Preparation of TiO2 Pillared Montmorillonite Photocatalyst and Its Photocatalytic Activity to Degradation Reaction of Acidic Fuchsine by Sunlight
YANG Wu,CHENG Li-yan,XUE Zai-lan,GUO Hao,GAO Jin-zhang
Department of Chemistry and Chemical Engineering, Northwest Normal University, Key Lab of Eco-Environment Related Polymer Materials of MOE, Lanzhou 730070, China
Abstract：TiO2 pillared montmorillonite composite photocatalyst was synthesized by acid-catalyzed sol method and characterized by IR, UV-Vis, TG/DTA, XRD, SEM etc. Spectral analyses have demonstrated that TiO2 pillared montmorillonite(Ti-MMT) has wider interlayer distance than Na substituted montmorillonite(Na-MMT) and higher optical absorption efficiency than nanoscale anatase TiO2. The photocatalytic degradation reaction of acidic fuchsine by sunlight was employed to evaluate the catalytic activity of the composite catalyst. It was found that, besides easy reclaimation, the photocatalytic activity of the catalyst was much higher than that of the pure nanosized anatase TiO2. When the addition amount of Ti-MMT is 0.2 g·(100 mL)-1 and pH of acidic fuchsine solution is 3, the dye could be degraded thoroughly in 40 min and the degradation reaction obeys Langmuir- Hinshelwood equation.
杨武,成莉燕,薛再兰,郭昊,高锦章. TiO2柱撑蒙脱土的制备及其对品红降解的催化反应[J]. 光谱学与光谱分析, 2008, 28(05): 1122-1125.
YANG Wu,CHENG Li-yan,XUE Zai-lan,GUO Hao,GAO Jin-zhang. Preparation of TiO2 Pillared Montmorillonite Photocatalyst and Its Photocatalytic Activity to Degradation Reaction of Acidic Fuchsine by Sunlight. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(05): 1122-1125.
[1] CHEN Xiao-quan, GU Guo-bang(陈小泉，古国榜). Chinese Journal of Catalysis(催化学报), 2002, 23(4): 312. [2] Yan M C, Chen F, Zhang J L, et al. J. Phys. Chem. B, 2005, 109: 8673. [3] Ito S, Inoue S, Kawada H, et al. J. Colloid Interf. Sci., 1999, 216:59. [4] HUA Nan-ping，GAN Yu-qin，XU Jiao-zhen，et al（华南平, 甘玉琴，徐娇珍，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2005，25（11）: 1861. [5] YAO Bing-hua, WANG Li-ming, YU Xiao-jiao, et al(姚秉华，王理明，余晓皎，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2005，25（6）: 934. [6] Bandyopadhyay M, Birkner A, van den Berg M W E, et al. Chem. Mater., 2005, 17: 3820. [7] JIANG Yin-shan, JIN Wei-qun, ZHANG Jun, et al(蒋引珊，金为群，张 军，等). Journal of Inorganic Materials(无机材料学报), 2002, 17(6): 1301. [8] Serwicka E M, Bahranowski K. Catalysis Today, 2004, 90: 85. [9] Dana Y M, Chen Y, Nir S, et al. Environ. Sci. Technol., 2005, 39: 1231. [10] Miao S D, Liu Z M, Han B X, et al. J. Colloid Interf. Sci., 2006, 301: 116. [11] Korosi L, Nemeth J, Dekany I. Appl. Clay Science, 2004, 27: 29. [12] Tabet D, Saidi M, Houari M, et al. J. Environm. Manag., 2006, 80: 342. [13] Fetter G, Heredia G, Velfizquez L A, et al. Appl. Catal. A: Gen., 1997, 162: 41. [14] Hur S G, Kim T W, Hwang S J, et al. J. Phys. Chem. B, 2006, 110: 1599. [15] Binitha N N, Sugunan S. Microporous and Mesoporous Materials, 2006, 93(1-3): 82. [16] Ooka C, Yoshida H, Horio M, et al. Appl. Catal. B, 2003, 41: 313. [17] Yuan P, Yin X L, He H P, et al. Microp. Mesop. Mater., 2006, 93: 240.