| Preparation and Photocatalytic Properties of Supported TiO2 Photocatalytic Material |
| GUO Yu, JIN Yu-jia, WU Hong-mei, LI Dong-xin |
| School of Chemical and Environmental Engineering, Liaoning University of Technology, Jinzhou 121001, China |
|
|
|
|
Abstract Titanium dioxide (TiO2) supported on spherical alumina substrate was prepared by using sol-gel method combined with dip-coating process. The surface morphology and structure of the synthesized samples were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD) pattern. The results show that the morphology of the supported TiO2 composite material was obviously different from that of the original support. It reveals a layer formed by anatase TiO2 nanoparticles of 10～20 nm was deposited on the alumina substrate. Energy dispersive X-ray spectroscopy (EDX) analyses on the spherical alumina substrate and the resulting TiO2 composite catalyst were performed to determine the TiO2 loading content in the samples. It indicates that the TiO2 loading content on alumina substrate could be effectively increased by increasing the times of dip-coating alumina support in TiO2 sol. When dip-coating times increased to 5, the TiO2 loading content increased from 3.8 Wt.% to 15.7 Wt.%. In addition, the photocatalytic performances of the supported TiO2 materials prepared by different dip-coating times have been investigated by degrading methylene blue. It was found that the surface morphology of the supported TiO2 material was not only improved, but also the photocatalytic activity could be promoted significantly by increasing the dip-coating times. When the alumina substrate was dip-coated in TiO2 sol from 1 to 4 times, the degradation rate of methylene blue increased from 40% to 83.1%. However, after dip-coating the alumina support in TiO2 sol for 5 times, the degradation of methylene blue was only up to 85.6%. This indicates that the photocatalytic activity increased slowly when the TiO2 content in the supported catalyst was up to some extent. It is attributed to the continuous dip-coating resulted in less opportunities and weak intensity of illumination for the TiO2 nano-particles that under lower layer. The photocatalytic activity was relatively stable after repeated use of the supported TiO2 material for 5 times.
|
|
Received: 2014-06-09
Accepted: 2014-10-12
|
|
|
|
Corresponding Authors:
GUO Yu
E-mail: guoyulnut@163.com
|
|
[1] Yu J G, Li Q L, Shu Z. Electrochim. Acta, 2011, 56(18): 6293.
[2] Hoffmann M R, Martin S T, Choi W, et al. Chem. Rev., 1995, 95(1): 69.
[3] Liu Y, Sun D Z. Appl. Catal. B-Environ., 2007, 72: 205.
[4] Fahim N F, Sekino T. Chem. Mater., 2009, 21: 1967.
[5] Wang W G, Yu J G, Xiang Q J, et al. Appl. Catal. B-Environ., 2012, 119: 109.
[6] Wen C Z, Jiang H B, Qiao S Z, et al. J. Mater. Chem., 2011, 21(20): 7052.
[7] Koparde V N, Cummings P T. ACS Nano, 2008, 2(8): 1620.
[8] Xu X Y, Yin D H, Wu S F et al. Ceram. Int., 2010, 36(2): 443.
[9] Ho W, Yu J C, Yu J. Langmuir, 2005, 21(8): 3486.
[10] LIU Yan, LIANG Pei, GUO Li, et al(刘 艳, 梁 沛, 郭 丽, 等). Acta Chimica Sinica(化学学报), 2005, 63(4): 312.
[11] Huang C F, Zhu M Y, Kang L H, et al. Chem. Eng. J., 2014, 242: 69.
[12] Zhang H B, Li K, Sun T H, et al. Chem. Eng. J., 2014, 241: 92.
[13] Lee S W, Paraguay-Delgado F, Arizabalo R D, et al. Mater. Lett., 2013, 107: 10.
[14] Torimoto T, Ito S, Kuwabata S, et al. Environ. Sci. Technol., 1996, 30: 1275.
