Characterizing Methods of Structure and Character for Silane Film on Metal Surface
XU Yi1，TANG Shou-yuan2，ZHANG Xiao-feng2
1. Chemistry and Chemical Engineering College, Chongqing University, Chongqing 400044, China 2. Photo-electric Technology & System Key Lab of Chinese Educational Committee, Chongqing 400044, China
Abstract：Surface analysis methods for structure and characters of silane film on metal surface were reviewed in this paper. Many instrumental methods, such as XPS, ATR-FTIR, RA-FTIR, SIMS, ellipsometry, EIS and so on, were applied to characterizing different silane films on different metal base surfaces. According to the research on silane film formation mechanism, silane film state, silane film structure, silane film thickness, silane film corrosion resistance and so on, factors which affect silane film properties were discussed. Various parameters were proposed for characterizing silane film. Merits and defects of various surface analysis methods were expressed. In order to acquire more chemical information, different surface analysis methods can be combined for detection at the same time. Regarding the results from these detection and analysis, new silane treatment technique for metal surface can be optimized and improved greatly. Some other kinds of surface analysis methods were also mentioned in this paper. More advanced researches in the field of silane film analysis on metal surface were prospected.
徐 溢1，2，唐守渊1，张晓凤1. 金属表面硅烷试剂膜结构及性能表征方法 [J]. 光谱学与光谱分析, 2004, 24(04): 495-498.
XU Yi1，TANG Shou-yuan2，ZHANG Xiao-feng2 . Characterizing Methods of Structure and Character for Silane Film on Metal Surface . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(04): 495-498.
[1] Van Ooij W J, Zhang Chunbin, Zhang Jun Q et al. Proceedings of the Symposium on Advances in Corrosion Protection by Organic Coatings (Volume Ⅲ), 1998，97. [2] Van Ooij W J, Song J，Subramanian V. International Symposium on Aluminum Surface Science & Technology. Antwerp, Belgium, 1997，May，12. [3] Beorio F J, Armogan L，Cheng S Y. J. Colloid Interface Sci., 1980，73: 416. [4] Van Ooij W J, Child T F. Fourth Intenational Forum and Business Development Conference on Surface Modification, Couplants and Adhesion Promoters, Adhesion & Coupling Agent Technology 97. 1997, September, 22. [5] Gettings M，Kinloch A J. J. Mater. Sci., 1977，12: 2511. [6] Boerio F J, Ondrus D J. J. Adhesion, 1987，22: 1. [7] Leung Y L, Zhou M Y, Wong P C et al. Appl. Surf. Sci., 1992, 59: 23. [8] Subramanian V, Van Ooij W J. Corrosion, 1998，3: 204. [9] Bascom W D. Macromolecules, 1972, 5: 792. [10] XU Yi et al(徐 溢等). J. of Instrumental Analysis(分析测试学报)，2002, 21(2): 72. [11] Gettings M，Kinloch A J. Surf. Interf. Anal., 1979，1: 189. [12] Van Ooij W J, Sabata A. Surf. Interf. Anal., 1993，20: 475. [13] Sabata A, Van Ooij W J，Koch R J. J. Adhesion Sci. Technol., 1993，7(11): 1153. [14] Tutas D J, Stromberg R，Passaglia E. Spe. Trans., 1964，4: 256. [15] Leidheiser H. Prog. in Org. Coat., 1979, 7: 79. [16] 虞兆年. 防腐蚀涂料和涂装. 北京：化学工业出版社，1994. [17] Geenan F M. Europ. Coat. J., 1992, 3: 10. [18] Joung-man Park，Hak kim jin. J. Colloid Interface Sci., 1994，168(1): 103. [19] XU Yi et al(徐 溢等). Chinese J. of Applied Chemistry(应用化学), 2000，17(3): 331. [20] XU Yi et al(徐 溢等). Corrosion & Protection(腐蚀与防护)，2002，23(5): 193. [21] XU Yi et al(徐 溢等). Surface Technology(表面技术)，2001; 30(3): 48.