纳米Ce1-4x(FeAlCoLa)xO2-δ固溶体微观光谱特征及氧化还原性能研究

doi:10.3964/j.issn.1000-0593(2024)07-1883-06

Abstract
References
Related Citation (15)

Download: PDF (8065 KB)
Export: BibTeX | EndNote (RIS)

Abstract Hydrothermal method was used to synthesize nanosized Fe³⁺, Al³⁺, Co²⁺, and La³⁺ co-doped Ce_1-4x(FeAlCoLa)_xO_2-δ(x=0.00~0.05) solid solutions. The solid solutions' microstructure, morphology, spectral characteristics, and redox activities were systematically characterized and analyzed by XRD, TEM, SEM, UV, PL, Raman, and temperature-programmed reduction (TPR) with H₂. XRD results showed the Ce_1-4x(FeAlCoLa)_xO_2-δ solid solutionsexhibited the CeO₂ cubic fluorite structure. A tiny diffraction peak corresponding to the Co₃O₄ impurity phase at 36.6° was observed when the doped content reached x=0.04, indicating that x=0.04 was the solid solubility of doped ions in the CeO₂ lattice. The positions of the (111) diffraction peaks were shifted towards a higher angle, which proved the doped ionsinduced the distortion of the lattice. The TEM and SEM images showed the samples were spherical with high crystallinity, and doping caused lattice contraction. The UV absorption spectra revealed that the doped samples' absorption edges were gradually red-shifted compared to pure CeO₂. Extra absorption peaks corresponding to the doped ions were found in the region of 560~780 nm. The band gap energies decreased from 2.84 eV (pure CeO₂) to 2.1 eV (x=0.05). The reasoncould be that the doped ions formed new impurity energy levels between the valence and conduction bands, which allowed the electrons to transition from the valence band to the lower impurity energy levels and then lowered the band gap energies. In addition, the distortion of the lattice and increased concentration of oxygen vacancies prevented the electrons from transferring to higher energies, which can also result in the reduction of band gap energies. PL spectra showed that doping significantly reduced the emission peak intensities. Raman spectra demonstrated that the dopingresulted in the shift of the F_2g peak, the decrease of peak intensities, and the widening of peaks. Meanwhile, the relative intensities of the peak corresponding to the oxygen vacancies were also observed to be enhanced. Thus, both the PL and Raman spectra proved that doping increased the degree of lattice distortion and the concentration of oxygen vacancies. The H₂-TPR test results showed that doping can effectively reduce the redox reaction temperatures and improve the redox activities. The sample doped with x=0.03 possess the lowest surface reduction temperature and the largest peak areas, which meansthis sample exhibited the best redox activities. It can be concluded that the redox performances of the samples were closely related to the grain sizes, lattice defects, and oxygen vacancy concentrations. This study showed that the four ions co-doped with CeO₂ could effectively modify the microstructure and improve the samples' catalytic activities at a low doping concentration.

Key words：Nanosized Ce_1-4x(FeAlCoLa)_xO_2-δ solid solutions; Co-doped; Oxygen vacancy; Redox activity

Received: 2023-05-07 Accepted: 2023-09-09

ZTFLH:

O611.4

Corresponding Authors: ZHANG Guo-fang E-mail: afang1001@126.com

Cite this article:

SUN Shi-long,ZHANG Guo-fang,SHU Jun, et al. Microscopic Spectral Characteristics and Redox Properties of Nanosized Ce_1-4x(FeAlCoLa)_xO_2-δ Solid Solutions[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(07): 1883-1888.

URL:

https://www.gpxygpfx.com/EN/10.3964/j.issn.1000-0593(2024)07-1883-06 OR https://www.gpxygpfx.com/EN/Y2024/V44/I07/1883

[1] Matussiin S N, Harunsani M H, Khan M M. Journal of Rare Earths, 2023, 41(2): 167.
[2] Liu Y, Wang M, Shen M, et al. Journal of Inorganic Materials, 2021, 36(1): 88.
[3] Zhang G F, Li Y M, Hou Z H, et al. Journal of Solid State Chemistry, 2018, 264: 148.
[4] Wang Z, Jiang S, Li Y, et al. Sci. China Mater., 2017, 60: 646.
[5] Zhang G F, Li Y M, Zhao X, et al. Journal of Rare Earths, 2020, 38(3): 241.
[6] Killivalavan G, Sathyaseelan B, Kavitha G, et al. MRS Advances, 2020, 5: 2503.
[7] Lee J, Lee M W, Kim M J, et al. Journal of Hazardous Materials, 2021, 414: 125523.
[8] CAI Ji-jun, CUI Wang-jun, LI Bing, et al（蔡济钧，崔王君，李冰，等）. Electrochemistry（电化学）, 2015, 21(2): 145.
[9] SU Jun, LU Wen-lin, ZHANG Guo-fang, et al（束俊，陆旻琳，张国芳，等）. Materials and Chemical Engineering（材料工程），2023, 51(3): 138.
[10] Mao X, Xia X, Li J, et al. Journal of Materials Engineering and Performance, 2021, 30: 3795.
[11] Zhang G, Li Y, Zhao X, et al. Journal of Rare Earths, 2020, 38(3): 241.
[12] ZHU Hong-qiu, ZHOU Tao, LI Yong-gang, et al（朱红求，周涛，李勇刚，等）. Analytical Chemistry(分析化学), 2019, 47(4): 576.
[13] Kumar M P, Suganya J A, Sivasamy A, et al. Journal of Molecular Liquids, 2017, 242: 789.
[14] Wang W, Zhu Q, Dai Q G, et al. Chemical Engineering Journal, 2017, 307: 1037.
[15] WANG Xiang, LI Mei-jun, WU Zi-li（王翔，李美俊，吴自力）. Chinese Journal of Catalysis，2021，42(12)：2122.
[16] Singh K, Kumar R, Chowdhury A. Journal of Materials Science, 2016, 51: 4134.
[17] Li J, Lu G Z, Wu G S. Catalysis Science & Technology, 2014, 4(5): 1268.
[18] Li P, Chen X Y, Li Y D, et al. Catalysis Today, 2019, 327: 90.
[19] TU Zi-qiang, HE Xuan, DU Xing, et al（涂自强，何漩，杜星，等）. Bulletin of the Chinese Ceramic Society（硅酸盐通报），2023, 21(4)：1.
[20] Zhang J, Guo J, Liu W, et al. European Journal of Inorganic Chemistry, 2015, 6: 969.
[21] HUANG Xiu-bing, WANG Peng, TAO Jin-chang, et al（黄秀兵，王鹏，陶进长，等）. Journal of Inorganic Materials（无机材料学报）, 2020, 35(5)：573.
[22] LI Hong-mei, LAN Li, LIU Da-yu, et al（李红梅，兰丽，刘达玉，等）. Rare Metal Materials and Engineering（稀有金属材料与工程）, 2020, 49(3)：769.