Raman Studies of Nanocrystalline BaTiO3 Ceramics |
XIAO Chang-jiang1,2, JIN Chang-qing2, WANG Xiao-hui3 |
1. Department of Material Science and Engineering, Henan University of Technology, Zhengzhou 450007, China 2. Institute of Physics, Chinese Academy of Sciences, Beijing 100080, China 3. State Key Laboratory of New Ceramics and Fine Processing,Department of Materials Science and Engineering,Tsinghua University,Beijing 100084, China |
|
|
Abstract High pressure can significantly increase the densification. Further, during the high pressure assisted sintering, the nucleation rate is increased due to reduced energy barrier and the growth rate is suppressed due to the decreased diffusivity. Thus high pressure enables the specimen to be fabricated with relatively lower temperature and shorter sintering period that assures to obtain dense nanocrystalline ceramics. Dense nanocrystalline BaTiO3 ceramics with uniform grain sizes of 60 and 30 nm, respectively, were obtained by pressure assisted sintering. The crystal structure and phase transitions were investigated by Raman scattering at temperatures ranging from -190 to 200 ℃. The Raman results indicated that the evolution of Raman spectrum with grain size is characterized by an intensity decrease, a broadening of the line width, a frequency shift, and the disappearance of the Raman mode. With increasing temperature, similar to 3 mm BaTiO3 normal ceramics, the successive phase transitions from rhombohedral to orthorhombic, orthorhombic to tetragonal, and tetragonal to cubic were also observed in nanocrystalline BaTiO3 ceramics. In addition, when particle size is reduced to the nanoscale, one will find some unusual physical properties in nanocrystalline ceramics, compared with those of coarse-grained BaTiO3 ceramics. The different coexistences of multiphase were found at different temperature. Especially, the ferroelectric tetragonal and orthorhombic phase can coexist at room temperature in nanocrystalline BaTiO3 ceramics. The phenomenon can be explained by the internal stress. The coexistences of different ferroelectric phases at room temperature indicate that the critical grain size for the disappearance of ferroelectricity in nanocrystalline BaTiO3 ceramics fabricated by pressure assisted sintering is below 30 nm.
|
Received: 2007-08-05
Accepted: 2007-10-26
|
|
Corresponding Authors:
XIAO Chang-jiang
E-mail: cjxiao@haut.edu.cn
|
|
[1] Zhao Z,Buscaglia V,Viviani M,et al. Phys. Rev. B,2004, 70: 024107. [2] Lin S, Lü T Q, Jin C Q, et al. Phys. Rev. B,2006, 74: 134115. [3] Wang X H, Deng X Y, Wen H, et al. Appl. Phys. Lett.,2006, 89: 162902. [4] LI Ying, DUAN Yu-ran, LI Wei-hua(李 颖, 段玉然, 李维华). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2002, 22(5): 783. [5] Poniatowski E H, Jouanne M, Morhange J F, et al. Phys. Rev. B,1999, 60(14): 10080. [6] Fujii M, Nagareda T, Hayashi S, et al. Phys. Rev. B,1991, 44(12): 6243. [7] Fujii M, Kanzawa Y, Hayashi S, et al. Phys. Rev. B,1996, 54(12): R8373. [8] Skandao G. Nanostruct. Mater.,1995, 5(2): 111. [9] Liao S C, Chen Y J, Kear B H, et al. Nanostruct. Mater.,1998, 10(6): 1063. [10] Li B R, Wang X H, Li L T. Mater. Chemistry and Physics, 2002, 78: 292. [11] Perry C H, Hall D B. Phys. Rev. Lett., 1965, 15: 700. [12] Venkateswaran U D, Naik V M, Naik R. Phys. Rev. B, 1998, 58(21): 14256. [13] Du Y L,Zhang M S, Chen Q, et al. Appl. Phys. A,2003, 76: 1099. [14] Arlt G, Hennings D, With G de. J. Appl. Phys., 1985, 58(4): 1619. [15] Arlt G. Ferroelectrics,1990, 104: 217. [16] Frey M H, Payne D A. Phys. Rev. B, 1996, 54(5): 3158. |
