Preparation, Spectral Analysis and Photocatalytic Activities of TiO2 Films Codoped with Iron and Nitrogen |
LIU Wan-bing1, DENG Jian1*, ZHAO Yu-bao1, XU Jin-sheng2, ZHOU Liang1 |
1. School of Chemistry and Chemical Engineering,University of South China,Hengyang 421001, China 2. Hengyang Normal College, Hengyang 421008, China |
|
|
Abstract Using tetrabutyl titanate as the titanium source, and ammonia and ferric nitrate as the sources of nitrogen and ferrum respectively, iron and nitrogen-codoped nano-TiO2 gelatins were prepared by sol-gel method. The iron and nitrogen-codoped nano-TiO2 complex films were prepared with the obtained gelatins used to coat the surface of cleaned glass slides by several times of dipping-lifting procedure, followed by natural seasoning at room temperature and calcined at 450 ℃ for 3 hours, then the films were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), X-ray photoelectron spectrum (XPS) and ultraviolet-visible diffuse reflectance spectrum (UV-Vis). The XRD spectra of samples showed that the Fe-TiO2-xNx films were of anatase structure with a few of oxygen atoms in the lattice of anatase TiO2 substituted by nitrogen atoms, resulting in the distorsion of crystal lattice. The SEM image showed that the nanoparticles of the films have a good dispersion characteristic and uniform orbicular shape with an average diameter of about 19 nm. The absorption edges of UV-Vis spectra exhibited a red shift up to 740 nm when the TiO2 films were codoped with iron and nitrogen. The XPS of the Fe-TiO2-xNx film presented a lowering of Ti 2p3/2 electron binding energy because of the codoping of iron and nitrogen, which then resulted in the widening of the absorption of visible light range. The photocatalytic properties were studied by photocatalytical degradation of sudan Ⅰ as a model reaction in a self-assembled light-reactor. When the atomic ratio of Fe3+/Ti4+ reached 0.4%, the Fe-TiO2-xNx film showed the highest catalytic performance in degradation of sudan Ⅰ which was decomposed by up to 97% after 4 hours of photocatalytic reaction. Codoping of nitrogen and appropriate amount of iron in TiO2 enhances photoresponse and utilizing efficiency in visible light region, and then improves the performances of Fe-TiO2-xNx photocatalyst. The complex film catalyst prepared by this method will have potential application in areas of wastewater disposal.
|
Received: 2008-01-08
Accepted: 2008-04-16
|
|
Corresponding Authors:
DENG Jian
E-mail: lights7622@yahoo.com.cn
|
|
[1] Liu Yan, Sun Dezhi. Applied Catalysis B, Environmental, 2007, 72: 205. [2] Carneiro J O, Teixeira V, Portinha A, et al. Materials Science and Engineering B, 2007, 138: 144. [3] Yang Songwang, Gao Lian. Journal of the American Ceramic Society, 2004, 87(9): 1803. [4] Kuroda Y, Mori T, Yagi K, et al. Langmuir, 2005, 21(17): 8026. [5] ZHENG Huai-li, ZHANG Jun-hua, LI Hong, et al(郑怀礼,张峻华,李 宏, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2005, 25(12): 2065. [6] LIU Bao-shun, HE Xin, ZHAO Xiu-jian, et al(刘保顺,何 鑫,赵修建, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(2): 208. [7] Ohno T, Miyamoto Z, Nishijima K, et al. J. Appl. Catal. A: General, 2006, 302: 62. [8] HUANG Dong-sheng, CHEN Chao-feng, LI Yu-hua, et al(黄东升,陈朝凤,李玉花,等). Chinese Journal of Inorganic Chemistry(无机化学学报),2007, 23(4): 738. [9] Yoshitaka Nakano, Takeshi Morikawa, Takeshi Ohwaki, et al. Appl. Phys. Lett., 2005, 86: 132104. [10] Zhang H, Banfield J F. Phys. Chem. B, 2000, 104(15): 3481. [11] Asahi R, Morikawa T, Ohwaki T, et al. Science, 2001, 293(5528): 269. [12] Ihara T, Miyoshi M, Iriyama Y, et al. Applied Catalysis B, Environmental, 2003, 42(4): 403. [13] Burda C, Lou Y, Chen X, et al. Nano Letters, 2003, 3(8): 1049. [14] Catastini C, Sarakha M, Maihot G, et al. The Science of the Total Envionment, 2002, 298(1-3): 219. [15] Selvam K, Muruganandham M, Muthuvel I, et al. Chemical Engineering Journal, 2007, 128(1): 51. |
