Abstract ScVO4∶Eu3+ red phosphor was prepared using-high temperature solid-state method. The phase, morphology and luminescence properties of the samples were characterized by X-ray powder diffraction (XRD), scanning electron microscope (SEM) and photoluminescence spectrum (PL). The results showed that: the synthesized ScVO4∶Eu3+ red phosphor was a tetragonal system with near-spherical surface. In the excitation spectrum, the excitation peaks at 382 nm, 395 and 466 nm were attributed to 7F0→5L7, 7F0→5L6 and 7F0→5D2 transitions, respectively. In the emission spectrum, the emission peaks at 598, 622 and 710 nm correspond to 5D0→7F1, 5D0→7F2 and 5D0→7F4 transitions of Eu3+. When Eu3+ has a doping ratio of 7% and is calcined at 1 200 ℃ for 3 h, ScVO4∶Eu3+ red phosphor has a CIE color coordinate of (0.671 6, 0.327 3) and fluorescence lifetime of 0.521 ms, which is a kind of high-efficiency red phosphor expected to be used in white LED.
[1] ZHANG Na,ZHUO Ning-ze,CHENG Shao-wen, et al(张 娜, 卓宁泽, 程少文,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2018, 38(10): 3030.
[2] Li Zhao, Wang Yongfeng, Cao Jing. Journal of Wuhan University of Technology·Materials Science, 2018, 33(5): 1028.
[3] Li Zhao, Wang Yongfeng, Cao Jing, et al. Journal of Rare Earths, 2016,34(2): 143.
[4] Cho S. Journal of the Korean Physical Society, 2019, 74(7): 707.
[5] Hämmer M, Gassmann A, Reller A, et al. Journal of Electronic Materials, 2019, 48(4): 2294.
[6] LI Zhao,ZHAO Xi-cheng,JIANG Yuan-ru, et al(李 兆, 赵西成, 江元汝,等). Journal of the Chinese Ceramic Society(硅酸盐学报), 2014, 42(10): 1279.
[7] LI Zhao,ZHAO Xi-cheng,JIANG Yuan-ru, et al(李 兆, 赵西成, 江元汝,等). Jorunal of Functional Materials(功能材料), 2014,(15): 15046.
[8] LI Zhao,WU Kun-yao,WANG Yong-feng, et al(李 兆, 吴坤尧, 王永锋,等). Chinese Journal of Materials Research(材料研究学报), 2017,(4): 274.
[9] LI Zhong-yuan,LI Yong,XIA Ai-lin(李中元, 李 勇, 夏爱林). Chinese Journal of Luminescence(发光学报), 2017,(3):296.
[10] YAN Ying-lin,WANG Juan,WANG Liang-liang, et al(燕映霖, 王 娟, 王亮亮, 等). Chinese Journal of Materials Research(材料研究学报), 2015, 29(4): 307.