[1] |
DONG Jia-lin1, HONG Ming-jian1, 3*, ZHENG Xiang-quan2, 3, XU Yi2, 3. Discrimination of Human, Dog and Rabbit Blood Using Raman Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(02): 459-466. |
[2] |
ZHANG Bao-yong1,2,ZHOU Hong-ji1,2,WU Qiang1,2,GAO Xia3. Raman Spectra Characteristics of Gas Hydrate Growth with Different Driving Forces[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(09): 2768-2773. |
[3] |
WU Cheng-ling1, GUO Jun-hong1, 2, YAO Heng-bin1, PAN Ling-nan1, WANG Fei1, WU Wen-qi1, JI Tong1, HU Fang-ren1, 2*. Study on the Photoluminescence Properties of ZnO Single Crystal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(06): 1700-1702. |
[4] |
XU Dong-mei1, PAN Kun1, LIU Xu-wei1, WANG Xue-jin1*, WANG Wen-zhong2, LIANG Chun-jun3, WANG Zhi2 . Raman and Visible-Near Infrared Spectra of Cu(InGa)Se2 Films [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3197-3201. |
[5] |
WANG Guo-xiang1, WANG Hai-yan2, WANG Hu1, ZHANG Zheng-yong2, LIU Jun1 . Study on the Recognition of Liquor Age of Gujing Based on Raman Spectra and Support Vector Regression[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(03): 729-735. |
[6] |
ZHANG Bao-yong1, 2, YU Yue1, 2*, WU Qiang1, 2, GAO Xia3 . Quantitative Analysis of the Hydration Process of Mine Gas Mixture Based on Raman Spectroscopy [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(07): 1912-1916. |
[7] |
LI Tao, TANG Yan-lin*, LING Zhi-gang, LONG Zheng-wen . Study on the Frontier Orbital and Raman Spectra of Aflatoxin B1 and Isomer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(08): 2122-2125. |
[8] |
LI Jing1, MAO Shi-de1*, ZHENG Hai-fei2,3 . Raman Spectroscopic Quantitative Study of NaCl-CaCl2-H2O System at High Temperatures and Pressures[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(07): 1747-1753. |
[9] |
WU Dun, SUN Ruo-yu, LIU Gui-jian*, YUAN Zi-jiao. The Spectrum Studies of Structure Characteristics in Magma Contact Metamorphic Coal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(10): 2861-2864. |
[10] |
TAO Dong-yan, LIU Chao*, YIN Chun-hai, ZENG Yi-ping . Raman Spectra Analysis of GaN∶Er Films Prepared by Ion Implantation [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(03): 699-703. |
[11] |
HAN Jing-hua1, DUAN Tao2, FAN Wei-xing1, 3, FENG Guo-ying1*, YANG Li-ming4, NIU Rui-hua1, YANG Jie1, ZHAI Ling-ling1, GUO Chao1. Study on Characteristics of Laser Ablation in KTP Crystal and Its Influence on the Raman Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(07): 1820-1824. |
[12] |
SHI Bin, ZHANG Hai-jun, WU Lan, ZHANG Dong-xian*. Study of the Raman-AFM System for Simultaneous Measurements of Raman Spectrum and Micro/Nano-Structures[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(04): 993-996. |
[13] |
ZHANG Fei-fei, ZHENG Hai-fei*. Research on Raman Spectra of Isooctane at Ambient Temperature and Ambient Pressure to 1.2 GPa[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(03): 676-680. |
[14] |
LIANG Xiao-feng1,2,3, YIN Guang-fu2, YANG Shi-yuan1, WANG Jun-xia1 . Raman Spectrum Study of the Calcium Phosphate Glass Structure Affected by the Addition of TiO2 [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(07): 1790-1793. |
[15] |
SHEN Long-hai1, LI Qian1, WU Li-jun1, MA Yan-mei2, CUI Qi-liang2 . Raman Characterization of High-Pressure Phase Transition in AlN Nanowires[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(03): 696-699. |
|
|
|
|