| Cathodoluminescent Properties of Na2GdPO4F2∶Tb3+ Green Phosphors |
| LI Song-bo1，2，ZHAO Wen-yu2，FAN Bin2，AN Sheng-li1,3* |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
2. School of Chemistry and Chemical Engineering, Inner Mongolia University of Science & Technology, Baotou 014010, China
3. School of Metallurgical and Material Engineering, Inner Mongolia University of Science & Technology, Baotou 014010, China |
|
|
|
|
Abstract The green emitting phosphors, Na2GdPO4F2∶Tb3+, was synthesized by high temperature solid-state method. X-ray diffraction (XRD) and cathodoluminescence (CL) spectrum were used to characterize the samples. Under the low-voltage electron beam (0.5~5 kV) excitation, the Tb3+-doped Na2GdPO4F2 phosphor showed a very strong green emission corresponding to the characteristic transitions of Tb3+ (5D3,4→7FJ transitions, J=6~2) with the strongest emission at 546 nm, corresponding to 5D4→7F5 of Tb3+. The cathodoluminescent color of Na2Gd0.95Tb0.05PO4F2 was green to the naked eye with the Commission International de l’Eclairage (CIE) coordinates of x=0.240 3, y=0.438 6, and the color temperature at about 8 634.3 K. The CL intensity increases upon raising the accelerating voltage, filament current and the doping concentrations, thereinto, the optimal concentrations of Tb3+ is 10 mol%.
|
|
Received: 2010-06-08
Accepted: 2010-10-06
|
|
|
|
Corresponding Authors:
AN Sheng-li
E-mail: san@imust.cn
|
|
[1] DUAN Chun-yan, CHEN Jun, DENG Shao-zhi, et al(段春艳, 陈 军, 邓少芝, 等). Chinese Journal of Electron Device(电子器件), 2008, 32(1): 184.
[2] Li Guogang, Li Chunxia, Hou Zhiyao, et al. Optics Letters, 2009, 34(24): 3833.
[3] Chen Wanping, Liang Hongbin, Xie Mubiao, et al. Journal of the Electrochemical Society, 2010, 157(2): 21.
[4] Chen Wanping, Liang Hongbin, Han Bing, et al. J. Phys. Chem. C, 2009, 113(39): 17194.
[5] Shannon R D. Acta Crystallogr，1976, A32: 751.
[6] Xu Zhenhe, Yang Jun, Hou Zhiyao, et al. Materials Research Bulletin，2009，44：1850.
[7] Xu Zhenhe, Li Chunxia, Li Guogang, et al. J. Phys. Chem. C，2010, 114：2573.
[8] Tian Zifeng, Liang Hongbin, Chen Wangping, et al. Optics Express, 2009, 17(2): 956.
[9] Tian Zifeng, Liang Hongbin, Su Qiang, et al. Materials Research Society, 2008, 23(6): 1537.
[10] Liu Xiaoming, Lin Jun. Solid State Sciences, 2009, 11: 2030.
[11] ZHANG Si-yuan(张思远). Spectroscopy of Rare Earth Ions(稀土离子的光谱学). Beijing: Science Press(北京: 科学出版社), 2008. 140.
|
| [1] |
FAN Bin1, LIU Jun2, QI Shi-mei3, ZHAO Wen-yu1*. Preparation and Luminescent Properties of Green Phosphors LaGaO3∶Tb3+,Sn4+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 65-70. |
| [2] |
ZHANG Na1,2, ZHUO Ning-ze1,2,3*, CHENG Shao-wen4, ZHU Yue-hua1,2, WANG Hai-bo2*. Preparation of ZnO∶Zn Green Phosphors via Sintering Temperatures with Solid State Reaction and Their Application in Near-UV LEDs[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(10): 3030-3035. |
| [3] |
WAN Ying，HE Jiu-yang, MA Yuan-yuan, ZHOU Zhi-xuan, Taximaiti·Yusufu, Aierken·Sidike*. Synthesis and Luminescence Properties of a New Type of Green Fluorescent Powder BaAl2Si2O8∶Tb3+, Ce3+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(05): 1595-1600. |
| [4] |
ZHAO Wen-yu1，2, FAN Bin1*, LI Song-bo1，2, ZHANG Guo-bin3, DAI Ya-tang4 . Photoluminescence of Green Phosphors Gd2Ba3B3O12 Doped with Tb3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(03): 617-620. |
| [5] |
QU Chong1, XU Zheng2, CHEN Yue-ning2 . Investigation of Luminescence Mechanism of Hybrid MEH-PPV/ SiO2 and Super Liner Characteristic of Amorphous SiO2 [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(12): 3223-3227. |
| [6] |
LI Jun-ming, XU Zheng*, ZHAO Su-ling, ZHANG Fu-jun, SONG Dan-dan, LIU Xiao-dong, SONG Jing-lu, XU Xu-rong, WANG Yong-sheng. Evaluating Acceleration Ability of Electrons of Different Acceleration Layers in Solid State Cathodoluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(11): 2893-2896. |
| [7] |
LOU Zhi-dong,XU Zheng,YI Lan-jie,YANG Sheng-yi. Cathodoluminescent Characteristics of Green-Emitting ZnAl2O4∶Mn Thin Film Phosphors[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(06): 1218-1221. |
| [8] |
LIU De-ang, XU Zheng, TENG Feng, ZHAO Su-ling, WANG Yong-sheng, XU Xu-rong* . The Influence of Frequency on Solid State Cathodoluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(06): 987-990. |
| [9] |
LIU Ming1, 2,CHEN Xiao-hong3,XU Zheng1,TENG Feng1,YI Li-xin1,GAO De-wen2,GUO Li-qun2 . Proof of Solid State Cathodoluminescence by Using Brightness Waveform [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(10): 1556-1559. |
| [10] |
LIU Shan-shan, TENG Feng, XU Zheng, LIU Ming, SUN Shi-ju, XU Xu-rong . The Influence of Thickness of SiO2 on the Electron Acceleration in Cathodluminescence-Like Emission [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(07): 790-794. |
|
|
|
|