Synthesis of La2(MoO4)3∶Eu Magnetically Fluorescent Nanoparticles and Its Application for Latent Fingerprint Development |
YU Ao-yang1, 2, YANG Rui-qin1*, WANG Meng2 |
1. Department of Forensic Science,People’s Public Security University of China, Beijing 100038, China
2. Department of Trance Examination, National Police University of China, Shenyang 110035, China |
|
|
Abstract In this study, fluorescent La2(MoO4)3∶Eu and magnetic Fe3O4 nanomaterials were synthesized by hydrothermal and coprecipitation, respectively. The size, morphology, crystal structure, and fluorescent property of as-synthesized nanomaterials were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) spectroscopy, and fluorescence spectroscopy (FS). The La2(MoO4)3∶Eu fluorescent nanomaterials were flaky in shape, and the crystal structure was tetragonal La2(MoO4)3 phase. The La2(MoO4)3∶Eu fluorescent nanomaterials could emit strong red fluorescence under 254 nm ultraviolet(UV) excitation.While the magnetic Fe3O4 nanomaterials were spherical in shape with an average diameter of about 60 nm, and the crystal structure was cubic Fe3O4 phase. Subsequently, the above two nanomaterials were mixed together in a certain ratio to form the La2(MoO4)3∶Eu/Fe3O4 superparamagnetic fluorescent nanomaterials. The as-prepared La2(MoO4)3∶Eu/Fe3O4 nanomaterials were of sheet structure mixed with spherical particles in shape, which could emit red fluorescence weaker than pureLa2(MoO4)3∶Eu fluorescent nanomaterials under 254 nm ultraviolet excitation. However, the red fluorescence from La2(MoO4)3∶Eu/Fe3O4 nanomaterials could still meet the needs of the fingerprint development. Although the as-prepared nanomaterials and La2(MoO4)3∶Eu fluorescent nanomaterials have same effect in developing fingerprint on smooth object, the as-prepared nanomaterials could form a suitable fringe by using a magnetic applicator to prevent dust pollution and develop the detail features of fingerprint with bright red fluorescence stimulated by the excitation of 254 nm ultraviolet light. Finally, the as-prepared nanomaterials were applied to develop the fresh latent fingerprints on various smooth and rough substrates. The results showed that the latent fingerprints developed by our nanomaterials could appear the detailed features of friction ridges with a high contrast. In addition, the nanomaterials-based fingerprint development also possessed some other advantages, such as low background interference, high developing contrast, wide application range of substrates, and no powder dusting. The as-prepared fluorescent nanomaterials are superparamagnetic fluorescent nanomaterials. The performance of this powder is obviously better than non-magnetic fluorescent nanomaterials. Therefore, the as prepared superparamagnetic fluorescent nanomaterials have been proved to be an ideal material for latent fingerprint development, which have great potential in forensic applications.
|
Received: 2017-01-05
Accepted: 2017-05-12
|
|
Corresponding Authors:
YANG Rui-qin
E-mail: rqyang1971@yahoo.com
|
|
[1] Wang M, Li M, Yu A Y, et al. Adv. Funct. Mater., 2017, 14: 1606243.
[2] Yu A Y, Zhang D, Hu Y F, et al. J. Mater. Sci.: Mater Electron, 2014, 25: 4434.
[3] Wang J, Wei T, Li X Y, et al. Angew. Chem. Int. Ed., 2014, 53: 1616.
[4] Wang M, Li M, Yu A Y, et al. ACS Appl. Mater. Interfaces, 2015, 7: 28110.
[5] Lee J, Chan W L, Kim J M, ACS Appl. Mater. Interfaces, 2016, 8: 6245.
[6] M Saif, M Shebl, ANabeel, et al. Sensor Actuat B-Chem, 2015, 220: 162.
[7] Xiang R,Wang Z Z, Zhang Z J, et al. Chem. Commun., 2016, 52: 557.
[8] P Kumar, R Gupta, R Singh, et al. Forensic Leg. Med., 2015, 32: 64.
[9] WANG Meng(王 猛). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2015, 35(6): 1601.
