The Synthesis and Characteristic of Co3O4 Nanocrystals |
TAO Dong-liang1, XU Yi-zhuang2, HUANG Yi1, WEI Fei1*, WU Jin-guang2, XU Duan-fu3 |
1. Laboratory of Reaction and Engineering, Department of Chemical Engineering, Tsinghua University, Beijing 100084, China 2. State Key Laboratory of Rare Earth Materials Chemistry and Application, College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China 3. State Key Laboratory of Polymer Physics and Chemistry, Center for Molecular Science, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China |
|
|
Abstract The authors found a new method to synthesize Co3O4 nanocrystals, which were synthesized using Co(CH3COO)2·4H2O and PVP as precursor. The as-prepared products were measured by SEM, TEM and XRD. Co(CH3COO)2·4H2O and PVP were dissolved together in a kind of solvent. Then, the solution was vaporized in water bath at 60 ℃ till the solution became viscid. The viscid solution was transferred into a ceramic boat and was dried in a oven at 110 ℃ for 12 hours. Finally, the dried sample was calcined in tube-like stove at 400 ℃ for 2 hours in air to produce the Co3O4 nanocrystals. To prepare the precursor composed of PVP and Co(CH3COO)2·4H2O, the authors employed two different solvent (ethanol and H2O). It was found that different appearance of Co3O4 nanocrystals was achieved by using different solvent. When ethanol is used as solvent, the prepared spherical particles with diameter of about 1 μm were consisted of Co3O4 nanocrystals with diameter of 20-50 nm. However, only Co3O4 nanocrystals with diameter of 20 nm were synthesized when H2O is used as solvent. This indicated that the solvent played a big role for the final appearance of Co3O4 nanocrystals.
|
Received: 2004-02-16
Accepted: 2004-05-08
|
|
Corresponding Authors:
WEI Fei
|
|
Cite this article: |
TAO Dong-liang,XU Yi-zhuang,HUANG Yi, et al. The Synthesis and Characteristic of Co3O4 Nanocrystals [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(01): 5-9.
|
|
|
|
URL: |
https://www.gpxygpfx.com/EN/Y2005/V25/I01/5 |
[1] Koinuma M, Hirae T, Matsumoto Y. J. Mater. Res., 1998, 13: 837. [2] Jansson J, Palmqvist A E C, Fridell E. J. Catal., 2002, 211: 387. [3] Choi S D, Min B K. Sens. Actuators B, 2001, 77: 330. [4] Makhlouf S A. J. Magn. Mater., 2002, 246: 184. [5] Jiang Y, Wu Y, Xie B et al. Mater. Chem. Phys., 2002, 74: 234. [6] Koshizaki N, Narazaki A, Sasaki T. Scr. Mater., 2001, 44: 1925. [7] Svegl F, Orel B, Grabec-Svegl I et al. Electrochim. Acta, 2000, 45: 4359. [8] Ni Y, Ge X, Zhang Z et al. Mater. Res. Bull., 2001, 36: 2383. [9] Zhu X, Liao L, Chui Y. Inorg. Chem. Ind., 2001, 34: 1. [10] Zeng H C, Lim Y Y. J. Mater. Res., 2000, 15: 1250. [11] Furlanetto G, Formaro L. J. Colloid Interface Sci., 1995, 170: 169. [12] Garavaglia R, Mari C M, Trasatti S. Surf. Technol., 1983, 19: 197. [13] Ardizzone S, Spinolo G, Trassatti S. Electrochim. Acta, 1995, 40: 2683. [14] Yang H M, Hu Y H, Zhang X C. Mater. Lett., 2004, 58: 387. [15] Li Q, Li T, Wu J G. J. Phys. Chem. B, 2001, 105: 12293. [16] YANG Qing-lin,GUO Lin,WU Zhong-hua(杨青林, 郭 林, 吴中华). Chemical J. of Chinese Universities(高等学校化学学报), 2003, 24: 82.
