Preparation and Characterization of MgxZn1-xO Powders |
LIU Quan-sheng,ZHANG Xi-yan*,BAI Zhao-hui,WANG Xiao-chun,MI Xiao-yun,LU Li-ping,ZHOU Ying |
School of Material Science and Engineering, Changchun University of Science and Technology, Changchun 130022, China |
|
|
Abstract MgxZn1-xO has been subjects of intense attention as a novel photo-electronic functional material in recent years. In the present paper, MgxZn1-xO powders were prepared by sol-gel method. Effects of Mg contents on MgxZn1-xO structure and luminescence properties were studied. The authors observed that MgxZn1-xO exhibited two kinds of structures, hexagonal wurtzite and face center cubic while x was in the range of 0 and 1. The MgxZn1-xO powders were hexagonal wurtzite structure with x<0.2, face center cubic structure with x>0.2 and their blend structure with x between 0.2 and 0.8. Luminescence spectrum analysis indicated that all MgxZn1-xO samples with various composition showed luminescence of ultra-violet and visible light. The ultraviolet emission peak was from 370 nm to 384 nm and the visible emission peak was around at 468 nm. The average size of MgxZn1-xO powders was about 100 nm.
|
Received: 2007-11-25
Accepted: 2008-02-26
|
|
Corresponding Authors:
ZHANG Xi-yan
E-mail: xiyzhang@126.com
|
|
[1] Schreiber P, Dang T, Smith G, et al. Proc. SPIE, 1999, 3629: 230. [2] Teng C W, Muth J F, Ozgur U, et al. Appl. Phys. Lett., 2000, 76(8): 979. [3] ZHAO Dong-xu, LIU Yi-chun, SHEN De-zhen, et al(赵东旭, 刘益春, 申德振, 等). Research & Progress of Solid State Electronics(固体电子学研究与进展), 2002, 22(4): 433. [4] CHEN Han-hong, YE Zhi-zhen(陈汉宏, 叶志镇). Semiconductor Information(半导体情报), 2001, 38(2): 37. [5] Shannon R D. Acta Cryst., 1976, A32: 751. [6] Yang W, Hullavarad S S, Nagaraj B, et al. Applied Physics Letters, 2003, 82(20): 3424. [7] Choopun S, Vispute R D, Yang W, et al. Applied Physics Letters, 2002, 80(9): 1529. [8] WU Chun-xia, Lü You-ming, LI Bing-hui, et al(吴春霞, 吕有明, 李炳辉, 等). Chinese Journal of Luminescence(发光学报), 2004, 25(3): 277. [9] WU Chun-xia, Lü You-ming, SHEN De-zhen, et al(吴春霞, 吕有明, 申德振, 等). Chinese Journal of Semiconductors(半导体学报), 2004, 25(10): 1258. [10] LIAN Jie, WANG Qing-pu, ZHAO Yi-kun, et al(连 洁, 王青圃, 赵懿昆, 等). Journal of Optoelectronics·Laser(光电子技术·激光), 2006, 17(5): 554. [11] CHEN You-cun, ZHANG Yuan-guang(陈友存, 张元广). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2004, 24(9): 1032. [12] LI Jin-hua, ZHANG Xin-tong, LI Yi-chun, et al(李金华, 张昕彤, 刘益春, 等). Chemical Journal of Chinese Universities(高等学校化学学报),2003, 24: 1830.
|
[1] |
QIU Zhi-che, GU Mu*, LIU Xiao-lin, LIU Bo, HUANG Shi-ming, NI Chen . Preparation and Performances of the M′-Type LuTaO4∶Eu3+ Transparent Scintillator Films[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(02): 336-339. |
[2] |
GUO Yu, JIN Yu-jia, WU Hong-mei, LI Dong-xin . Preparation and Photocatalytic Properties of Supported TiO2 Photocatalytic Material[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(06): 1677-1681. |
[3] |
Lü Shan-shan1, FANG Xuan1*,WANG Jia-qi1, FANG Fang1,ZHAO Hai-feng2, CHU Xue-ying1, LI Jin-hua1, FANG Dan1, TANG Ji-long1, WEI Zhi-peng1, MA Xiao-hui1, WANG Xiao-hua1*, PU Shuang-shuang1, XU Li1 . Preparation of MgxZn1-xO /Au/MgxZn1-xO Multilayer Transparent Conductive Film and Studies of Its Photoelectric Properties[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(09): 2355-2359. |
[4] |
WANG Xi-gui,QI Xia,BO Su-ling,NA Mi-la . Preparation and Luminescence Properties of Nanomaterials TiO2—SiO2 Doped with Eu3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(05): 1193-1196. |
[5] |
WU Yang, WANG Yong-sheng*, HE Da-wei*, FU Ming, CHEN Zhen-min, LI Yue, MIAO Feng . Synthesis of the Zn2SiO4∶Eu3+ Red Phosphor by Sol-Gel Method [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(04): 890-893. |
[6] |
FAN Yang-yang, LIU Xiao-lin*, GU Mu, NI Chen, HUANG Shi-ming, LIU Bo . Modification and Luminescence Properties of Transparent Lu2SiO5∶Ce3+ Thin-Film Phosphors [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(02): 344-348. |
[7] |
PAN Jing1, HU Xiao-yun1*, LIU Guo-jing1, ZHANG De-kai1, FAN Jun2 . Influence of the Amount of H2O on the Emission Spectra of Tb Doped SiO2 Xerogels [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(05): 1179-1183. |
[8] |
GU Mu, ZHOU Feng, LIU Xiao-lin, NI Chen, HUANG Shi-ming, LIU Bo . Preparation and Luminescence Properties of Transparent Gd2O3∶Eu Thick Film [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(03): 603-606. |
[9] |
LIU Wan-bing1, DENG Jian1*, ZHAO Yu-bao1, XU Jin-sheng2, ZHOU Liang1 . Preparation, Spectral Analysis and Photocatalytic Activities of TiO2 Films Codoped with Iron and Nitrogen [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(05): 1394-1397. |
[10] |
FENG Shi-hong1,JIA Tai-xuan2,3,LIU Zi-li2,3*. Preparation of Mo-Fe Catalysts by Sol-Gel Method and Its XRD, FTIR Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(02): 548-550. |
[11] |
JIN Zhen-xing1,HUANG Hong-yan1,LIU Shou-xin2. Preparation of N-Doped Nanosize TiO2 and Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(02): 370-373. |
[12] |
SONG Guo-li. Luminescence Characteristics of Terbium-Doped Nanocrystalline Zinc Oxide[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(12): 2409-2412. |
[13] |
WANG Xiao-dong, LIU Xiao-hua*,CHEN Shao-jun, LI Ming, LIU Min. Preparation of CeO2∶Eu3+ Powders by Sol-Gel Method and Their Photoluminescence Properties[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(11): 2182-2185. |
[14] |
SONG Guo-li,SUN Kai-xia, YANG You-tong. Preparation and Photoluminescence Investigation of Europium-Doped Zinc Oxide Nanocrystalline[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(04): 639-642. |
[15] |
ZENG Dong-ming1,LI Yan-hua1, 2,FU Chang-cheng1,LIU You-nian1,SHU Wan-gen1 . Effect of PEG400 on the Luminescent Eu(BA)3/SiO2[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(02): 236-239. |
|
|
|
|