Preparation and Optical Properties of MgAl2O4/Ce∶YAG Transparent Ceramics
HE Long-fei1, FAN Guang-han1*, LEI Mu-yun2, LOU Zai-liang2, CHEN Zhi-wu1, XIAO Yao1, ZHENG Shu-wen1, ZHANG Tao1
1. Institute of Opto-electronic Materials and Technology, South China Normal University, Guangzhou 510631, China 2. Bright Crystals Technology Ltd., Beijing 100018, China
Abstract:High-purity ultrafine MgAl2O4 powder was synthesized by metal-alkoxide method and calcining for 2~4 h.And then MgAl2O4/Ce∶YAG tra nsparent ceramics were fabricated by hot-pressed sintering and hot isostatic pressed sintering technique with YAG∶Ce powder and MgAl2O4 powder. The tra nsparent ceramics were characterized by XRD, SEM, EDS and fluorescence spectrometer, respectively. The results show that the crystal phase of the tra nsparent ceramic was composed of MgAl2O4 and YAG,and the YAG phase dispersed well in the matrix of MgAl2O4. The excitation spectra had a weak band at 345 nm and a strong band at 475 nm. The broad emission peaks at about 533 nm were attributed to 5d→4f tra nsition of Ce3+ io ns. Decay curves for the fluorescence of MgAl2O4/Ce∶YAG tra nsparent ceramic test show that the lifetime of the Ce∶YAG glass ceramic was 59.74 ns. All results show that MgAl2O4/Ce∶YAG tra nsparent ceramic may be a promising fluorescent material for white LED applicatio ns.
Key words:YAG;MgAl2O4;Transparent ceramic;White LED
[1] Geusic J E, Marcos H M, Van Uitert L G. Appl. Phys. Lett., 1964, 4(10): 182. [2] Steranka F M, Bhat J, Collins D, et al. Phys. Status Solidi A, 2002, 194(2): 380. [3] Zych E, Brecher C. J. Lumi., 2000, 90(3/4): 89. [4] Yanagida T, Takahashi H, Ito T, et al. IEEE T. Nucl. Sci., 2005, 52(5): 1836. [5] SHI Yun, PAN Yu-bai, FENG Xi-qi, et al(石 云, 潘裕柏, 冯锡淇, 等). Chinese J. Inorg. Mater.(无机材料学报), 2010, 25(2): 125. [6] Nishiura S, Tanabe S, Fujioka K, et al. Opt. Mater., 2011, 33(5): 688. [7] Owen J F, Dorain P B, Kobayasi T. J. Appl. Phys., 1981, 52(3): 1216. [8] Zych E, Brecher C. J. Alloys Compd., 2000, 300: 495. [9] Zych E, Brecher C, Glodo J. J. Phys.: Condens. Matter, 2000, 12(8): 1947. [10] Weber M J. Solid State Commun., 1973, 12(7): 741. [11] Raukas M, Basun S A, Schaik W V, et al. Appl. Phys. Lett., 1996, 69(22): 3300. [12] Blasse G, Grabmaier B C. Luminescent Materials. Berlin: Springer-Verlag,1994. 45. [13] YANG Jie-hui, XU You(杨杰慧, 徐 游). Acta Phys. Sin.(物理学报), 1997, 49(1): 170. [14] Blasse G, Bril A. Appl. Phys. Lett., 1967, 11(2): 53. [15] Lakshminarasimhan N, Varadaraju U V. J. Electrochem. Soc., 2005, 152(9): 152. [16] ZHANG Kai, LIU He-zhou, WU Ya-ting, et al(张 凯, 刘河洲, 仵亚婷, 等). Chinese J. Inorg. Mater.(无机材料学报), 2008, 23(5): 1045. [17] YANG Xin-bo, PAN Yu-bai, XU Jun, et al(杨新波, 潘裕柏, 徐 军). Acta Phys. Sin.(物理学报), 2009, 58(11): 8050. [18] Pang R, Li C Y, Shi L L, et al. J. Phys. Chem. Solids, 2009, 70(2): 303. [19] Zhang K, Liu Q, Liu Q, et al. J. Comb. Chem., 2010, 12(4): 453. [20] Furman J D, Gundiah G, Page K, et al. Chem. Phys. Lett., 2008,465(1/3): 67.