Infrared Spectral Fitting Analysis of Barium Ferrite Precursor in High Energy Ball Milling Process
YI Shi-wen1, LI Jie1, 2*, WU Jing-xuan1, ZHANG Wen-hao1, ZU Peng1, LI Min1, LIN Jia-wei1
1. School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resource, Baotou 014010, China
2. Key Laboratory of New Metal Materials of Inner Mongolia Autonomous Region, Inner Mongolia University of Science and Technology, Baotou 014010, China
Abstract：High energy ball milling method was a common method in the process of material preparation, which produced crystal vacancy defects through the material running with high speed to achieve the doping of elements, so the chemical adsorption or chemical reaction has occurred. New phase formed, and it has a great impact on the performance of subsequent synthetic materials. Barium ferrite has been used in many functional materials because of its good magnetic properties. In the paper, barium ferrite precursor was prepared by the high energy ball mill method. Using XRD, SEM and FTIR methods, the changes in phase, microstructure and functional groups of barium ferrite precursor with different high energy ball milling times were investigated. By the second derivative infrared spectroscopy and smooth fitting calculation method, the phase changes were quantitatively analyzed in the process of high-energy ball mill of materiel. XRD and SEM results show that with the increase of ball milling time, the diffraction peak width of each phase of the barium ferrite precursor becomes wider, the powder is refined, the crystal lattice is gradually distorted, and crystal vacancy defects are produced, so that Ba dissolves into the Fe2O3 lattice to produce the solid solution of BaxFe2-xO3, and the adsorption “agglomeration” is produced phenomenon. When the milling time was longer than 40 h, the “nano-size effect” occurred, and magnetic Fe3O4 and BaxFe3-xO4 solid solutions were generated. The results of infrared spectrum analysis showed that the characteristic peaks of BaCO3 and α-Fe2O3 decreased and shifted significantly with the increase of ball milling time, indicating that the particle size of decreased and chemical reactions occurred with the increase of ball milling time. The smooth fitting spectrum and the second derivative spectrum of the infrared spectrum showed that the area of each absorption peak decreased obviously with the increase of the milling time. Compared with that of ball milling under 0h, after ball milling for 10, 20 and 40 h, the vibration absorption peak area of Fe—O bond at 473 cm-1 decreased by 48.84%, 65.97% and 93.54%, respectively, and at 540 cm-1, the absorption peak area of the Fe—O bond decreased by 37.11%, 51.76% and 82.85%, respectively. Similarly, the absorption peak area of in-plane bending vibration of the O—C—O bond at 856 cm-1 was 30.62%, 44.71% and 67.10%, respectively, and the peak area of C—O bond asymmetric stretching vibration at the wavenumber of 1 446 cm-1 decreased by 0.03%, 27.63% and 57.90%, respectively, compared with that of ball milling at 0 h. In this way, the phase changes of barium ferrite precursors during high energy ball milling were investigated, and the percentage changes of reaction product content were accurately determined based on quantitative analysis, which has important guiding significance for the research on the changes in subsequent materials synthesis and properties with the phase changes of barium ferrite precursor.
Key words：Barium ferrite precursors; High energy ball milling; Spectral fitting; Second derivative spectrum
弋诗文，李 解，武靖轩，张文浩，祖 鹏，李 敏，林嘉威. 钡铁氧体前驱体高能球磨过程的红外拟合光谱分析[J]. 光谱学与光谱分析, 2022, 42(05): 1634-1641.
YI Shi-wen, LI Jie, WU Jing-xuan, ZHANG Wen-hao, ZU Peng, LI Min, LIN Jia-wei. Infrared Spectral Fitting Analysis of Barium Ferrite Precursor in High Energy Ball Milling Process. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(05): 1634-1641.
[1] CHANG Jing-yu，KONG Di，MA Zhen-zhen, et al（常靖宇，孔 迪，马振振，等）. Journal of Synthetic Crystals（人工晶体学报），2017，46(9)：1786.
[2] WANG Chun-man，PENG Zhi-jian，WANG Cheng-biao, et al（汪春满，彭志坚，王成彪, 等）. Rare Metal Materials and Engineering（稀有金属材料与工程），2018，47(S1)：179.
[3] Hu S L, Liu J, Yu H Y，et al. Journal of Magnetism and Magnetic Materials，2019，473：79.
[4] MA Zhi-jun，ZHAO Hai-tao，MANG Chang-ye, et al（马志军，赵海涛，莽昌烨, 等）. Journal of Synthetic Crystals（人工晶体学报），2019，48(11)：2080.
[5] WU Zhi-fang，LIU Chao，ZHOU Fan（吴志方，刘 超，周 帆）. Powder Metallurgy Industry（粉末冶金工业），2016，26(2)：58.
[6] ZHONG Bin，ZHANG Lin，LI Xue-wu（钟 斌，张 林，李雪伍）. Journal of Functional Materials（功能材料），2020，51（7）：7092.
[7] WANG Jing-min，ZHANG Jing-chao，ZHANG Zun-ju（王静敏，张景超，张尊举）. Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2019，39(1)：161.
[8] WEN Lu，LIANG Wan-xue，ZHANG Zheng-gang, et al（闻 辂，梁婉雪，章正刚, 等）. Mineral Infrared Spectroscopy（矿物红外光谱学）. Chongqing：Chongqing University Press（重庆：重庆大学出版社），1988.
[9] GUAN Ye-bin，TU You-zhi，WANG Xiao-hong, et al（官叶斌，涂友志，汪小红, 等）. Bulletin of the Chinese Ceramic Society（硅酸盐通报），2018，37(5)：1605.
[10] Rufus A，Sreeju N，Philip D. RSC Advances，2016，6(96)：94206.
[11] WENG Shi-fu，XU Yi-zhuang（翁诗甫，徐怡庄）. Fourier Transform Infrared Spectrum Analysis（傅里叶变换红外光谱分析）. Beijing：Chemical Industry Press（北京：化学工业出版社），2016.