不同溶胶体系对纳米氧化锌发光特性的影响
郭书霞,张兴堂,张忠锁,赵慧玲,李蕴才,黄亚彬,杜祖亮*
河南大学特种功能材料省重点实验室,河南 开封 475001
Influence of Different Sol-Gel System on the Luminescence of Nanocrystalline ZnO Powder
GUO Shu-xia, ZHANG Xing-tang, ZHANG Zhong-suo, ZHAO Hui-ling, LI Yun-cai, HUANG Ya-bin, DU Zu-liang*
Key Laboratory of Special Functional Materials, Henan University, Kaifeng 475001, China
摘要 : 采用溶胶-凝胶工艺制备ZnO纳米粉体,研究了两种不同溶剂下制备的纳米ZnO的荧光特性。实验结果表明两种氧化锌样品有相同的晶型和能带结构,其紫外发光相似,但其带间的可见发射表现出了巨大差异,其原因在于两溶剂的极性不同导致两体系凝胶、烧结的微过程不同,从而使两种ZnO样品的表面态结构和布局发生变化。
关键词 :纳米ZnO;Sol-Gel法;光致发光
Abstract :ZnO nanopowders were prepared by the sol-gel techniques with two kinds of solvent.Microstructure of powder samples was examined by XRD and TEM.The results indicate that the two ZnO samples have the same crystal and energy band structure.Their photoluminescence (PL) spectra in ultraviolet region are analogous, but their photoluminescence (PL) spectra in visible region are different.The reason is that the two kinds of solvent with different polarity result in the difference in configuration and distribution of the sample surface states in the two systems.
Key words :ZnO nanopowder;Sol-Gel;Photoluminescence
收稿日期: 2004-02-10
修订日期: 2004-06-29
通讯作者:
杜祖亮
E-mail: DU Zu-liang
引用本文:
郭书霞,张兴堂,张忠锁,赵慧玲,李蕴才,黄亚彬,杜祖亮* . 不同溶胶体系对纳米氧化锌发光特性的影响[J]. 光谱学与光谱分析, 2005, 25(08): 1195-1198.
GUO Shu-xia, ZHANG Xing-tang, ZHANG Zhong-suo, ZHAO Hui-ling, LI Yun-cai, HUANG Ya-bin, DU Zu-liang* . Influence of Different Sol-Gel System on the Luminescence of Nanocrystalline ZnO Powder . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(08): 1195-1198.
链接本文:
https://www.gpxygpfx.com/CN/Y2005/V25/I08/1195
[1] Zhang S B, Wei S H,Zunger Alex.Phys.Rev.B, 2001, 63: 075205. [2] Vanheusden K, Warren W L,et al.J.Appl.Phys., 1996, 79: 7983. [3] Studenikin S A, Cocivera Michael.J.Appl.Phys., 2002, 91: 5060. [4] Kohan A F, Ceder G, Morgan D,et al.Phys.Rev.B, 2000, 61: 15019. [5] L Shu-chen, SONG Guo-li, XIAO Zhi-yan,et al(吕树臣,宋国利,肖芝燕,等).Chin.J.Lumin.(发光学报),2002, 23(3): 306. [6] Lin Bixia,Fu Zhuxi.Appl.Phys.Lett.,2001, 79: 943. [7] Garces N Y, Wang L, Bai L,et al.Appl.Phys.Lett.,2002, 81: 622. [8] L Shu-chen, SONG Guo-li, ZHANG Jia-hua, et al(吕树臣,宋国利,张家骅,等).Spectroscopy and Spectral Analysis(光谱学与光谱分析),2003,23(6): 1049. [9] Zhang G B, Zhou H J, Shi C S, et al.Surface Review and Letters, 2002, 9: 699. [10] Mikrajuddin Abdullah, Tsuuomu Morimoto,Kikuo Okuyama.Adv.Funct.Mater.,2003, 13: 800. [11] XU Xiao-liang, XU Jun, XU Chuan-ming,et al(许小亮,徐 军,徐传明,等).Chin.J.Lumin.(发光学报),2003, 24: 171.
[1]
覃丽梅,沈锡田. 抚顺煤精的光致发光光谱特征研究 [J]. 光谱学与光谱分析, 2023, 43(10): 3180-3185.
[2]
朱红伟,程佑法,陈淑祥,范春丽,李 婷,刘海彬,赵潇雪,山广褀,李建军. 一种疑似合成钻石的天然钻石光谱学特征 [J]. 光谱学与光谱分析, 2023, 43(06): 1690-1696.
[3]
严雪俊,周 扬,胡丹静,俞丹燕,余思逸,严 俊. 基于UV-Vis漫反射、Raman与PL光谱联用技术在黄色珍珠无损检测中的应用 [J]. 光谱学与光谱分析, 2023, 43(06): 1703-1710.
[4]
李 兆,王亚楠,徐祎朴,曹 静,王永锋,吴坤尧,邓 璐. 白光LED用YVO4 ∶Tm3+ 蓝色荧光粉的制备及发光性能 [J]. 光谱学与光谱分析, 2023, 43(02): 623-628.
[5]
廖逸民,闫胤洲,王 强,杨立学,潘永漫,邢 承,蒋毅坚. ZnO微米晶的激光制备装置及发光性能研究 [J]. 光谱学与光谱分析, 2022, 42(10): 3000-3005.
[6]
王 滔,刘建勋,葛啸天,王荣新,孙 钱,宁吉强,郑昌成. 蓝光激光器结构中InGaN/GaN多量子阱界面效应的精细光致发光光谱研究 [J]. 光谱学与光谱分析, 2022, 42(04): 1179-1185.
[7]
李 兆,吴坤尧,王亚楠,曹 静,王永锋,鲁媛媛. 蓝光激发的Y2.93 Al5 O12 ∶0.07Ce3+ 黄色荧光粉的制备及光致发光 [J]. 光谱学与光谱分析, 2022, 42(02): 381-385.
[8]
. 光致发光光谱在鉴别不同类型珍珠中的应用 [J]. 光谱学与光谱分析, 2022, 42(01): 20-25.
[9]
. 墨西哥红蓝料琥珀的宝石学及谱学特征 [J]. 光谱学与光谱分析, 2021, 41(08): 2618-2625.
[10]
. Tb3+ 掺杂锂铝硅酸盐玻璃的光致发光和辐照致发光 [J]. 光谱学与光谱分析, 2021, 41(06): 1863-1868.
[11]
. Cr3+ 单掺杂及Eu3+ /Cr3+ 共掺杂GdAlO3 近红外长余辉发光纳米粒子的制备、微结构及光学特性 [J]. 光谱学与光谱分析, 2021, 41(01): 80-87.
[12]
. 激基复合物和非激基复合物中C545T薄层的发光机制 [J]. 光谱学与光谱分析, 2020, 40(12): 3711-3715.
[13]
. 退火对磁控溅射掺铕氧化钇薄膜光致发光谱的影响 [J]. 光谱学与光谱分析, 2020, 40(11): 3336-3340.
[14]
. 海水养殖黑色珍珠UV-Vis反射光谱的类型及其特异的PL光谱特征 [J]. 光谱学与光谱分析, 2020, 40(09): 2781-2785.
[15]
. 硅铝酸盐基底材料中Dy3 Al2 (AlO4 )3 的拉曼光谱及其荧光光谱特征研究 [J]. 光谱学与光谱分析, 2020, 40(03): 809-812.