|
[1] |
SUN Da-wei1, 2, 3, DENG Jun1, 2*, JI Bing-bing4. Study on the Preparation Mechanism of Steel Slag-Based Biomass Activated Carbon by Special Steel Slag-Discard Walnut Shells Based on ICP-MS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(07): 2308-2312. |
[2] |
SUN Feng1, 2, YAN Qing-qing1, WANG Lu1, SUN Zhen-fei1. Study on the Conditions of Hydrothermal Synthesis of Chinese Purple BaCuSi2O6 and the Analysis of Its Products[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(07): 2284-2287. |
[3] |
ZHANG Hao1,2, ZHANG Lei1, LIU Xiu-yu1. Study on Preparation Stage and Mechanism of Modified Desulfurization Ash-Based Eco Rubber by X-Ray Diffraction[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(02): 616-621. |
[4] |
YE Ping, WU Miao-miao, WEI Ming, YANG Zhen, HAN Qiao-feng*. Preparation, Characterization and Properties of BiOCl1-xIx and BiOBr1-xIx Solid Solution[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(08): 2443-2449. |
[5] |
GONG Tian-cheng1,2, ZHU Yong1*, WANG Xin-yu1,3, WANG Ning1, ZHANG Jie1. Research on Preparation Process Optimization and Surface Enhanced Raman Spectroscopy (SERS) of Graphene-Silver Nanoparticle Composites[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(11): 3321-3327. |
[6] |
SHANG Jian-li, ZONG Zhi-fang*, SONG Dong-yi, TIAN Ye. Study on Preparation Mechanism of Ce-La/TiO2 Composites and Photocatalytic-Mositure-Heat Properties Based on FTIR and UV-Vis Spectra[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(06): 1728-1732. |
[7] |
WANG Fang, MA Zong-min*, ZHAO Min, LIN Zhao-dong, ZHANG Shao-wen, QU Zhang, LIU Jun, LI Yan-jun. Spectral Characteristics and Concentration Quantitative Analysis of NV Center Ensembles in Diamond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(05): 1477-1481. |
[8] |
ZHANG Hao1,2 . Study on Preparation Mechanism and Property of Biomass Environmental Coordination Function Material with Fourier Transform Infrared Spectrum [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(02): 412-415. |
[9] |
SHANG Jian-li,ZHANG Hao*,XIONG Lei,MA Xiang-long. Study on Preparation Mechanism of Decanoic Acid-Palmitic Acid/SiO2 Phase Change and Humidity Storage Composite Materials by Fourier Transform Infrared Spectrum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(06): 1690-1695. |
[10] |
LI Zhao1, ZHAO Xi-cheng2*, CHEN Li-jun3, JIANGYuan-ru3, LUO Lei2 . Contrastive Research of the Y3Al5O12: Ce3+ Yellow Phosphors Prepared by Different Methods[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(03): 695-699. |
[11] |
MA Xiao-yuan1, 2, 3, LIU Ying1, WANG Zhou-ping1, 3* . Preparation, Characterization and Surface-Enhanced Raman Properties of Agarose Gel/Gold Nanoparticles Hybrid [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(08): 2126-2131. |
[12] |
ZHENG Qing-fu1, 2, WANG Yong-he1, SUN Yue-guang1, NIU He-he1, ZHOU Jia-ru1, WANG Zhi-min1, ZHAO Ji3* . Study on Structural Properties of Biochar under Different Materials and Carbonized by FTIR [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(04): 962-966. |
[13] |
LU Jin1, WANG Hai-wen2, HAO Hong1, GAO Bo1, JIA Jian-li2. Optimizing the Method for 31P-NMR Analysis of Organic Phosphorus from Wetland Sediments [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 3157-3161. |
[14] |
YANG Fa-zhan1, WANG Shi-qing1, 2, SHEN Li-ru1*, CHEN Qing-chuan1 . XPS and Raman Studies of Diamond-Like Carbon Films Prepared by Various Deposition Techniques[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(07): 1800-1803. |
[15] |
HU Shu-wan1, LI Wen-jun1*, CHANG Zhi-dong1, WANG Huan-ying1, GUO Hui-chao1, ZHANG Jing-hua2, LIU Yang2 . Removal of Methyl Orange from Aqueous Solution by Magnetic Carbon Nanotubes [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(01): 205-209. |
|
|
|
|