Preparation and Characteristics of A Novel Cu(Ⅱ)-Imprinted Epoxy Resin-Based Monolithic Polymer
HOU Lin-xi, GUO Zhi-yong, WANG Sui*
State Key Laboratory Base of Novel Functional Materials and Preparation Science, Faculty of Material Science and Chemical Engineering, Ningbo University, Ningbo 315211, China
Abstract：A novel Cu(Ⅱ)-imprinted monolithic polymer was prepared by step-polymerization reaction of epoxy resin. A homogenous mixture of epoxy resin, diethylenetriamine as curing agent, copper ion as target molecule and polyethylene glycol as pore-forming reagent was poured into a glass-tube and polymerized under controlled reaction temperature and time. The PEG and copper ions were all removed from the solid product by deionized water and strong acid, respectively. The Cu(Ⅱ)-imprinted epoxy resin-based monolithic porous polymer was successfully obtained, which was used as solid-phase extraction matrix for preconcentration and separation of trace copper ions in aqueous solution for determination by atomic adsorption spectrometry. The effect of pH on adsorption, maximum adsorption capacity, selectivity, analytical precision and availability was investigated in details by a series of experiments. Under the optimized enrichment conditions, i.e. pH 5.0-9.0 of medium and flow rate below 5.0 mL·min-1,the recovery of Cu(Ⅱ) ions in the aqueous solution could be over 95%. The maximum adsorption capacity is 126 mg Cu(Ⅱ)·g-1 dried resin. The selective recognition ability of Cu(Ⅱ)-imprinted monolithic column is evidently preponderant over the non-imprinted materials. The up-loaded column could be completely eluted with 1.0 mol·L-1 HNO3 and flow rate below 2.0 mL·min-1. The proposed procedure was applied to the analysis of a mixed sample with satisfied result.
[1] GU Cong-ying，LIN Li，FANG Neng-hu(谷从影，蔺 丽，方能虎). Chemical Research and Application(化学研究与应用)，2005，17(3)：281. [2] CHEN Guo-liang，ZHANG Xiao-hui，SHANG De-fa，et al(陈国良，张晓慧，商德发，等). Chinese Journal Analytical Chemistry(分析化学)，2006，34(10)：1496. [3] BAO Xiao-ling，XU Xu(鲍笑岭, 许 旭). Chinese Journal Analytical Chemistry(分析化学)，2005，33(11)：1653. [4] Branovic K, Forcic D, Ivancic J, et al. J. Virological Methods,2003，110：163. [5] Nordborg A, Svec F, Fréchet J M J, et al. J. Sep. Sci.,2005，28：2401. [6] Barut M, Podgornik A, Brne P, et al. J. Sep. Sci.,2005，28：1876. [7] Wang S, Zhang R F. Anal. Chem. Acta,2006, 575(2)：166. [8] Tsujioka N, Hira N, Aoki S, et al. Macromolecules，2005，38(24)：9901. [9] Dominic S P, Thomas R, Frantisek S. Anal. Chem.,2003, 75：5328. [10] Aimin T, Salete B, Jack D H. Anal. Chem.,2003，75：550. [11] Shota M, Kei M, Norio I. J. Chromatogr., A,2004, 1043：19. [12] Molochnikov L S, Kovalyova E G, Zagorodni A A, et al. Polymer，2003，44：4805. [13] Ersz A，Say R，Denizli A. Anal. Chem. Acta,2004，502：91. [14] Gladis J M，Rao T P. Microchim. Acta，2005，146(3-4)：251. [15] L Yun-kai, YAN Xiu-ping(吕运开，严秀平). Chinese J. Anal. Chem.(分析化学)，2005，33(2)：254. [16] ZHU Xiao-lan，YANG Jun，SU Qing-de，et al(朱晓兰，杨 俊，苏庆德，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(10): 1817. [17] Norrlw O, Glad M, Mosback K. J. Chromatogr.，1984，299：29. [18] Shea K J, Sasaki D Y. J. Am. Chem. Soc.，1989，111：3442. [19] XIAO Shan-mei, CHEN Jian-rong, SHEN Yu-qin(肖珊美，陈建荣，沈玉勤). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(5): 955. [20] SU Yao-dong，LI Jing，HUANG Yan，et al(苏耀东，李 静，黄 燕，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2006,26(3): 564.