The Optics and Magnetic Properties of Cr Doped ZnO Thin Films |
CHEN Xiang1, YANG Wen-yu1, ZHANG Hui-qin1, ZOU Ming-zhong1, ZHUANG Bin1, LIN Ying-bin1,2, HUANG Zhi-gao1,2* |
1. College of Physics and Energy, Fujian Normal University, Provincial Key Laboratory of Quantum Manipulation and New Energy Materials, Fuzhou 350117, China 2. Fujian Provinical Collaborative Innovation Center for Optoeletronic Semiconductors and Efficient Devices, Xiamen 361005, China |
|
|
Abstract The precursor solution is sent to the ultrasonic nozzle directly through a needle tube to prepare Zn1-xCrxO (x=0, 0.01, 0.03 and 0.05)films on quartz substratesby ultrasonic spray method. The structures, optical and magnetic properties of the films were measured by X-ray diffracmeter(XRD), scanning electron microscope(SEM), fluorescence spectrometer, ultraviolet-visible light detector, vibrating sample magnetometer (VSM) and so on. The experimental results indicate that, the undopedZnO thin films exhibit the hexagonal wurtzite crystalline structure with a preferential orientation of (002); the Cr doping restrains the preferred orientation of C axis; the average grain sizes of the samples increase withCr doping, and thesize attains the maximum(31.4 nm) when x=3%. The SEMimages show that the Zn1-xCrxO (x=0, 0.01, 0.03 and 0.05) films are grain-like particles. And it exhibits a long strip shape when x=5%. Moreover, the doping of Cr makes the photoluminescence (PL) spectra of Zn1-xCrxO films change evidently. The undoped sample shows an ultraviolet emission peak at 378 nm as well as a defect related green peak at around 550 nm. However, for the doping samples, there is only a wide range of emission peak from 350 to 550 nm. By gaussian fitting,it is found that VZn, Zni and V-Zn defects exist in the Cr doping films, and VZn is largest when x=3%. The band gap increases with the doping of Cr, and reaches the maximum when x=3%. The doping of Cr hasthe band gap of the samples increase, and the band gapreachs themaximum(3.37 eV) when x=3%. Magnetic measured results show that threedoping samples Zn1-xCrxO(x=1%, 3% and 5%) are ferromagnetic at room temperature, and the magnetization of Zn1-xCrxO (x=3%) is the largest, which is corresponding to the most VZn defect. The experimental results also prove the the oretical prediction that the substitutive Cr in the oxidation state of +3 and the neutral Zn vacancy in the ZnO∶Cr sample are the most favorable defect complex to maintain a high stability of ferromagnetic order.
|
Received: 2015-02-21
Accepted: 2015-06-12
|
|
Corresponding Authors:
HUANG Zhi-gao
E-mail: zghuang@fjnu.edu.cn
|
|
[1] Bedia A, Bedia F Z, Aillerie M, et al. Optical Materials, 2014, 36: 1123. [2] Benramache S, Benhaoua B. Superlattices and Microstructures, 2012, 52: 807. [3] WU Xiao-juan, WEI Zhi-qiang, WU Yong-fu, et al(武晓娟, 魏智强, 吴永富, 等). Spectroscopy and Spectral Analysis( 光谱学与光谱分析, 2013, 33(8): 2035. [4] Punnoose A, Seehra M S, Park W K, et al. Appl. Phys., 2003, 93: 7867. [5] Weng Z Z, Huang Z G, Lin W X. J. Appl. Phys., 2012: 113915. [6] XIE Ling-ling, CHEN Shui-yuan, LIU Feng-jin, et al(谢玲玲, 陈水源, 刘凤金, 等). (物理学报), 2014, 63(7): 077102. [7] Adolph D, Ive T. Appl. Surf. Sci., 2014, 307: 438. [8] Babu E S, Hong S K. Superlatticesand Microstructures, 2015, 82: 349. [9] Al-Assiri M S, Mostafa M M, Ali M A, et al. Superlattices and