Study on Crystal Growth and Vibrational Spectra of Ybx∶KY1-x(WO4)2
LIU Jing-he1,ZHANG Ying1,ZHANG Li-jie1,ZENG Fan-ming1,WANG Cheng-wei2,ZHANG Xue-jian3
1. Research Center of Optoelecronic Functional Materials, Changchun University of Science and Technology，Changchun 130022, China 2. China Weapon Research Institute，Beijing 100089, China 3. Jilin Architectual and Civil Engineering Institute, Changchun 130021, China
Abstract：Ybx∶KY1-xW(x=0.05)and KYbW crystals were grown by TSSG method. Both of the structure and spectral properties were compared. The condition for the crystal growth is：the rotation rate 10-15 r·min-1,the pulling speed 1-2 mm·d-1,the growing period 10-15 d，cooling growing speed 0.05-0.1 ℃·h-1,and the cooling speed 20 ℃·h-1. X-ray powder diffraction analysis was performed for the crystal powder. They belong to β-KYW structure with low thermal phase. The cell parameters of the two crystals were calculated, and they are respectively a1=1.063 nm，b1=1.034 nm，c1=0.755 nm，β1=130.75°，Z1=4 and a2=1.061 nm，b2=1.029 nm，c2=0.749 nm，β2=130.65° and Z2=4. The infrared spectrum and Raman spectrum of crystal were measured. The sample of Ybx∶KY1-xW(x=0.05) had stronger infrared absorption peaks at 925，891，840，777 and 749 cm-1,which were caused by stretching vibration. The sample of KYW had stronger infrared absorption peaks at 484 and 437 cm-1 caused by bending vibration. The vibration modes were analysed and vibrational frequencies of vibratory activity was assigned. The two crystals had strong Raman activity. The vibration of WOOW and WOW exists from 200 to 1 000 cm-1.
[1] Fan T Y. IEEE J. Quantum Electron, 1993,29(6): 1457. [2] Giesen A, Hugel H, Voss A, et al. Appl. Phys. B, 1994, 58: 365. [3] TU Chao-yang，LI Jian-fu，ZHU Zhao-jie, et al(涂朝阳，李坚富，朱昭捷，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2003，23(4)：672. [4] Brenier A. Journal of Luminescence,2001, 92: 199. [5] Liu H, Nees J, Mourou G. Opt. Lett.,2001,26: 1723. [6] LIU Huang-qing, QIN Guan-shi, LIN Hai-yan, et al(刘晃清，秦冠仕，林海燕，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2004，24(1)：9. [7] Klopp P, Griebner U, Petrov V, et al. Appl. Phys. B,2002, 74: 185. [8] Fornasiero L, Mix E, Peters V, et al. Crystal Research and Technology, 1999, 34: 255. [9] LI Yan-hong，LI Jian-li，HONG Yuan-jia，et al(李艳红, 李建利, 洪元佳，等). China Laser(中国激光)，2002,29(5): 444. [10] Wang P, Dawes J M, Dekker P, et al. Journal of Opt. Soc. Am. B, 1999, 16: 63. [11] Macalika L, Hanuzaa J, Kaminskiib A A. Journal of Molecular Structure,2000, 555: 289. [12] Metrat G, Boudeulle M, Muhlstein N, et al. Journal of Cryst. Growth., 1999, 197: 883. [13] Payne S A, DeLoach L D, Smith L K, Appl. Phys., 1994, 76: 497. [14] Bruesselbach H W, Sumida D S, Reeder R A, Byren R W. IEEE Journal of Selected Topics Quantum Electronics, 1997, 3(1): 105.