| Photoluminescence from Bis-t-Butylbenzoxazolylthiophene Doped Silica Films |
| WANG Jun-ling1, HE Zhi-qun1*, WANG Yong-sheng1, MU Lin-ping1, YE Shi2, JING Xi-ping2 |
1. Key Laboratory of Luminescence and Optical Information, Ministry of Education, Institute of Optoelectronic Technology, Beijing Jiaotong University, Beijing 100044, China
2. The State Key Laboratory of Rare Earth Materials Chemistry and Applications, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China |
|
|
|
|
Abstract Thin nano-porous silica films doped with high concentrations of fluorescent material, 2,5-bis(5-tert-butyl-2-benzoxazolyl)-thiophene (BBOT) were prepared via a sol-gel process. Uniform and bright blue fluorescence was observed. Light emission properties of these organic molecule doped inorganic silica films, i.e., hybrid films, were measured using ultraviolet-visible (UV-Vis) absorption spectroscopy, steady and time-resolved fluorescence spectroscopy as well as optical microscopy. Features of these materials were revealed in this investigation: Firstly, photoluminescence intensity from BBOT doped silica films increased linearly as the concentrations of BBOT increased if the dopant concentration was relatively low and below 6×10-3 mol·L-1; Secondly, no molecular aggregation or phase separation was observed using optical microscopy when the BBOT concentration was below 6×10-3 mol·L-1 in BBOT doped silica films. Thirdly, the fluorescence lifetimes of BBOT in the doped silica films were longer than that in a dilute dioxane solution (1.957 ns), which was contradicted to our general understanding that the fluorescence lifetime may be reduced in a condensed matter due to molecular interactions or quenching. It was further found that the fluorescence lifetime also varied with the gelation conditions. Taking a BBOT concentration of 6×10-3 mol·L-1 for an example, the lifetime of BBOT in doped silica films was about 2.45 ns for a specimen polymerized at 50 ℃; while the lifetime was increased to 3.04 ns for a specimen polymerized at 90 ℃. This work demonstrates no concentration quenching when the BBOT dopant concentrations increased to as high as 6×10-3 mol·L-1 in the silica matrix. In comparison with the changes in time-resolved photoluminescence of BBOT in dioxane solution and that of the BBOT doped nano-porous silica in relation to their concentration dependence and the gelation conditions, it was found that concentration quenching can be effectively suppressed by the nano-porous silica matrix. A stable fluorescent organic-inorganic hybrid material is thus obtained.
|
|
Received: 2008-03-16
Accepted: 2008-06-20
|
|
|
|
Corresponding Authors:
HE Zhi-qun
E-mail: zhqhe@bjtu.edu.cn
|
|
[1] Stracke F, Heupel Ma, Thiel E. Journal of Photochemistry and Photobiology A: Chemistry, 1999, 126(1-3): 51.
[2] Galanin M D. Luminescence of Molecules and Crystals, Cambridge: Cambridge Internal Science Pub., 1996.
[3] Sakakibara Y, Okutsu S, Enokida T, et al. Applied Physics Letters, 1999, 74(18): 2587.
[4] Lutz D R, Nelson K A, Gochanour C R, et al. Chemical Physics, 1981, 58(3): 325.
[5] López I Arbeloa. Journal of Photochemistry, 1982, 18(2): 161.
[6] López F Arbeloa, Ruiz P Ojeda, López I Arbeloa. Journal of Photochemistry and Photobiology, A: Chemistry, 1988, 45(3): 313.
[7] Bera R N, Sakakibara Y, Abe Sh, et al. Synthetic Metals, 2005, 150(1): 9.
[8] CAO Duxia, LIU Zhiqiang, ZHAO Guohui, et al. Dyes and Pigments, 2008, 76(1): 118.
[9] ZHONG Xian-qiong, YANG Jing-guo, HA Yuan-qing, et al(钟先琼，杨经国，哈元清，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2001, 21(4): 450.
[10] WANG Jun-ling, HE Zhi-qun, MAO Hua-xiang, et al. Journal of Luminescence, 2007, 122-123: 268.
[11] DONG Wenting, ZHU Congshan. Materials Letters, 2000, 45(6): 336.
[12] Johnston C T. Philosophic Degree of Dissertation, University of California, Riverside, CA, 1983.
[13] Casalboni M, Senesi R, Prosposito P, et al. Applied Physics Letters, 1997, 70(22): 2969.
[14] ZHENG Wei, HUANG Zhi-wei, XIE Shu-sen, et al(郑蔚，黄志伟，谢树森，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 1997, 17(3): 20.