[10] Lu H Y, Xu C S, Chen H Y, et al. Biomaterials,2016, 90: 27. |
[1] |
LEI Hong-jun1, YANG Guang1, PAN Hong-wei1*, WANG Yi-fei1, YI Jun2, WANG Ke-ke2, WANG Guo-hao2, TONG Wen-bin1, SHI Li-li1. Influence of Hydrochemical Ions on Three-Dimensional Fluorescence
Spectrum of Dissolved Organic Matter in the Water Environment
and the Proposed Classification Pretreatment Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 134-140. |
[2] |
XIA Ming-ming1, 2, LIU Jia3, WU Meng1, 2, FAN Jian-bo1, 2, LIU Xiao-li1, 2, CHEN Ling1, 2, MA Xin-ling1, 2, LI Zhong-pei1, 2, LIU Ming1, 2*. Three Dimensional Fluorescence Characteristics of Soluble Organic Matter From Different Straw Decomposition Products Treated With Calcium Containing Additives[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 118-124. |
[3] |
GU Yi-lu1, 2,PEI Jing-cheng1, 2*,ZHANG Yu-hui1, 2,YIN Xi-yan1, 2,YU Min-da1, 2, LAI Xiao-jing1, 2. Gemological and Spectral Characterization of Yellowish Green Apatite From Mexico[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 181-187. |
[4] |
HAN Xue1, 2, LIU Hai1, 2, LIU Jia-wei3, WU Ming-kai1, 2*. Rapid Identification of Inorganic Elements in Understory Soils in
Different Regions of Guizhou Province by X-Ray
Fluorescence Spectrometry[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 225-229. |
[5] |
LIU Wei1, 2, ZHANG Peng-yu1, 2, WU Na1, 2. The Spectroscopic Analysis of Corrosion Products on Gold-Painted Copper-Based Bodhisattva (Guanyin) in Half Lotus Position From National Museum of China[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3832-3839. |
[6] |
WANG Hong-jian1, YU Hai-ye1, GAO Shan-yun1, LI Jin-quan1, LIU Guo-hong1, YU Yue1, LI Xiao-kai1, ZHANG Lei1, ZHANG Xin1, LU Ri-feng2, SUI Yuan-yuan1*. A Model for Predicting Early Spot Disease of Maize Based on Fluorescence Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3710-3718. |
[7] |
CHENG Hui-zhu1, 2, YANG Wan-qi1, 2, LI Fu-sheng1, 2*, MA Qian1, 2, ZHAO Yan-chun1, 2. Genetic Algorithm Optimized BP Neural Network for Quantitative
Analysis of Soil Heavy Metals in XRF[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3742-3746. |
[8] |
SONG Yi-ming1, 2, SHEN Jian1, 2, LIU Chuan-yang1, 2, XIONG Qiu-ran1, 2, CHENG Cheng1, 2, CHAI Yi-di2, WANG Shi-feng2,WU Jing1, 2*. Fluorescence Quantum Yield and Fluorescence Lifetime of Indole, 3-Methylindole and L-Tryptophan[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3758-3762. |
[9] |
WANG Zhi-qiang1, CHENG Yan-xin1, ZHANG Rui-ting1, MA Lin1, GAO Peng1, LIN Ke1, 2*. Rapid Detection and Analysis of Chinese Liquor Quality by Raman
Spectroscopy Combined With Fluorescence Background[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3770-3774. |
[10] |
YI Min-na1, 2, 3, CAO Hui-min1, 2, 3*, LI Shuang-na-si1, 2, 3, ZHANG Zhu-shan-ying1, 2, 3, ZHU Chun-nan1, 2, 3. A Novel Dual Emission Carbon Point Ratio Fluorescent Probe for Rapid Detection of Lead Ions[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3788-3793. |
[11] |
YANG Ke-li1, 2, PENG Jiao-yu1, 2, DONG Ya-ping1, 2*, LIU Xin1, 2, LI Wu1, 3, LIU Hai-ning1, 3. Spectroscopic Characterization of Dissolved Organic Matter Isolated From Solar Pond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3775-3780. |
[12] |
QI Guo-min1, TONG Shi-qian1, LIN Xu-cong1, 2*. Specific Identification of Microcystin-LR by Aptamer-Functionalized Magnetic Nanoprobe With Laser-Induced Fluorescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3813-3819. |
[13] |
HE Yan-ping, WANG Xin, LI Hao-yang, LI Dong, CHEN Jin-quan, XU Jian-hua*. Room Temperature Synthesis of Polychromatic Tunable Luminescent Carbon Dots and Its Application in Sensitive Detection of Hemoglobin[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3365-3371. |
[14] |
LIN Hong-jian1, ZHAI Juan1*, LAI Wan-chang1, ZENG Chen-hao1, 2, ZHAO Zi-qi1, SHI Jie1, ZHOU Jin-ge1. Determination of Mn, Co, Ni in Ternary Cathode Materials With
Homologous Correction EDXRF Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3436-3444. |
[15] |
LI Xiao-li1, WANG Yi-min2*, DENG Sai-wen2, WANG Yi-ya2, LI Song2, BAI Jin-feng1. Application of X-Ray Fluorescence Spectrometry in Geological and
Mineral Analysis for 60 Years[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 2989-2998. |
|
|
|
|