[1] |
ZONG Zhi-fang1, XU Wei-cheng2, CHEN De-peng1*, TANG Gang1, ZHOU Xiao-hui1, DONG Wei1, WU Yu-xi2. Preparation Mechanism of Decylic Acid-Palmitic Acid/SiO2@TiO2
Photocatalytic Phase Change Microcapsules Based on
Multiple Spectrum Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(04): 1306-1313. |
[2] |
QI Dong-li, CHENG Jia, SUN Hui, ZHANG Rui-xin, SONG Jian-yu, QIN Yan-li, LI Hong-da, SHEN Long-hai*. Research on Spectral Characteristics and Photocatalytic Properties of Ball Milled TiO2[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3063-3067. |
[3] |
ZHANG Li-sheng. Photocatalytic Properties Based on Graphene Substrate[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(04): 1058-1063. |
[4] |
DENG Ya-li1, LI Mei2, WANG Ming2*, HAO Hui1*, XIA Wei1. Surface Plasmon Resonance Gas Sensor Based on Silver/Titanium Dioxide Composite Film[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(03): 743-748. |
[5] |
JIAO Dian, XIAO Si-guo*. Luminescence and Long Afterglow Properties of In3+ and Si4+ Co-Doped ZnBi0.02Ga1.98O4∶Cr3+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(12): 3716-3721. |
[6] |
FENG Ai-ming1, WANG Fu-qiang1, ZHANG Hong1*, AN Peng2, LI Yang-hui1, 3, WANG Le1*. Significantly Improved Luminescence Properties of YAG Phosphor via Localized Surface Plasmon Resonance of Nanotitania[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3081-3085. |
[7] |
JI Bang1,2, ZHAO Wen-feng3, DUAN Jie-li4, FU Lan-hui1, MA Li-zhe3, YANG Zhou1*. Spectral Characteristics of Ag3PO4/GO on Nickel Foam and Photocatalytic Degradation of Ethylene Under Visible Light[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2743-2750. |
[8] |
CHEN Min-nan, TAO Hong*, SONG Xiao-feng, WANG Yi-xin, SHAO Ling, HAN Xiao, LIU Wei, YIN Guang-yi, XIE Xin-yu, YAN Nan-xia. Spectroscopic Analysis of Nitric Acid-Assisted Synthesis of Nitrogen-Defected Graphite Carbon Nitride Materials[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(07): 2159-2163. |
[9] |
RU Ping1, YUAN Cui-fang1, QIAO Hai-xia1, HUANG Yong1, 2*, ZHANG Xue-jiao1, DONG Xin-yu1, Lü Zi-wei1, ZHANG Min1, WANG Yi-rao1, DANG Xian-yang1, CHEN Yun-long1, YANG He-jie3, ZHANG Xiao-jun4, ZHANG Xiao-yun1*. Preparation and Characterization of Bionic Mg-Ag-HA/Gelatin Antibacterial Biocoating Based on FTIR and ICP-MS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(11): 3352-3358. |
[10] |
YANG Lei, LIN Bin-bin, ZHENG Qi-wei, WU Shu-lan, ZHENG Bing-yun, ZHU Zhi-fei, HU Wen-ying. Its Photochemical Recognition to Hg2+ and Preparation of Nitrogen and Sulfur-Codoped Carbon Dots by Sulfanilamide[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(11): 3388-3394. |
[11] |
MA Li-zhe1, JI Bang2, YANG Zhou2*, HUANG Quan-feng1, ZHAO Wen-feng1*. Study of Photocatalytic Degradation of Antibiotics Based on UV-LED Array[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2894-2900. |
[12] |
YE Ping, WU Miao-miao, WEI Ming, YANG Zhen, HAN Qiao-feng*. Preparation, Characterization and Properties of BiOCl1-xIx and BiOBr1-xIx Solid Solution[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(08): 2443-2449. |
[13] |
WANG Lin-na, CHENG Ya-wen, LIU Ke, ZHANG Xiu-ling*. The Stability of Ionic Liquids in DBD Plasma under Atmospheric Pressure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(05): 1372-1376. |
[14] |
LIU Jun-shao1, HUANG Lei2, XIE Wen-ju1, LIN Hao1, CHEN Yi-ping2, PAN Hai-bo2*. Preparation of Four Phenoxy Phthalocyanine Zinc/ZnO Composites with in-situ Method by DBU Liquid Phase Catalyst and Its Photocatalytic Selectivity[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(05): 1486-1491. |
[15] |
XUE Juan-qin1, DAI Ji-zhe2, WANG Zhen-xing1, LI Di1. Spectral Characteristic of Graphene Modified Zinc Stannate Materials and It’s Photocatalytic Properties[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(04): 1219-1224. |
|
|
|
|