| Donor Concentration Dependence of Upconversion Luminescence in YLiF4:Er3+, Yb3+ |
| ZHAO Su-ling1, XU Zheng1，2, PEI Xiao-jiang1 |
1. Institute of Optoelectronic Technology, Beijing Jiaotong University, the Lab of Materials for Information Storage and Displays, Beijing 100044, China
2. Tianjin University Postdoctoral Working Station, Economy and Technological Development Area Postdoctoral Working Station, Tianjin Zhong-Huan San-Jin Ltd., Tianjin 300457, China |
|
|
|
|
Abstract YLiF4:Er3+, Yb3+ was synthesized by hydrothermal method. The concentration of Er3+ was 2 mol%, and Yb3+ changed from 0 to 7 mol%. At room temperature the absorbance of YLiF4:Er3+, Yb3+ in all samples was measured from 200 to 1 200 nm. The absorbance around 980 nm increased with increasing Yb3+ concentration. The result shows that the upconversion intensity excited at 980 nm was enhanced. The enhanced intensity is dependent on the Yb3+ concentration. The excitation spectra and photoluminescence spectra were measured in the sample with Yb3+ concentration of 2 mol%. The red and green luminescence came from the transition 4F9/2→2I15/2 , and 4S3/2→2I15/2 and 2H11/2→2I15/2 , respectively.
|
|
Received: 2005-03-10
Accepted: 2005-07-20
|
|
|
|
Corresponding Authors:
ZHAO Su-ling
|
|
| Cite this article: |
|
ZHAO Su-ling,XU Zheng,PEI Xiao-jiang. Donor Concentration Dependence of Upconversion Luminescence in YLiF4:Er3+, Yb3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(12): 1933-1937.
|
|
|
|
| URL: |
|
https://www.gpxygpfx.com/EN/Y2005/V25/I12/1933 |
[1] Collings B C, Silversmith A J. Journal of Luminescence, 1994，62(6): 271.
[2] Zhang Long, Zhang Jun-Jie, Qi Chang-Hong, et al. Acta Physica Sinica, 2000，49(8): 1620.
[3] Hehlen M P, Frei G, Gudel H U. Physical Review B-Condensed Matter, 1994，50(22): 16264.
[4] Peters P M, Funk D S, Peskin A P, et al. Applied Optics, 1999，38(33): 6879.
[5] Wang Jin-Guo, Zhang Zhi-Guo, Xu Jing-Zhou, et al. Chinese Physics, 2000，9(3): 210.
[6] Binun P W, Boyd T L, Pessot M A, et al. Optics Letters, 1996, 21(23): 1915.
[7] Peterson P, Sharma M P. Optical and Quantum Electronics, 1998, 30(3): 161.
[8] XIAO Si-guo, LIU Zheng-wei(肖思国，刘政威). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2000, 20(4)：465.
[9] Gong X, Chen W J, Wu P F, et al. Applied Physics Letters, 1998, 73(20): 2875.
[10] Ostermayer F W，van der Ziel J P，Marcos H M, et al. Physical Review B, 1971, 3(8): 2698.
[11] Pollnau M. Th. Graf, Balmer J E, et al. Phys. Rev. A, 1994, 49: 3990.
[12] ZHAO Su-ling, HOU Yan-bing, PEI Xiao-jiang, et al(赵谡玲，侯延冰，裴晓将, 等). J. of Chinese Rare Earth Society(中国稀土学报)，待发表.
[13] Hewes R A. J. Luminescence, 1970, 1: 778.
[14] Sommerdijk J L. J. Luminescence, 1973, 6: 61.
