| The Application of X-Ray Photoelectron Spectroscopy on Refining Catalyst |
| QIU Li-mei, XU Guang-tong* |
| Research Institute of Petroleum Processing, SINOPEC, Beijing 100083, China |
|
|
|
|
Abstract XPS analysis provides qualitative, quantitative and chemical state information for surface elements of solid materials. Therefore, XPS is widely applied in the characterization of refining catalyst. In the present paper, the applications of XPS in the field of typical refining catalysts, including hydrogenation catalyst, S Zorb sorbent and rare-earth modified Y zeolite, are illustrated and exemplified. For sulfided Co(Ni)-Mo(W)/Al2O3(-SiO2) hydrodesulfurization catalysts, the anhydrous oxygen-free transfer process from the reactor to XPS chamber was illustrated. The identification and peak fitting of S(2p), Mo(3d), W(4f), Co(2p) and Ni(2p) XPS spectra were summarized. The typical chemical states of the active elements were described. Based on these results, the sulfidation extents of the active metals and the cause for the sulfidation inadequency of the catalysts were deduced. As for the application of XPS in S Zorb sorbent, the existence form of zinc was obtained from ZnLMM Auger spectra, and the fracture mechanism and deactivation reason of the sorbent were derived. The distribution of sulfur along the vertical direction was investigated using XPS and argon ion sputtering XPS. Besides, in situ XPS was applied to study the conversion of sulfur- and nickel-containing species for spent sorbent under hydrogen condition. Finally, for cerium modified Y zeolite, the location of cerium ion inside and outside Y zeolite cage was investigated. The results indicate that the liquid phase method is more suitable for the migration of cerium ion toward zeolite as compared with the solid phase method.
|
|
Received: 2014-08-08
Accepted: 2014-12-10
|
|
|
|
Corresponding Authors:
XU Guang-tong
E-mail: xugt.ripp@sinopec.com
|
|
[1] Pimerzin A A, Nikulshin P A, Mozhaev A V, et al. Appl. Cat. B: Environ.，2015, 168-169: 396.
[2] Qi D H, Duan A J, Zhao Z, et al. J. Porous Mat.，2015, 22: 127.
[3] Qiu L M, Xu G T. Appl. Surf. Sci., 2010, 256(11): 3413.
[4] Huang L C, Qin Z F, Wang G F, et al. Ind. Eng. Chem. Res., 2010, 49: 4670.
[5] XU Guang-tong, DIAO Yu-xia, ZOU Kang, et al(徐广通，刁玉霞，邹 亢，等). Petroleum Process Petroleum and Petrochemicals(石油炼制与化工), 2011, 42: 1.
[6] Qiu L M, Zou K, Xu G T. Appl. Surf. Sci., 2013, 266: 230. |
| [1] |
FAN Chun-hui1, 2, ZHENG Jin-huan3, LIU Hong-xin1. FTIR, 2D-IR and XPS Analyses on the Mechanism of Protoplast Derived From Calendula Officinalis in Response to Lead and Cadmium in Soil[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(05): 1420-1425. |
| [2] |
HE Xiong-fei1, 2, HUANG Wei3, TANG Gang3, ZHANG Hao3*. Mechanism Investigation of Cement-Based Permeable Crystalline Waterproof Material Based on Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(12): 3909-3914. |
| [3] |
LI Ping1,2, WU Yi-qiang1, LÜ Jian-xiong3, YUAN Guang-ming1, ZUO Ying-feng1*. Effect of Biomimetic Respiration Method on the Impregnation Effect of Silicate Modified Chinese Fir by XPS and FTIR Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(05): 1430-1435. |
| [4] |
GE Tao1, 2, LI Yang1, Wang Meng2, CHEN Ping3, MIN Fan-fei1, ZHANG Ming-xu1. Spectroscopic Characterization of Carbon Structure in High Sulfur Fat Coal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(01): 45-51. |
| [5] |
GE Tao1，2, LI Yang1, WANG Meng2, LI Fen1, ZHANG Ming-xu1. Structural Characterization and Molecular Model Construction of Gas-Fat Coal With High Sulfur in Shanxi[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(11): 3373-3378. |
| [6] |
LIU Xiu-yu, ZHANG Bing, ZHANG Hao, DU Xiao-yan, TANG Gang*. Research of Flame Retardant Mechanism for RPUF/EG Composites Based on TG-FTIR and XPS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(05): 1626-1633. |
| [7] |
GE Tao1,3, CAI Chuan-chuan1, CHEN Ping3, MIN Fan-fei1, ZHANG Ming-xu1. The Characterization on Organic Sulfur Occurrence in Coking Coal and Mechanism of Microwave Actionon Thiophene[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1321-1327. |
| [8] |
GE Tao1, ZHANG Ming-xu1, MA Xiang-mei2. XPS and FTIR Spectroscopy Characterization about the Structure of Coking Coal in Xinyang[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(08): 2406-2411. |
| [9] |
DONG Jun, REN Li-ming, CHI Zi-fang*, HU Wen-hua . Analysis of XPS in the Removal of Cr(Ⅵ) from Groundwater with rGO-nZⅥ[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(01): 250-255. |
| [10] |
LU Bao-qi, XU Yao-xian, SHEN Guang-yao, JI Jiang-hua, WANG Lin-jun. Raman Spectra Study on the Structure and Thermal Stability of Vacuum Annealed Cr-DLC Films Prepared with UBMS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3568-3571. |
| [11] |
ZHAO Hong-tao1, 2, 3, LI Hui-quan1*, BAO Wei-jun1, WANG Chen-ye1, LI Song-geng3*, LIN Wei-gang3 . Spectral Analysis of Trace Fluorine Phase in Phosphogypsum [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(08): 2333-2338. |
| [12] |
WANG Lei1, LIU Chang-sheng2, SHI Lei2, AN Cheng-qiang1 . Spectroscopic Study on Film Formation Mechanism and Structure of Composite Silanes-V-Zr Passive Film[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(02): 453-456. |
| [13] |
LIU Hong-fang1, 2, QIAN Tian-wei1*, ZHANG Min-gang2* . Analysis of XPS in the Removal of Se(Ⅳ) from Groundwater with Pyrite [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(02): 543-546. |
| [14] |
. Mechanism of Gold Solid Extraction from Aurocyanide Solution Using D3520 Resin Impregnated with TRPO [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 483-488. |
| [15] |
LI Lian-zhong, ZHUO Shang-jun*, SHEN Ru-xiang, QIAN Rong, GAO Jie . Quantitative Surface Analysis of Pt-Co, Cu-Au and Cu-Ag Alloy Films by XPS and AES [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 3128-3132. |
|
|
|
|