Microstructures, 2014, 75: 127. [10] Cittadini M, Sturaro M, Guglielmi M, et al. Sensors and Actuators B, 2015, 213: 493. [11] Oyola J S, Castro J M, Gordillo G. Solar Energy Materials & Solar Cells, 2012, 102: 137. [12] Zhang C, Chen X L, Geng X H, et al. Appl. Sur. Sci., 2013, 274: 371. [13] Bedia A, Bedia F Z, Aillerie M, et al. Optical Materials, 2014, 36: 1123. [14] Benramache S, Benhaoua B, Chabane F, et al. Optik, 2013, 124: 3221. [15] Karak N, Samanta P K, Kundu T K. Optik, 2013, 124: 6227. [16] Xu P S, Sun Y M, Shi C S, et al. Nucl. Instrum. Methods Phys. Res., Sect. B, 2003, 199: 286. |
[1] |
LI Shi-lun1, LIU Tao2, SONG Wen-min3, WANG Tian-le2, LIU Wei1, CHEN Liang1, LI Zhi-gang2*, FENG Shang-shen1*. Study of Two-Dimensional Ordered Magnetic Co Nanosphere Array Film Construction and Its Optical Properties[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(07): 2037-2042. |
[2] |
LI Zhao, WANG Yong-feng, CAO Jing, WU Kun-yao, WANG Ya-nan. Preparation and Performance of Red Phosphor ScVO4∶Eu3+ for White LEDs[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3077-3080. |
[3] |
WANG Xue-chuan1,2, BAI Peng-xia2, LUO Xiao-min1, LI Ji1. Synthesis of Carbon Quantum Dots Based on Gelatin and Study on It’s Optical Property[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1154-1161. |
[4] |
ZHANG Dong1, ZHAO Yan1*, SONG Shi-wei1, LI Yu-cai1, WANG Jian1, BI Xiao-guo1, GAO Jing2, WANG Chun-sheng2. Study on the Deposition and Optical Properties of GaN Films at Quartz Substrate[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(09): 2672-2675. |
[5] |
MA Miao, YAN Wei, XU Xiang-dong*, ZHU Hong-zhao, LIU Yu-tong, DAI Ze-lin, ZOU Rui-jiao, JIANG Ya-dong. Preparation and Optoelectronic Properties of Zinc Tetraphenyl Porphyrin-Signle Walled Carbon Nanotube Composite Films[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(10): 3150-3155. |
[6] |
ZHAI Hao-ying, ZOU Hao. Synthesis of Cr, Ag Co-Doped ZnS Nanomaterials and Its Adsorption Capability for Reactive Dyes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(08): 2638-2644. |
[7] |
DUAN Liang-fei1, 2, YANG Wen1, 2 , YANG Pei-zhi1, 2*, ZHANG Li-yuan1, 2, SONG Zhao-ning3 . Research on the Phase and Optical Properties of nc-Si Films Prepared by Low Temperature Aluminum Induced Crystallization [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(08): 2169-2174. |
[8] |
WU Xiao-juan1, 2, WEI Zhi-qiang1, 2*, WU Yong-fu2, ZHANG Ling-ling2, JIANG Jin-long2, YANG Hua1, 2 . Spectroscopic Study of Dilute Magnetic Semiconductors Zn1-xFexO Nanoparticles[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(08): 2035-2038. |
[9] |
XU Hui-xia1,2, CHEN Liu-qing1,2, WANG Hua1,2, HAO Yu-ying1, XU Bing-she1,2* . Molecular Structure and Luminescent Property of Bis(2-(4-Methyl-2-Hydroxyphenyl)benzothiazolate) Zinc [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(02): 504-507. |
[10] |
HAO Yu-ying1,GAO Zhi-xiang1,WANG Hua2,ZHOU He-feng2,MA Guo-zhang3,LIU Xu-guang2,XU Bing-she2 . Spectroscopic Properties of Salicylaldehyde Anil Zinc and Its Thin Film[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(03): 491-495. |
[11] |
ZHU Jia-qi1, HAN Jie-cai1, TAO Yan-chun2, JIANG Chun-zhu1 . Spectroscopic Ellipsometry Investigations of Amorphous Diamond Films Deposited with Filtered Arc [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(02): 203-207. |
|
|
|
|