|
| [1] |
WANG Chong1, WANG Jing-hua1, 2, LI Dong-dong1, SHE Jiang-bo2. Preparation of Gd3+-Doped LiYF4∶Yb3+/Ho3+ Micro-Crystal and the Application Research in Anti-Counterfeiting[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3581-3587. |
| [2] |
ZHANG Li-gang1, MA Li-hong1*, ZHAO Su-ling2, XU Zheng2, YANG Hai-jun1, LI Chen-pu1, WANG Ke1, LIU Gui-xia1, BAI Yong-qing1, SHEN Wen-mei1. Effect of Reaction Temperature on the Luminescence and Morphology of Na3ScF6∶Yb/Er Nanocrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3068-3072. |
| [3] |
WANG Chong1, MO Jian-ye1，2, LI Dong-dong1, SHE Jiang-bo2, LIU Zhen2. Application and Research of NaYF4∶Yb3+/Eu3+ Upconverting Luminescent Micro-Nano Particles in Anti-Counterfeiting Identification[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(05): 1525-1529. |
| [4] |
CHEN Xiao-bo1, LI Song1, ZHAO Guo-ying2, LONG Jiang-mi1, WANG Shui-feng1, MENG Shao-hua2, WANG Jie-liang1, GUO Jing-hua1, YOU Jia-jia1, MA Yu2, YU Chun-lei3, HU Li-li3. The Silver Surface Plasmon Enhancement for Er3+ Ion Upconversion of 978 and 1 539 nm Laser in Bismuth Glass[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2721-2726. |
| [5] |
WU Qi-xiao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, ZHANG Jun-jie1, 2, ZUO Peng-fei1, 2. Synthesis and Upconversion Mechanism of NaYF4∶Yb3+,Er3+ Nanocrystal Doped with Different Concentration of Sensitizer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(05): 1406-1411. |
| [6] |
CHEN Xiao-bo1, LI Song1, YU Chun-lei2, WANG Shui-feng1, ZHAO Guo-ying3, MA Hui1,ZHENG Dong1, YANG Guo-jian1, LIU Yuan1, DENG Zhi-wei1, HE Qing1, HU Li-li2. Intense Spectral Modulation by Quantum Cutting Luminescence of Er3+Yb3+ Ion-Pair in Nanophase Oxyfluoride Vitroceramics[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(06): 1949-1957. |
| [7] |
ZHANG Li-gang1，2, ZHAO Su-ling1*, XU Zheng1, ZHU Wei1, BAI Yong-qing2, QU Jiao2, FAN Hong2. The Controllable Synthesis and Luminescent Properties of ScF3, NaScF4, (NH4)2NaScF6 Nanaocrysals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(02): 401-406. |
| [8] |
CHEN Gan-xin1, CHENG Yun1*, QIAN Qi2. Energy Transfer Mechanism and Up-Conversion Emission Properties in Tm3+/Ho3+ Doped Tellurite Glasses[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(01): 302-307. |
| [9] |
HE En-jie1, DONG Jun2, GAO Wei2, ZHANG Zheng-long3. Upconversion Fluorescence Regulation of Single NaGdF4∶Yb3+,Er3+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(11): 3347-3353. |
| [10] |
WANG Zhen-xing, XUE Juan-qin, LI Di. Studies on the Ionic Liquid-Assisted Hydrothermal Synthesis of Zn2SnO4[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(04): 1198-1204. |
| [11] |
XU Shi-hua1, HUANG Zhong-jing1*, LIU Guo-cong2*, WEI Qing-min3 . Study on the Hydrothermal Synthesis and Fluorescence of LaF3∶Tb3+, Ce3+ Nanocrystals [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(03): 759-764. |
| [12] |
HAN Yu-ting1, XU Jing1, QIAO Shu-liang3, YANG Bo1, LI Li2, LIU Cai-hong2, YAO Shuang*, YAN Jing-hui1*, ZOU Ming-qiang2*. The Different Phase, Morphology Controllable Synthesis and Luminescent Properties Investigation of NaYF4∶Yb, Er[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(12): 3300-3304. |
| [13] |
CHEN Xiao-bo1, ZHOU Gu1, ZHOU Yong-fen2, WU Zheng-long1, GUO Yu-ying1, WANG Shui-feng1, ZOU Qiu-yan3, ZHUANG Jian4, 5, CHEN Xiao-duan1, LI Chun-mi1, YAO Wen-ting1, CHENG Huan-li1 . Near-Infrared Quantum Cutting Downconversion Luminescence of Yb3+ Ion Cooperative Energy Transferred from YVO4 Matrix Donor [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(02): 315-319. |
| [14] |
LI Rui-qin, QIU Jian-bei, YANG Zheng-wen*, LIAO Jia-yan, WU Hang-jun, LAI Shen-feng, SONG Zhi-guo, YANG Yong, ZHOU Da-cheng, WANG Rong-fei . Preparation and Up-Conversion Luminescence Properties of Yb3+/Tm3+ Co-Doped Sb2O4 Powder [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(03): 630-633. |
| [15] |
YAO Li-li, LUO Li*, DONG Guo-shuai，WANG Yin-hai . Crystal Structure and Upconversion Emission of Yb3+/Er3+-Co-Doped NaYF4 Nanocrystals [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2917-2920. |
|
|
|
|