Preparation and Luminescence Properties of Core-Shell ZnS∶Cu/ZnS Nano-Particles |
CAO Li-xin, SUN Da-ke, LIN Ying-xia |
Institute of Materials Sciences and Engineering, Ocean University of China, Qingdao 266003, China |
|
|
Abstract Core-shell structured ZnS∶Cu/ZnS nano-particles and Cu2+-doped ZnS nano-particles without any shell were prepared, and the effect of ZnS shell on the luminescence properties of ZnS∶Cu2+ nano-particles was studied. The observed emission peak at 450 nm was assigned to the recombination of an electron from the shallow delocalized donor levels at the t2 level of Cu2+. The ZnS shell did enhance the luminescence at 450 nm, which resulted from the reduction of nonradiative recombination sites.
|
Received: 2005-09-28
Accepted: 2006-01-06
|
|
Corresponding Authors:
CAO Li-xin
|
|
Cite this article: |
CAO Li-xin,SUN Da-ke,LIN Ying-xia. Preparation and Luminescence Properties of Core-Shell ZnS∶Cu/ZnS Nano-Particles [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(11): 2000-2002.
|
|
|
|
URL: |
https://www.gpxygpfx.com/EN/Y2006/V26/I11/2000 |
[1] Spanhel L, Haase M, Weller H,et al. J. Am. Chem. Soc., 1987, 109: 5649. [2] Danek M, Jensen K F, Murray C B,et al. Chem. Mater., 1996, 8: 173. [3] Hines M A, Guyot-Sionnest P. J. Phys. Chem., 1996, 100: 468. [4] Harrison M T, Kershaw S V, Rogach A L,et al. Adv. Mater., 2000, 12: 123. [5] Gerion D, Pinaud F, Williams S C, et al. J. Phys. Chem. B, 2001, 105: 8861. [6] TENG Feng, TANG Ai-wei, GAO Yin-hao, et al(滕 枫,唐爱伟,高银浩, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2005,25(5):651. [7] Heesun Y, Paul H H. Appl. Phys. Lett., 2003, 82(12): 1965. [8] Steigerwald M L, Alivisatos A P, Gibson J M, et al. J. Am. Chem. Soc., 1988, 110: 3046. [9] YAO Lian-zeng et al(姚连增, 等). The Basic of Crystal Growth(晶体生长基础). Hefei: Press of University of Science and Technology of China(合肥: 中国科学技术大学出版社),1995. 258. [10] Brus L E. J. Chem. Phys., 1984, 80: 4403. [11] Liu C X, Liu J X, Xu W. Materials Science and Engineering, 2000,B75: 78. [12] Xu S J, Chua S J, Liu B,et al. Appl. Phys. Lett., 1998, 73(4): 478. [13] Wang M, Sun L, Fu X, et al. Solid State Commun., 2000, 115: 493. [14] Yang P, Lu M, Xu D, et al. Chem. Phys. Lett., 2001, 336: 76. [15] Ageeth A B, Joke F, Jaap A B, et al. J. Luminescense, 2002, 99(4): 325. [16] Sang W, Qian Y, Min J, et al. Solid State Commun., 2002, 121(9-10): 475. |
[1] |
LAI Niu, HUANG Qi-qiang, ZHANG Qin-yang, ZHANG Bo-wen, WANG Juan, YANG Jie, WANG Chong, YANG Yu, WANG Rong-fei*. Introduction to Perovskite Quantum Dots and Metal-Organic Frameworks and the Development of Composites[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3321-3329. |
[2] |
DING Han. Background-Free Development of Latent Fingerprints on Fluorescent
Substrates[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3427-3435. |
[3] |
QIN Li-mei, Andy Hsitien Shen*. Photoluminescence Spectral Characteristics of Jet From Fushun, Liaoning Province[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3180-3185. |
[4] |
