Study on Raman Spectra and Fluorescence Spectra of Dy3Al2(AlO4)3 in Aluminosilicate Substrates
ZHENG Bao-feng1, YANG Xiao-yun2,3, MIN Chun-gang2,3, CUI Xiao-ying2,3, DONG Kun2,3*
1. College of Materials Science and Engineering,Kunming University of Science and Technology,Kunming 650093,China
2. Research Center for Analysis and Measurement Kunming University of Science and Technology,Kunming 650033,China
3. Yunnan Analysis and Testing Center, Kunming 650033,China
Abstract:Silicoaluminate substrates doped with Dy at different concentrations are synthesized by high temperature solid state method. X-ray diffraction phase analysis shows that one of the main phases is Dy3Al2(AlO4)3. By Raman spectroscopy analysis, the intensity of the Raman peak is at 874.5 cm-1, which is related to the stretching vibration of Dy-[AlO4]. With the increase of Dy doping content, the intensity of Raman peaks increases first and then decreases. The peak at 419.9 cm-1 is related to the bending vibration of Dy-[AlO4]. With the increase of Dy doping content, the intensity of Raman vibration peak, the peaks of fluorescence spectrum measured by fluorescence spectrophotometer and the photoluminescence spectrum measured by Raman spectrophotometer all show the rule of first increasing and then decreasing. The matching amount of Dy-[AlO4] increases gradually, and when the amount of Dy doping exceeds a certain limit, concentration quenching occurs in the system, which results in the decrease of fluorescence properties. Compared with Tb system, the Raman spectra of the two systems have great similarities and slight differences. The Raman vibration peaks of Tb doped materials are 870.0 and 408.0 cm-1. The fluorescence intensity of two kinds of fluorescent materials doped with different elements are consistent, which indicates that the matching amount of rare earth elements with Al (Si) oxygen tetrahedron is the key factor to determine the fluorescence properties of the materials.
郑堡峰,杨晓云,闵春刚,崔小英,董 鹍. 硅铝酸盐基底材料中Dy3Al2(AlO4)3的拉曼光谱及其荧光光谱特征研究[J]. 光谱学与光谱分析, 2020, 40(03): 809-812.
ZHENG Bao-feng, YANG Xiao-yun, MIN Chun-gang, CUI Xiao-ying, DONG Kun. Study on Raman Spectra and Fluorescence Spectra of Dy3Al2(AlO4)3 in Aluminosilicate Substrates. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 809-812.
[1] Salehabadi A, Sarrami F, et al. Journal of Alloys and Compounds, 2018,744:574.
[2] Parc R L,Champagnon B,Dianoux J,et al. Journal of Non-Crystalline Solids,2003,323(1-3):155.
[3] JIAN Rong-hua,PANG Tao(简荣华,庞 涛). Journal of the Chinese Society of Rare Earths(中国稀土学报),2018,36(5):535.
[4] CAO Pei-ming,YOU Jing-lin, WANG Jian, et al(曹培明,尤静林,王 建,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2018,38(Suppl.1):237.
[5] Lipinska-Kalitak K E, Gramsch S A, Kalita P E, et al. J. Raman Spectrosc., 2005, 36: 938.
[6] LIANG Xiang-hui,MAO Qiu-ping, et al(梁向晖,毛秋平, 等). Analytical Instrumentation(分析仪器),2018,(4): 164.
[7] Papagelis K,Arvanitidis J,et al. Physica B,1999,265:277.
[8] GUAN Li,ZUO Jin-gai, et al(关 丽, 左金改,等). Chinese Journal of Luminescence(发光学报). 2011, 32(8): 779.
[9] Wang Zhengliang,Liang Hongbin,et al. Chem. Phys. Lett., 2005, 412(4-6): 313.
[10] YANG Hao,ZHANG Le, et al(杨 浩,张 乐,等). Journal of Nanjing University of Technology·Natural Science Edition(南京工业大学学报·自然科学版),2012, 34(2): 16.