Comparative Study on SERS and Stability of Negative Silver Colloids |
LI Qing-yu1,LI Shi-rong2,SI Min-zhen2*,ZHANG Peng-xiang3 |
1. Department of Basic Courses, Southwest Forestry College, Kunming 650224, China 2. Department of Physics and Electronic Science, Chuxiong Teacher’s College, Chuxiong 675000, China 3. IAMPE Kunming University of Science and Technology, Kunming 651000, China |
|
|
Abstract Negatively charged colloidal nano-silver particles were prepared by the colloidal chemical method. A 1.7% solution of silver nitrate(2 mL) was diluted with deionized water to 100 mL. A 1% solution of tannic acid(1 mL) was added dropwise to the solution stirring, then a 1% solution of potassium carbonate anhydrous(3-4 drops) was added to the mixed solution. Finally, a red-brown silver sol was obtained. It was testified that the silver sol is a negatively charged colloid by experiment of electrophoresis. The negative silver colloids (for short, old NCS) were kept on at the room temperature two year ago in order to test its SERS and stability. The sizes of particles were determined by Hitachi H-800 transmission electron microscope. Absorption spectroscopy and SERS were used to determine the main properties. Absorption spectra were obtained with UV-2401PC. Raman spectra were recorded with RENISHAW MIK 2000 Raman micro-spectroscopy. The 514.5 nm line of an argon ion laser with about 3 mw was used. Compared with the newly perpared negative silver colloids (for short, new NCS). It was found that the mean diameter of the old NCS was larger than the new NCS; old NCS had absorption maximum at 431 nm but new NCS at 418 nm, the absorbance spectrum of old NCS had a 12 nm red shift, and the red shift rate is about 0.5 nm/month; Both strong SERS spectra were observed when cationic molecules of fuchsine basic and neutral molecules of alcidine orange adsorbed on old NCS and new NCS; For cationic molecules of methylene blue, the SERS is stronger on new NCS than old NCS; but no SERS was observed for the anionic molecule of benzoic acid both on new NCS and on old NCS.
|
Received: 2005-12-28
Accepted: 2006-04-06
|
|
Corresponding Authors:
SI Min-zhen
E-mail: siminzhen@cxtc.edu.cn
|
|
Cite this article: |
LI Qing-yu,LI Shi-rong,SI Min-zhen, et al. Comparative Study on SERS and Stability of Negative Silver Colloids[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(02): 299-301.
|
|
|
|
URL: |
https://www.gpxygpfx.com/EN/Y2007/V27/I02/299 |
[1] Lee P C, Meisel D P. J. Phys. Chem., 1982, 86: 3391. [2] Creighton J A. Chem. Soc. Faraday Trans., 1979, 75(2): 790. [3] Munro C H. Smith W E, Garner. Langmuir, 1995, 11: 3712. [4] SI Min-zhen, WU Rong-guo, ZHANG Peng-xiang(司民真, 武荣国, 张鹏翔). Acta Photonica Sinica(光子学报),1999,28(9):839. [5] SI Min-zhen, WU Rong-guo, ZHANG Peng-xiang(司民真, 武荣国, 张鹏翔). Chin. J. Chem. Phys.(化学物理学报), 2001,14(6):732. [6] SI Min-zhen, WU Rong-guo, ZHANG Peng-xiang(司民真, 武荣国, 张鹏翔). Acta Photonica Sinica(光子学报),2001,30(8):1016. [7] SI Min-zhen, ZHANG Peng-xiang(司民真, 张鹏翔). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2001,21(4): 501. [8] SI Min-zhen, WU Rong-guo, ZHANG Peng-xiang(司民真, 武荣国, 张鹏翔). Chin. J. Chem. Phys.(化学物理学报),2001, 14(4): 465. [9] LI Jia-wei, BAI Ying, MO Yu-jun, et al(李佳伟,白 莹,莫育俊,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(3):463.