[15] Anderson M R, Mattes B R, Reiss H, et al. Science, 1991, 252: 1412. |
| [1] |
LIU Jun-shao1, HUANG Lei2, XIE Wen-ju1, LIN Hao1, CHEN Yi-ping2, PAN Hai-bo2*. Preparation of Four Phenoxy Phthalocyanine Zinc/ZnO Composites with in-situ Method by DBU Liquid Phase Catalyst and Its Photocatalytic Selectivity[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(05): 1486-1491. |
| [2] |
XUE Juan-qin1, DAI Ji-zhe2, WANG Zhen-xing1, LI Di1. Spectral Characteristic of Graphene Modified Zinc Stannate Materials and It’s Photocatalytic Properties[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(04): 1219-1224. |
| [3] |
ZHANG Xiao-lei, ZHU Yong*, DING Yi-min, ZHANG Jie. TiO2/Graphene/Ag Composite Structure for Surface-Enhanced Raman Scattering[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(11): 3441-3445. |
| [4] |
MA Hui-yan1,2, ZHOU Dan1, LIU Ju-ming2, ZHANG Qian-cheng1,2*. Preparation and Spectral Characteristics of SO2-4/CeO2-TiO2 Photocatalyst[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(10): 3315-3320. |
| [5] |
CHEN Jun-yu, JIANG Gui-min, TENG Yuan, CHEN Dong-dong, YAN Ji-kang*, GAN Guo-you. Research on Infrared Spectra of (Fe, N) Doped TiO2 by the Electronegativity Principle[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 2305-2310. |
| [6] |
WANG Zhen-xing, XUE Juan-qin, LI Di. Studies on the Ionic Liquid-Assisted Hydrothermal Synthesis of Zn2SnO4[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(04): 1198-1204. |
| [7] |
KANG Le, ZHANG Yao-jun*, ZHANG Li, ZHANG Ke, YANG Meng-yang . Preparation and Photocatalytic Activity of CeO2 Loaded Porous Alkali-Activated Steel Slag-Based Catalyst[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 875-880. |
| [8] |
LI Li-xia1, 2, CAO Bing1, 2*, SUN Yu-meng1, 3, LI Hong-yan1, 2, XIAO Qiang1, 2, NI Xiao-hui1, 2, YI Wen-ping1, 2 . Infrared Spectrum Studies of Coatings under Irradiation of Sunlight and Ultraviolet [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3159-3162. |
| [9] |
CUI Yu-min, LI Hui-quan, MIAO Hui, TAO Dong-liang, FAN Su-hua . The Latest Research Progress of Coupling between BiOX and Semiconductor Photocatalyst[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(08): 2579-2584. |
| [10] |
ZHONG Xiao-li1，2，HAN Xiao-xia1，RUAN Wei-dong1*，YANG Xu-wei2*. Surface-Enhanced Raman Scattering Study on Photocatalysis of PATP When Adsorbed on Ag/TiO2 Nanotubes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(06): 1740-1744. |
| [11] |
WANG Kai1, 2, YAO Wen-qing1*, TENG Fei2*, ZHU Yong-fa1. Study on Photocatalytic Performance of LaPO4 Nanorods with Different Crystal Phases[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(05): 1440-1444. |
| [12] |
MA Hui-yan, LIU Zheng-jiang, CHENG Lin, YANG Ju-cai, ZHANG Qian-cheng* . Spectral Characteristics and Catalytic Performances of SO2-4/Ce-TiO2 with Visible Light Response [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(04): 1133-1138. |
| [13] |
QIU Zhi-che, GU Mu*, LIU Xiao-lin, LIU Bo, HUANG Shi-ming, NI Chen . Preparation and Performances of the M′-Type LuTaO4∶Eu3+ Transparent Scintillator Films[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(02): 336-339. |
| [14] |
HAN Zhi-zhong1, 2, REN Li-li2, PAN Hai-bo2*, LI Chun-yan1, CHEN Jing-hua1, CHEN Jian-zhong2 . Spectral Analysis of CdZnSe Ternary Quantum Dots Sensitized TiO2 Tubes and Its Application in Visible-Light Photocatalysis [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(11): 3161-3166. |
| [15] |
ZHOU Jing-rong1, DENG Dong-yan1, HUANG Ke1, TIAN Yun-fei2*, HOU Xian-deng1,2* . Simultaneous Determination of Se and Te in Ores by HG-AFS After Online Preconcentration with Nano-TiO2 Immobilized on Silica Gel[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(09): 2401-2406. |
|
|
|
|