ZHU Hong-wei1, CHENG You-fa1, CHEN Shu-xiang2*, FAN Chun-li1, LI Ting1, LIU Hai-bin1, ZHAO Xiao-xue1SHAN Guang-qi1, LI Jian-jun1. Spectroscopic Characteristics of a Natural Diamond Suspected of Synthetic Diamond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1690-1696. |
[5] |
YAN Xue-jun1, ZHOU Yang2, HU Dan-jing1, YU Dan-yan1, YU Si-yi1, YAN Jun1*. Application of UV-VIS Diffuse Reflectance Spectrum, Raman and
Photoluminescence Spectrum Technology in Nondestructive
Testing of Yellow Pearl[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1703-1710. |
[6] |
HAN Zhao-xia1, 2, 3*, YANG Zhi-jin1, ZHANG Zhi-hong1, DING Shu-hui1, ZHANG Da-wei1, 2, 3, HONG Rui-jin1, 2, 3, TAO Chun-xian1, 2, 3, LIN Hui1, 2, 3, YU De-chao1, 2, 3. Preparation of Full-Color Carbon Quantum Dots and Their Application in WLED[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1358-1366. |
[7] |
LI Zhao, WANG Ya-nan, XU Yi-pu, CAO Jing, WANG Yong-feng, WU Kun-yao, DENG Lu. Synthesis and Photoluminescence of Blue-Emitting Phosphor
YVO4∶Tm3+ for White Light Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 623-628. |
[8] |
ZHAI Yan-ke1, PAN Yi-xing1, XIANG Hao1, XU Li1*, ZHU Ze-ce2, LEI Mi1. Coordination Interaction of DSAZn With Quercetin and High Sensitivity Detection of Quercetin[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(01): 122-128. |
[9] |
FAN Dan-yang1, ZHANG Xue-cheng1, GAO Jun1, WANG Jia-bin2, LÜ Hai-xia1*. Study on Specific Detection of Sulfadimethoxine Based on Aptamer-Modified Up-Conversion Fluorescent Nanomaterial[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3409-3414. |
[10] |
ZHAO Guo-qiang1, QIU Meng-lin1*, ZHANG Jin-fu1, WANG Ting-shun1, WANG Guang-fu1, 2*. Peak Splitting Method of Ion-Beam-Induced-Luminescence Spectrum Based on Voigt Function Fitting[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3512-3518. |
[11] |
WANG Chong1, WANG Jing-hua1, 2, LI Dong-dong1, SHE Jiang-bo2. Preparation of Gd3+-Doped LiYF4∶Yb3+/Ho3+ Micro-Crystal and the Application Research in Anti-Counterfeiting[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3581-3587. |
[12] |
LIAO Yi-min1, YAN Yin-zhou1, WANG Qiang2*, YANG Li-xue3, PAN Yong-man1, XING Cheng1, JIANG Yi-jian1, 2. Laser-Induced Growth Device and Optical Properties of ZnO
Microcrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3000-3005. |
[13] |
ZHANG Li-gang1, MA Li-hong1*, ZHAO Su-ling2, XU Zheng2, YANG Hai-jun1, LI Chen-pu1, WANG Ke1, LIU Gui-xia1, BAI Yong-qing1, SHEN Wen-mei1. Effect of Reaction Temperature on the Luminescence and Morphology of Na3ScF6∶Yb/Er Nanocrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3068-3072. |
[14] |
ZHANG Xiao-teng, LIU Wei, LIU Hai-feng*, ZHENG Zun-qing, MING Zhen-yang, CUI Yan-qing, WEN Ming-sheng, YAO Ming-fa. Intensity Distribution and Inversion Reconstruction of Spectrum of
Hydroxyl Radicals in Spray Combustion of PODE Under Different
Environmental Oxygen Concentrations[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(08): 2587-2594. |
[15] |
HU Xin-yan1, CAO Long-fei1, LI Jin-hua1, 2, 3, LI Shuang1*. Eu3+/Dy3+ Co-Doped Sr3Y2(BO3)4 Phosphor Luminous Properties
Research[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(07): 2063-2068. |
|
|
|
|