不同浓度掺铊碘化铯(CsI∶Tl)晶体的光谱特性
吴正龙
北京师范大学分析测试中心,北京 100875
Comparisons of Spectral Properties of CsI∶Tl Crystals with Various Tl+ -Doped Concentrations
WU Zheng-long
Analytical and Testing Center, Beijing Normal University, Beijing 100875, China
摘要 : 对含有不同浓度Tl+ 激活剂的CsI∶Tl晶体进行了光吸收光谱和荧光光谱测量,以研究CsI∶Tl的光学吸收和发光特性。实验观察到,在紫外吸收谱中包含有三个特征结构峰297,273和247 nm,高浓度Tl+ 晶体的吸收结构峰比低浓度的峰明显加宽,其中A吸收峰297 nm红移20 nm。室温下不同能量紫外光激发的荧光带形状相同,不受Tl+ 浓度影响。分析认为,晶体中掺杂Tl+ 后晶格畸变是导致吸收峰或荧光激发峰变化的主要原因,但对发光带峰宽和峰位影响不明显。
关键词 :碘化铯晶体;闪烁体;吸收光谱;三维荧光谱
Abstract :Absorption Spectra and Photoluminescence (PL) spectra of CsI∶Tl crystals with various Tl+ -concentrations were measured for absorption and luminescent research in CsI∶Tl. Their UV absorption spectra contained three peaks at 297, 273 and 247 nm. The experiments were demonstrated that the peaks in the high Tl+ -concentration CsI∶Tl crystals are broader than ones in the low Tl+ -concentration crystals and their absorption A-peak shift by 20 nm, but their PL with UV excitations are similar. It was suggested that lattice distortions in the high Tl+ -concentration CsI∶Tl lead to the changes in absorption or fluorescence excitation peaks, but no changes in the fluorescence band widths and locations at room temperature.
Key words :Cesium Iodide crystal;Scintillator;Absorption spectrum;Three-dimension fluorescence spectrum
收稿日期: 2010-10-24
修订日期: 2011-02-27
通讯作者:
吴正龙
E-mail: wuzl@bnu.edu.cn
[1] Schotanus P, Kamermans R,Dorenbos P. IEEE Transactions on Nuclear Science, 1990, 37(2):177. [2] Carel W E van Eijk. Phys. Med. Biol., 2002, 47:R85. [3] Nagirnyi V, Zazubovich S, Zepelin V,et al. Chemical Physics Letters, 1994, 227(16):533. [4] Babin V, Fabeni P, Kalder K,et al. Radiation Measurements, 1998, 29(3-4):333. [5] Trefilova L N, Charkina T, Kudin A, et al. J. Lumin., 2003, 102-103:543. [6] Babin V, Kalder K, Krasnikov A,et al. J. Lumin., 2002, 96:75. [7] Trefilova L, Grinyov B, Alekseev V,et al. Radiation Measurements, 2007, 42:839. [8] Babin V, Krasnikov A, Wieczorek H, et al. Nucl. Instr. and Meth. in phys. Res. A, 2012, 486:486. [9] Pazzi G P, Nikl M, Bacci M,et al. J. Lumin., 1994, 69&61:527. [10] Wu Z,Yang B, Townsend P. Nuclear Instruments and Methods in Physics Research B, 2008,226:4757. [11] Kawai T, Ichmura N,Hashimoto S. Phys. Stat. Sol. B, 2001, 227(20):587. [12] Nagirnyi V, Stolovich A, Zazubovich S,et al. J Phys. Condens Matter,1995, 7:3637.
[1]
白西林,彭 越,张雪东,葛 晶. CdSe/ZnS量子点和量子点-受体分子复合物的超快动力学研究 [J]. 光谱学与光谱分析, 2024, 44(01): 56-61.
[2]
郑培超,尹义同,王金梅,周椿棪,张 莉,曾金锐,吕 强. 紫外吸收光谱结合SPA-ELM算法的水体磷酸根离子检测研究 [J]. 光谱学与光谱分析, 2024, 44(01): 82-87.
[3]
刘 佳,郑亚龙,王成博,尹作为,潘少逵. 新疆和田硬水铝石-蓝宝石谱学研究 [J]. 光谱学与光谱分析, 2024, 44(01): 176-180.
[4]
顾一露,裴景成,张誉慧,尹希严,余敏达,赖潇静. 墨西哥黄绿色磷灰石的宝石学和光谱学研究 [J]. 光谱学与光谱分析, 2024, 44(01): 181-187.
[5]
郑尼娜,谢品华,秦 敏,段 俊. 组合式LED宽带光源灯结构对差分吸收光谱反演的影响和扣除方法研究 [J]. 光谱学与光谱分析, 2023, 43(11): 3339-3346.
[6]
段明轩,李仕春,刘家辉,王 怡,辛文辉,华灯鑫,高 飞. 中红外差分吸收激光雷达探测苯气体浓度 [J]. 光谱学与光谱分析, 2023, 43(11): 3351-3359.
[7]
方 正,王涵博. 基于X射线吸收光谱法的塑料薄膜厚度测量 [J]. 光谱学与光谱分析, 2023, 43(11): 3461-3468.
[8]
黄 丽,马瑞峻,陈 瑜,蔡 祥,颜振锋,唐 昊,李艳芬. 利用紫外-可见光谱与平行因子分析法快速检测水体中多种有机磷农药的实验研究 [J]. 光谱学与光谱分析, 2023, 43(11): 3452-3460.
[9]
王 鹏,高永宝,寇少磊,门倩妮,张 敏,何 涛,姚 薇,高 瑞,郭文弟,刘昌瑞. 基于灰色关联度-RSM模型对原子吸收光谱法测定金元素条件的多目标优化 [J]. 光谱学与光谱分析, 2023, 43(10): 3117-3124.
[10]
贾雨歌,杨明星,游博雅,余柯烨. 冻胶绿松石及其原料的宝石学与谱学鉴别 [J]. 光谱学与光谱分析, 2023, 43(09): 2974-2982.
[11]
杨 欣,夏 敏,叶 寅,王 静. 店埠河农业小流域水体溶解性有机质光谱时空分布特征 [J]. 光谱学与光谱分析, 2023, 43(09): 2983-2988.
[12]
常 振,钟鸣宇,苏静明,司福祺,王 煜,周海金,窦 科,张 泉. MAX-DOAS重建NO2 竖直平面分布的方法研究 [J]. 光谱学与光谱分析, 2023, 43(08): 2413-2418.
[13]
刘衔宇,杨九昌,涂 彩,徐娅芬,徐 畅,陈全莉. 中国四川平武雪宝顶白钨矿的光谱学表征 [J]. 光谱学与光谱分析, 2023, 43(08): 2550-2556.
[14]
田思迪,王 振,杜艳君,丁艳军,彭志敏. 基于波长调制-直接吸收光谱的CO分子2.3 μm处谱线参数高精度测量 [J]. 光谱学与光谱分析, 2023, 43(07): 2246-2251.
[15]
梁文科,魏广芬,王铭淏. 洛伦兹线型近似引起的甲烷检测误差研究 [J]. 光谱学与光谱分析, 2023, 43(06): 1683-1689.