Research on the Synthesis and Luminescence Characterization of Deepen Red Emission Novel Polymer |
CHENG Zhi-ming1, XU Zheng1*, FU Qiang2, ZHAO Su-ling1, ZHANG Fu-jun1 |
1. Key Laboratory of Luminescence and Optical Information (Beijing Jiaotong University), Ministry of Education,Beijing 100044,China 2. College of Physics, Liaoning University, Shenyang 110036,China |
|
|
Abstract A deep red emission polymer (PPV-Q) was synthesized successfully. The photoluminescence, electroluminescence and absorption performance of this polymer were studied in detail. The experimental results show that the polymer has strong absorption in the ultraviolet and blue emission wavelength region. The effective excitation wavelength is about 463 nm. The organic emitting diodes based on the polymer as the active layer were prepared with the device structure: ITO/PPV-Q/Al. The electroluminescence of these devices was obtained and the peak emission wavelength is about 670 nm; the electroluminescence spectra have the full width at half maximum of about 90 nm. The CIE coordinate remains constant at (x=0.67, y=0.32) without change with the increase in driving voltage. The electroluminescence of this device (ITO/PPV-Q/Al) shows deep red emission. However, the current increases with the increase in driving voltage.
|
Received: 2009-02-26
Accepted: 2009-05-18
|
|
Corresponding Authors:
XU Zheng
E-mail: zhengxu@bjtu.edu.cn
|
|
[1] Zhang F J, Voller A, Zhang J, et al. Organic Electronics, 2007, 8(5): 606. [2] Coe S, Woo W K, Steckel J S, et al. Organic Electronics, 2003, 4: 123. [3] Zhao J L, Zhang J Y, Jiang C Y, et al. J. Appl. Phys., 2004, 96: 3206. [4] Zhao J L, Bardecker J A, Munro A, et al. Nano Lett., 2006, 6: 463. [5] ZHANG Fu-jun, XU Zheng, HUANG Jin-zhao, et al(张福俊,徐 征,黄金昭,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(8): 1403. [6] Baldo M A, Lamansky S, Burrows P E, et al. Appl. Phys. Lett. 1999, 75: 4. [7] Zhang F J, Xu Z, Wang Y S, et al. J. Phys. D: Appl. Phys., 2007, 40: 4485. [8] Sentein C, Fiorini C, Lorin A. Adv. Mater., 1997, 9: 809. [9] Lu G H, Li L G, Yang X N. Adv. Mater., 2007, 19: 3594. |
[1] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
[2] |
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763. |
[3] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326. |
[4] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Properties of Phosphorescent Organic Light-Emitting Diodes with Different Doping Order on Light Emitting Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1763-1766. |
[5] |
MA Zhu1, YU Jun-sheng1*, JIANG Long-feng1, DONG Shou-cheng2, LI Zhen2*, HU Song3 . Spectra Characteristics and Electroluminescence Performance of Novel Fluorene Derivatives with Aggregation Fluorescence Enhancement[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(04): 935-939. |
[6] |
LIU Sheng-qiang1, YU Jun-sheng1*, ZENG Yan-bo1, ZHAO Juan1, DU Chun-lei2 . Spectral Characteristics of White Organic Light-Emitting Devices Based on Phosphorescent System of Three Iridium Chelates [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(03): 636-641. |
[7] |
ZHANG Chun-yu1,2, WANG Cheng3, XIAO Li-guang1, LU Jing-bin2, WANG Hong-jie1, KONG Ling-wei1 . Spectral Analysis of Organic/Microcavity Organic Light-Emitting Devices with the Change in Thickness of Organic Layer [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(01): 69-73. |
[8] |
LI Juan1, 2, WANG Hua1, 2, SONG Chun-li1, 2, ZHANG Cun1, 2, ZHANG Jun-ping1, 2, HAO Yu-ying1, 3, XU Bing-she1, 2* . Research on Synthesis and Luminous Mechanism of a Soluble Blue-Light Luminescence Material Derived from Carbazole [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(08): 2071-2075. |
[9] |
ZHAO Juan, YU Jun-sheng*, WEN Wen, JIANG Ya-dong . Electroluminescent Performance and Spectral Characteristics of a Novel (t-bt)2Ir(acac) Phosphorescent Iridium Complex [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(05): 1189-1192. |
[10] |
XU Deng-hui . Fabrication and Analysis of the Organic Light-Emitting Diode with Liquid Host Material [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(05): 1204-1207. |
[11] |
GAO Li-yan, ZHAO Su-ling*, XU Zheng, ZHANG Fu-jun, SUN Qin-jun, ZHANG Tian-hui, KONG Chao . Effects of Hole-Injection Layers on the Performance of Blue Organic Light-Emitting Diodes [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(04): 886-889. |
[12] |
XU Deng-hui1,LI Xiong1,WANG Xiu-e1,ZHAO Ci1,ZHAO Jia1,DENG Zhen-bo2,Lü Zhao-yue2,CHEN Zheng2 . Effect of Rubrene Position on the EL Performance of the Device and Analysis of the Exciton Recombination Zone [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(02): 340-343. |
[13] |
ZHANG Chun-yu1,2, LU Jing-bin2*,WANG Cheng3,WANG Hong-jie1 . Simulation of Microcavity Organic Light Emitting Device with Two Kinds of Resonant Cavity Lengths [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(01): 47-50. |
[14] |
LU Lin,LIAO Ying-jie,LIU Ji-zhong,WEI Bin*,ZHANG Jian-hua . Highly Efficient and Chromatic-Stability Yellow Organic Light Emitting Diodes Using Double Ultra Thin Yellow Emissive Layers [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(08): 2053-2056. |
[15] |
LIU Xiao-dong, ZHANG Fu-jun*, XU Zheng, ZHAO Su-ling, SONG Jing-lu, LI Jun-ming, SONG Dan-dan, WANG Yong-sheng. Influence of the Active Layer Thickness on the Performance of Bulk Heterojunction Solar Cell [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(07): 1752-1755. |
|
|
|
|