Spectral Analysis of the Effects of γ-Irradiation on Gadolinium-Containing Barium Phosphate Glass
YU Tao1, 2, 3, WANG Jun-xia3, LIU Hai-feng2, LIANG Xiao-feng1, 2, 3*, YANG Shi-yuan3, LUO Qing3
1. Medical Institute Department of Sichuan College of Traditional Chinese Medicine, Mianyang 621000, China
2. Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621000, China
3. School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621000,China
Abstract:The xGd2O3-(50-x)BaO-50P2O5 (0≤x≤7 mol%) series of glass samples were prepared with melt quenching method to develop new γ-ray shielding materials and irradiated with 60Co irradiation source. The light transmission characteristics and microstructure of the glass were studied by UV-Vis-nir and Raman. γ-ray irradiation makes the glass produce phosphorus oxygen hole center (class Ⅰ color), presenting brown. The resistance of phosphate glass to γ irradiation was enhanced by Gd2O3. The higher the content of Gd2O3 in glass, the lower the number of color centers caused by γ-ray irradiation. The transmittance on visible and near infrared light regions were reduced with the addition of Gd2O3. γ-ray irradiation causes the glass to exhibit optical absorption band loss, and the transmittance of the glass in the ultraviolet to visible region is reduced. The glass samples are mainly based on Q2 partial phosphate structure, accompanied by Q1 pyrophosphate and Q0 orthophosphate glass structure, and γ-ray irradiation has little effect on the microstructure of glass.
余 涛,王军霞,刘海峰,梁晓峰,杨世源,罗 庆. γ射线辐照对含钆磷酸钡玻璃影响的光谱分析[J]. 光谱学与光谱分析, 2018, 38(11): 3607-3610.
YU Tao, WANG Jun-xia, LIU Hai-feng, LIANG Xiao-feng, YANG Shi-yuan, LUO Qing. Spectral Analysis of the Effects of γ-Irradiation on Gadolinium-Containing Barium Phosphate Glass. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(11): 3607-3610.
[1] LUO Qing. Research of Structure of Gadolinium Phosphate Glass Radiation Shielding Material. Master Degree Thesis. Mianyang: Southweat University of Science and Technology,2017.
[2] Kulwinder S M. Nucl. Eng. Technol., 2017, 47: 192.
[3] Bootjomchai C, Laopaiboon J, Yenchai C, et al. Radiat. Phys. Chem., 2012, 81(7): 785.
[4] Kaur K, Singh K J, Anand V. Nucl. Eng. Des., 2015, 285: 31.
[5] Mahani R M, Marzouk S Y. J. Alloy. Compd., 2013, 579: 394.
[6] Jiménez J A, Hockenbury J B. J. Mater. Sci., 2013, 48: 6921.
[7] Doris M, Sindy R, Daniel S, et al. J. Non-Cryst. Solids., 2014, 383: 33.
[8] Fan S J, Yu C L, He D B, et al. Radiat. Meas., 2011, 46(1): 46.
[9] Magdas D A, Vedeanu N S, Toloman D. J. Non-Cryst. Solids., 2015, 428: 151.
[10] Shi M Q, Liang Y J, Chai L Y, et al. Journal of Molecular Structure, 2015, 1081: 389.
[11] Wang F, Liao Q L, Chen K R, et al. J. Non-Cryst. Solids., 2015, 409: 76.
[12] Hsu S M, Yung S W, Hsu Y, et al. Ceram. Int., 2016, 42: 4019.
[13] Wang C L, Liang X F, Li H J, et al. J. Nucl. Mater., 2014, 453(1-3): 220.
[14] Karina M Heffernan, Nancy L, et al. J. Solid. State. Chem., 2016, 241: 180.