[15] CHEN Bi-fang, LIU Tian-fu(陈碧芳，刘天夫). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(8): 1513.
|
| [1] |
LEI Hong-jun1, YANG Guang1, PAN Hong-wei1*, WANG Yi-fei1, YI Jun2, WANG Ke-ke2, WANG Guo-hao2, TONG Wen-bin1, SHI Li-li1. Influence of Hydrochemical Ions on Three-Dimensional Fluorescence
Spectrum of Dissolved Organic Matter in the Water Environment
and the Proposed Classification Pretreatment Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 134-140. |
| [2] |
XIA Ming-ming1, 2, LIU Jia3, WU Meng1, 2, FAN Jian-bo1, 2, LIU Xiao-li1, 2, CHEN Ling1, 2, MA Xin-ling1, 2, LI Zhong-pei1, 2, LIU Ming1, 2*. Three Dimensional Fluorescence Characteristics of Soluble Organic Matter From Different Straw Decomposition Products Treated With Calcium Containing Additives[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 118-124. |
| [3] |
GU Yi-lu1, 2，PEI Jing-cheng1, 2*，ZHANG Yu-hui1, 2，YIN Xi-yan1, 2，YU Min-da1, 2, LAI Xiao-jing1, 2. Gemological and Spectral Characterization of Yellowish Green Apatite From Mexico[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 181-187. |
| [4] |
HAN Xue1, 2, LIU Hai1, 2, LIU Jia-wei3, WU Ming-kai1, 2*. Rapid Identification of Inorganic Elements in Understory Soils in
Different Regions of Guizhou Province by X-Ray
Fluorescence Spectrometry[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2024, 44(01): 225-229. |
| [5] |
LIU Wei1, 2, ZHANG Peng-yu1, 2, WU Na1, 2. The Spectroscopic Analysis of Corrosion Products on Gold-Painted Copper-Based Bodhisattva (Guanyin) in Half Lotus Position From National Museum of China[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3832-3839. |
| [6] |
WANG Hong-jian1, YU Hai-ye1, GAO Shan-yun1, LI Jin-quan1, LIU Guo-hong1, YU Yue1, LI Xiao-kai1, ZHANG Lei1, ZHANG Xin1, LU Ri-feng2, SUI Yuan-yuan1*. A Model for Predicting Early Spot Disease of Maize Based on Fluorescence Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3710-3718. |
| [7] |
CHENG Hui-zhu1, 2, YANG Wan-qi1, 2, LI Fu-sheng1, 2*, MA Qian1, 2, ZHAO Yan-chun1, 2. Genetic Algorithm Optimized BP Neural Network for Quantitative
Analysis of Soil Heavy Metals in XRF[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3742-3746. |
| [8] |
SONG Yi-ming1, 2, SHEN Jian1, 2, LIU Chuan-yang1, 2, XIONG Qiu-ran1, 2, CHENG Cheng1, 2, CHAI Yi-di2, WANG Shi-feng2，WU Jing1, 2*. Fluorescence Quantum Yield and Fluorescence Lifetime of Indole, 3-Methylindole and L-Tryptophan[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3758-3762. |
| [9] |
WANG Zhi-qiang1, CHENG Yan-xin1, ZHANG Rui-ting1, MA Lin1, GAO Peng1, LIN Ke1, 2*. Rapid Detection and Analysis of Chinese Liquor Quality by Raman
Spectroscopy Combined With Fluorescence Background[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3770-3774. |
| [10] |
YI Min-na1, 2, 3, CAO Hui-min1, 2, 3*, LI Shuang-na-si1, 2, 3, ZHANG Zhu-shan-ying1, 2, 3, ZHU Chun-nan1, 2, 3. A Novel Dual Emission Carbon Point Ratio Fluorescent Probe for Rapid Detection of Lead Ions[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3788-3793. |
| [11] |
YANG Ke-li1, 2, PENG Jiao-yu1, 2, DONG Ya-ping1, 2*, LIU Xin1, 2, LI Wu1, 3, LIU Hai-ning1, 3. Spectroscopic Characterization of Dissolved Organic Matter Isolated From Solar Pond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3775-3780. |
| [12] |
QI Guo-min1, TONG Shi-qian1, LIN Xu-cong1, 2*. Specific Identification of Microcystin-LR by Aptamer-Functionalized Magnetic Nanoprobe With Laser-Induced Fluorescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3813-3819. |
| [13] |
HE Yan-ping, WANG Xin, LI Hao-yang, LI Dong, CHEN Jin-quan, XU Jian-hua*. Room Temperature Synthesis of Polychromatic Tunable Luminescent Carbon Dots and Its Application in Sensitive Detection of Hemoglobin[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3365-3371. |
| [14] |
LIN Hong-jian1, ZHAI Juan1*, LAI Wan-chang1, ZENG Chen-hao1, 2, ZHAO Zi-qi1, SHI Jie1, ZHOU Jin-ge1. Determination of Mn, Co, Ni in Ternary Cathode Materials With
Homologous Correction EDXRF Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(11): 3436-3444. |
| [15] |
LI Xiao-li1, WANG Yi-min2*, DENG Sai-wen2, WANG Yi-ya2, LI Song2, BAI Jin-feng1. Application of X-Ray Fluorescence Spectrometry in Geological and
Mineral Analysis for 60 Years[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 2989-2998. |
|
|
|
|