Guo-yuan1, ZHANG Xin-yao1, 4, ZHA Xiao-qin1, 4. Determination of Trace Tellurium Content in Aluminium Alloy by
Inductively Coupled Plasma-Atomic Emission Spectrometry Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3125-3131. |
[3] |
ZHU Yu-qi1, 2, ZHANG Xin2, DU Pan-pan2, LIU Shu1, ZHANG Gui-xin1, 2, GUAN Song-lei2*, ZHENG Zhong1*. Infrared Spectroscopy and X-Ray Spectroscopy Combined With
Inductively Coupled Plasma Mass Spectrometry for Quality
Control of Mongolian Medicine Yu Grain Soil[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3163-3169. |
[4] |
WANG Yu-chen1, 2, KONG Ling-qin1, 2, 3*, ZHAO Yue-jin1, 2, 3, DONG Li-quan1, 2, 3*, LIU Ming1, 2, 3, HUI Mei1, 2. Hyperspectral Reconstruction From RGB Images for Tissue Oxygen
Saturation Assessment[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3193-3201. |
[5] |
LI Yu-tang1, WANG Lin-zhu1, 2*, LI Xiang3, WANG Jun1. Characterization and Comparative Analysis of Non-Metallic Inclusions in Zirconium Deoxidized Steel[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(09): 2916-2921. |
[6] |
ZHANG Zhi-fen1, LIU Zi-min1, QIN Rui1, LI Geng1, WEN Guang-rui1, HE Wei-feng2. Real-Time Detection of Protective Coating Damage During Laser Shock Peening Based on ReliefF Feature Weight Fusion[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2437-2445. |
[7] |
GAO Ya1, LIAO Cui-ping1, ALATAN Chaolumen2, CHEN Jian-bo3, TU Ya4*. X-Ray Diffraction and Infrared Spectral Analysis of the Differential Chemical Indicators Between the Raw and Milk-Processed Corals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2494-2499. |
[8] |
XU Ming-kun, LIN Jia-xiang, ZHANG Xiao-lin, LI Zhen-yin, WANG Ya-ming, LIU Chun-tai, SHEN Chang-yu, SHAO Chun-guang*. In Situ Detection of Structural Evolution of Isotropic Polypropylene Crystals During Uniaxial Stretching by Two-Dimensional X-Ray Diffraction Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1426-1433. |
[9] |
SHI Zhi-feng1, 2, LIU Jia2, XIAO Juan2, ZHENG Zhi-wen1*. Investigation of Novel Method for Detecting Vanillin Based on X-Ray Diffraction Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1563-1568. |
[10] |
WANG Mei-li1, 2, SHI Guang-hai2*, ZHANG Xiao-hui1, YANG Ze-yu2, 3, XING Ying-mei1. Experimental Study on High-Temperature Phase Transformation of Calcite[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(04): 1205-1211. |
[11] |
SHAO Jin-fa1, LI Rong-wu2, PAN Qiu-li1, CHENG Lin1*. The Study of Non-Destructive Analysis of Tang Sancai Firing Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 781-787. |
[12] |
ZHANG Dian1, WANG Hui1, CHEN Yin-wei2, 3, WANG Ju-lin2, 3*. Identification and Influence of Color Components in Red Lime From the Roof of Yangxin Hall in the Palace Museum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 877-882. |
[13] |
ZHANG Yan1, 2, WANG Hui-le1, LIU Zhong2, ZHAO Hui-fang1, YU Ying-ying1, LI Jing1, TONG Xin1. Spectral Analysis of Liquefaction Residue From Corn Stalk Polyhydric
Alcohols Liquefaction at Ambient Pressure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 911-916. |
[14] |
LIU Jin, FU Run-juan, HAN Tong-shuai*, LIU Rong, SUN Di. Spectral Analysis of Human Tissues Based on a Direct Effective
Attenuation Coefficient Measurement[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(09): 2746-2751. |
[15] |
FAN Qing-jie, SONG Yan, LAI Shi-quan*, YUE Li, ZHU Ya-ming, ZHAO Xue-fei. XRD Structural Analysis of Raw Material Used as Coal-Based Needle Coke in the Coking Process[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(06): 1979-1984. |
|
|
|
|