Synthesis of the CaCO3∶Eu3+ Red Phosphor by Microwave Method
KANG Ming1, 2, LIU Jun1, SUN Rong1, YIN Guang-fu2, WANG Xing-ming1, YAN Wen-qing1
1.College of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010，China 2.School of Materials Science and Engineering, Sichuan University, Chengdu 610065, China
Abstract：The red phosphor of CaCO3 doped with Eu3+ was synthesized with the microwave method in the aqueous solution and characterized with electron microscope (SEM), X-ray diffraction (XRD), and photoluminescence and photoluminescence excitation (PL-PLE) spectrum.Also under investigation was the influence of microwave power on luminescence properties.The results showed that the synthesized CaCO3∶Eu3+ particles were the mixture of various particles in the forms of vaterite with flower-flake, calcite with cubic shape and aragonite with needle-like，which were evenly dispersed.The Eu3+ ion as the luminescent center inhabited the site of Ca2+ in mixed phases of CaCO3∶Eu3+.This feature was mainly characterized by the intense charge transfer band range from 200 to 300 nm in the PLE spectrum, which was the wide band excitation.Moreover, the narrow excitation peaks at 319, 395, 465, 535 nm and so on could be detected in the PLE spectrum.For the mixed phase, the magnetic-dipole transition 5D0 to 7F1 emission was split into two sublevels at about 589 and 593 nm by the crystal field.The mainly emission peaks were located in the vicinity of 614 and 620 nm, corresponding to the electric dipole transition 5D0→7F2 of Eu3+ ions that was the pure red emission.Moreover, with the improvement of the microwave power, the emission intensity was on rise for the morphology and phase of the sample changed from the flower-flake vaterite to the needle-like aragonite, coupled with the intensity of red light emission.
Key words：CaCO3∶Eu3+;Microwave synthesis;Red;Luminescence material
康 明1, 2，刘 军1，孙 蓉1，尹光福2，王兴明1，燕文清1 . 微波法合成红色荧光粉CaCO3∶Eu3+[J]. 光谱学与光谱分析, 2010, 30(01): 225-229.
KANG Ming1, 2, LIU Jun1, SUN Rong1, YIN Guang-fu2, WANG Xing-ming1, YAN Wen-qing1 . Synthesis of the CaCO3∶Eu3+ Red Phosphor by Microwave Method . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(01): 225-229.
[1] Li W M, Hanninen T, Leskela M, et al.Journal of Alloys and Compounds, 2001, 323-324: 236. [2] PAN Yue-xiao, WU Ming-mei, SU Qiang.Materials Research Bulletin, 2003, 38(9-10): 1537. [3] CHEN Li-miao, LIU You-nian, HUANG Ke-long.Materials Research Bulletin, 2006, 41(1): 158. [4] Ryu J H, Koo Sang-mo, Yoon Jong-won, et al.Materials Letters, 2006, 60(13-14): 1702. [5] ZHANG Ping, XU Ming-xia, ZHENG Zhen-tai, et al.Materials Science and Engineering B, 2007, 136(2-3): 159. [6] ZHAI Yong-qing, LIU Yuan-hong, LI Chang-e, et al(翟永清, 刘元红, 李常娥, 等).Rare Metal Materials and Engineering(稀有金属材料与工程), 2007, 36(9): 1657. [7] Cefalas A C, Kobe S, Drazic G, et al.Applied Surface Science, 2008, 254(21): 6715. [8] Kontoyannis C G, Vagenas N V.Analyst, 2000, 125: 251. [9] FANG Rong-chuan(方容川).Solid State Spectroscopy(固体光谱学).Hefei: The Publishing Company of China University of Science and Technology(合肥: 中国科学技术大学出版社), 2001.135. [10] Behrens G, Kuhn L T, Ubic R, et al.Spectroscopy Letters, 1995, 28(6): 983. [11] ZHAI Yong-qing, YANG Guo-zhong, LIU Yu, et al(翟永清, 杨国忠, 刘 宇, 等).Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2008, 28(3): 522. [12] GAO Xiao-rui, LEI Li-xu, Lü Chang-gui, et al.Journal of Solid State Chemistry, 2008, 181(8): 1776. [13] WANG Yu-hua, GAO Hui.Journal of Solid State Chemistry, 2006, 179(6):1870. [14] LIU Gui-xia, HONG Guang-yan, WANG Jin-xian, et al.Journal of Alloys and Compounds, 2007, 432(1-2): 200.