钴基铁酸盐的室温合成和表征
王 静,邓 彤,冯亚萍,戴玉杰
中国科学院过程工程研究所,北京 100080
Synthesis and Characteristic of Cobalt Bearing Ferrite Particles at Room Temperature
WANG Jing,DENG Tong,FENG Ya-ping,DAI Yu-jie
Institute of Process Engineering, Chinese Academy of Sciences,Beijing 100080, China
摘要 : 采用氧化-沉淀法在室温下合成了不同钴含量的铁酸盐。不同反应时间时的样品的IR和XRD谱图分析表明,钴基铁酸盐是通过中间体绿锈形成的。通过调节初始溶液中Co/Fe比(Co/Fe分别为: 1/20, 1/15, 1/10, 1/7, 1/5, 1/3)合成了钴含量分别为Co/Fe=0.05, 0.06, 0.08,0.12,0.17,0.18的钴基铁酸盐,并通过IR, XRD, SEM和化学测定分析了上述铁酸盐的化学计量,结构和形貌。实验结果表明: 在室温条件下,随初始溶液中钴含量的增加,钴在尖晶石结构中占据八面体空隙中Fe3+ 的位置,且钴含量的增加不利于尖晶石结构的形成。
关键词 :钴;铁酸盐;氧化-沉淀
Abstract :Cobalt bearing magnetite particles were synthesized by aerial oxidation of ferrous and cobalt ions at alkaline condition and room temperature.The samples obtained at different time intervals during reaction were subjected to XRD and IR, and it was indicated that the cobalt-bearing ferrites were produced through green-rust intermediate phase.Different compounds were synthesized using 1/20, 1/15, 1/10, 1/7, 1/5 and 1/3 Co2+ /Fe2+ starting ratios, and Co-ferrites with Co/Fe of 0.05, 0.06, 0.08,0.12,0.17,0.18 were obtained.The chemical composition, microstructure and micrograph of those precipitates were characterized by chemical analysis, IR, XRD and SEM.The results revealed that Co2+ replaced Fe3+ at octahedral position in spinel structure, and the increase of Co in initial solution showed deleterious effect on the crystallinity of the precipitates.
Key words :Cobalt;Ferrite;Oxidation-precipitation
收稿日期: 2004-06-06
修订日期: 2004-09-16
通讯作者:
王 静
引用本文:
王 静,邓 彤,冯亚萍,戴玉杰 . 钴基铁酸盐的室温合成和表征[J]. 光谱学与光谱分析, 2005, 25(08): 1366-1370.
WANG Jing,DENG Tong,FENG Ya-ping,DAI Yu-jie. Synthesis and Characteristic of Cobalt Bearing Ferrite Particles at Room Temperature . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(08): 1366-1370.
链接本文:
https://www.gpxygpfx.com/CN/Y2005/V25/I08/1366
[1] Tamaura Y, Katsura T, Rojarayanont S.Water Sci.Technol., 1991, 23: 1893. [2] Oscar Perales Perez, Yoshiaki Umetsu,Hiroshi Sasaki.Hydrometallurgy, 1998,50: 223. [3] Oscar Perales Perez, Yoshiaki Umetsu.Hydrometallurgy,2000,55: 35. [4] Oscar Perales Perez, Kazuyuki Tohji, Yoshiaki Umetsu.Journal of Alloys and Compounds,1999,290: 129. [5] Midori Ueda, Shiro Shimada,Michio Inagaki.J.Mater.Chem., 1993, 3(2): 1199. [6] Rajendran M, Pullar R C,Bhattacharya A K.Journal of Magnetism and Magnetic Materials,2001,232: 71. [7] ZHU Huai-wu, ZHANG Chao-ping(朱淮武,张朝平).Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2004, 24(1): 25. [8] JIANG Zhi-liang, LIU Shao-pu, ZHAO Bao-gang, et al(蒋治良,刘绍璞,赵保刚,等).Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2002,22(4): 615. [9] Masao Kiyama.Bull.Chem.Soc.Japan, 1974,47(7): 1646. [10] Okano Y, Nakamura T.Colloids and Surfaces A: Physicochemical and Engineering Aspects,1998,139: 279. [11] Prieto F, Barrado E, Medina J, et al.Journal of Alloys and Compounds,2001,325: 269. [12] Chin-Lin Huang, Egon Matijevic.Solid State Ionics,1996,84: 249.
[1]
陶隆凤,史 淼,徐丽娟,韩秀丽,刘倬君. 天然钴尖晶石的谱学特征及颜色成因 [J]. 光谱学与光谱分析, 2022, 42(07): 2130-2134.
[2]
. 深海富钴结核微区X射线荧光光谱分析和数据挖掘 [J]. 光谱学与光谱分析, 2021, 41(06): 1834-1840.
[3]
. 基于吸收系数的生脉注射液中聚山梨酯80含量测定新方法 [J]. 光谱学与光谱分析, 2019, 39(01): 199-203.
[4]
. 一种高锌背景下痕量钴离子浓度分光光度测量法 [J]. 光谱学与光谱分析, 2017, 37(12): 3882-3888.
[5]
. 基于变温紫外分光光度法研究温度对DNA凝聚过程影响 [J]. 光谱学与光谱分析, 2017, 37(06): 1831-1837.
[6]
张秀清;彭 君;凌 剑*;刘朝娟;曹秋娥;丁中涛 . 基于银纳米三角片与罗丹明6G的荧光共振能量转移法检测钴离子 [J]. 光谱学与光谱分析, 2015, 35(04): 951-955.
[7]
薛娟琴;毕 强;赵 肖;马 晶;于丽花;张 桀 . 四氨基钴酞菁紫外-可见光谱量子化学研究 [J]. 光谱学与光谱分析, 2014, 34(01): 141-144.
[8]
许孝芳;高永锋;吕 柳;曹祥祥;任乃飞;周 明 . Co膜中多次超快瞬态反射突变现象研究 [J]. 光谱学与光谱分析, 2013, 33(12): 3278-3281.
[9]
薛娟琴;赵 肖;马 晶;刘 瑶;汪 从;李京仙 . 四氨基钴酞菁的分子结构和红外光谱量子化学研究 [J]. 光谱学与光谱分析, 2013, 33(04): 959-962.
[10]
张 婧;胡 林*;刘艳辉;张碧程 . DNA凝聚性质的紫外光谱研究 [J]. 光谱学与光谱分析, 2012, 32(05): 1306-1309.
[11]
杨 伟;陈胜洲*;邹汉波;林维明; . 氮掺杂碳载钴催化剂制备及其TG-FTIR和XRD光谱分析 [J]. 光谱学与光谱分析, 2012, 32(04): 1114-1117.
[12]
李 雷;金 晶;史忠丰;邢永恒;牛淑云* . 光诱导下系列钴配合物的表面电子行为对比研究 [J]. 光谱学与光谱分析, 2010, 30(09): 2443-2446.
[13]
李金焕;艾仕云*;时伟杰;殷焕顺;杜红霞. 金属钴树状高分子与DNA相互作用的光谱法研究 [J]. 光谱学与光谱分析, 2009, 29(03): 726-729.
[14]
傅秋莲;蒋晓瑜;陈文哲;*. 柠檬酸溶胶凝胶法合成LiCoO2 的晶体结构研究 [J]. 光谱学与光谱分析, 2008, 28(06): 1222-1226.
[15]
黄焱;徐国兴*;彭亦如*;翁家宝;. 四磺基酞菁钴合成及其与牛血清白蛋白结合作用的研究 [J]. 光谱学与光谱分析, 2008, 28(02): 407-411.