|
[1] |
LIU Xin-peng1, SUN Xiang-hong2, QIN Yu-hua1*, ZHANG Min1, GONG Hui-li3. Research on t-SNE Similarity Measurement Method Based on Wasserstein Divergence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3806-3812. |
[2] |
LIN Hong-jian1, ZHAI Juan1*, LAI Wan-chang1, ZENG Chen-hao1, 2, ZHAO Zi-qi1, SHI Jie1, ZHOU Jin-ge1. Determination of Mn, Co, Ni in Ternary Cathode Materials With
Homologous Correction EDXRF Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3436-3444. |
[3] |
ZHAO Yu-wen1, ZHANG Ze-shuai1, ZHU Xiao-ying1, WANG Hai-xia1, 2*, LI Zheng1, 2, LU Hong-wei3, XI Meng3. Application Strategies of Surface-Enhanced Raman Spectroscopy in Simultaneous Detection of Multiple Pathogens[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(07): 2012-2018. |
[4] |
WANG Ke-qing1, 2*, WU Na1, 2, CHENG Xiao-xiang3, ZHANG Ran1, 2, LIU Wei1, 2*. Use of FTIR for the Quantitative Study of Corrosion Products of Iron
Cultural Relics[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1846-1853. |
[5] |
LI Jia-jia, XU Da-peng *, WANG Zi-xiong, ZHANG Tong. Research Progress on Enhancement Mechanism of Surface-Enhanced Raman Scattering of Nanomaterials[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1340-1350. |
[6] |
YANG Guo-wu1, HOU Yan-xia1, SUN Xiao-fei2, JIA Yun-hai1*, LI Xiao-jia1. Evaluation of Long-Term Stability for Non-Standard Method and
Application in Trace Element Analysis of Pure Nickel by Glow
Discharge Mass Spectrometry[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 867-876. |
[7] |
ZHANG Xue-fei1, DUAN Ning1, 2*, JIANG Lin-hua1, 2*, CHENG Wen2, YU Zhao-sheng3, LI Wei-dong2, ZHU Guang-bin4, XU Yan-li2. Study on Stability and Sensitivity of Deep Ultraviolet Spectrophotometry Detection System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(12): 3802-3810. |
[8] |
ZHU Pan-pan1, 2, NIU Xiao-tao3, WANG Xue3, SI Xin1, 2, XIE Qing-gang3, CHEN Bo3, JIANG Shi-long3, JU Ning1*, ZHANG Shu-wen2*, LÜ Jia-ping2. The Stability of Room Temperature Liquid Cheese Based on Turbiscan Multiple Light Scattering Technique[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3415-3422. |
[9] |
CHEN Huan-quan1, DONG Zhong-ji2, CHEN Zhen-wei1, ZHOU Jin1, SU Jun-hao1, WANG Hao1, ZHENG Jia-jin1, 3*, YU Ke-han1, 3, WEI Wei1, 3. Study on the High Temperature Annealing Process of Thermal
Regeneration Fiber Bragg Grating[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(06): 1934-1938. |
[10] |
HUANG Hui1, 2, TIAN Yi2, ZHANG Meng-die1, 2, XU Tao-ran2, MU Da1*, CHEN Pei-pei2, 3*, CHU Wei-guo2, 3*. Design and Batchable Fabrication of High Performance 3D Nanostructure SERS Chips and Their Applications to Trace Mercury Ions Detection[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(12): 3782-3790. |
[11] |
QIU Meng-qing1, 2, XU Qing-shan1*, ZHENG Shou-guo1*, WENG Shi-zhuang3. Research Progress of Surface-Enhanced Raman Spectroscopy in Pesticide Residue Detection[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(11): 3339-3346. |
[12] |
GAO Jian-kui1,2, LI Yi-jie3, ZHANG Qin-nan1, LIU Bing-wei1, LIU Jing-bo1, LING Dong-xiong1, LI Run-hua2, WEI Dong-shan1*. Temperature Effects on the Terahertz Spectral Characteristics of PEEK[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(11): 3347-3351. |
[13] |
LI Guang-mao, QIAO Sheng-ya, ZHU Chen, ZHENG Fu-li, YANG Sen, CAI Han-xian. Preparation and Application of Micro-Nano Structure SERS Substrate Based on Copper Mesh Displacement Reaction[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(10): 3166-3171. |
[14] |
TIAN Zhen-hua1, 2, HE Jing-xuan1, WANG Ying1, DUAN Lian3, LI Cong-hu4. Interaction and Thermal Stability of Oxidized Carboxymethyl Cellulose/Collagen Based on Two-Dimensional Infrared Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(09): 2782-2788. |
[15] |
GUI Bo1, 2, YANG Yu-dong1, ZHAO Qian1, 2, SHI Meng1, MAO Hai-yang1, 3*, WANG Wei-bing1, CHEN Da-peng1, 3. A SERS Substrate for On-Site Detection of Trace Pesticide Molecules Based on Parahydrophobic Nanostructures[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(08): 2499-2504. |
|
|
|
|