Abstract:Both of Raman and infrared spectra of seven non-stoichiometry and threestoichiometry uranium oxides,including UO2, U3O7 and UO2+x(0<x<0.66), are presented and discussed. The spectra of UO2+x in the stoichiometry range, U3O7 to U3O8, were first obtained and reported. Three typical peaks were observed at 445, 578 and 1 150 cm-1 in the Raman spectrum of uranium dioxide. The intensities of the peaks at 578 and 1 151 cm-1 decrease quickly with increasing x value of UO2+x, and while x=0.19, the two peaks disappear. Such peaks can therefore be considered as a fin-gerprint of the quasi-perfect UO2 fluorite structure. The peak at 445 cm-1 tends to weaken, broaden and shift to higher wavenumber in more oxidised samples. When x=0.32, this peak is shifted to the 459 cm-1 and a weak peak at about 630 cm-1 appears. The two new peaks are typical of the tetragonal U3O7. While x≥0.39, the peak at 459 cm-1 further splits into separate components. Two peaks at 235 and 754 cm-1 appear for UO2.39 and are visible with increased intensity as the oxygen-uranium ratio is increased. And the Raman spectra of UO2+x are gradually close to U3O8 in the α-phase, which has an orthorhombic unit cell. But several strongest features of theα-U3O8 specturm at 333, 397, 483 and 805 cm-1 are still not outstanding even in UO2.60. The main feature of the UO2 infrared spectrum shows a very broad and strong adsorption band at 400~570 cm-1 and another feature is a weak adsorption peak at about 700 cm-1. The 400~570 cm-1 band undergoes a progressive splitting into two new peaks at ~421 and ~515 cm-1 through increasing incorporation of oxygen into UO2. The weak peak at about 700 cm-1 disappears and a new weak peak appears at about 645 cm-1. The three new peaks are the infrared absorption features of U3O7. An absorption peak at 744 cm-1 which is the strongest feature ofα-U3O8 infrared spectrum appears for UO2.39 and is visible with increased intensity in more oxidised samples. The peak at about 645 cm-1 still exists and 515 cm-1 peak has no further splitting into two new peaks at 485 and 535 cm-1 which also are the infrared absorption features of U3O8 in UO2.60. This indicates that UO2.60 is still in the transition period between tetragonal and orthorhombic phase of uranium oxide. A sequence of phase transitions occurs through increasing x value of UO2+x with different Raman and infrared features.It is easy to identify different uranium oxides by comparing of relative intensities and locations of their characteristic peaks.
[1] Palacios M L, Taylor S T. Applied Spectroscopy, 2000, 54: 1372. [2] Desgranges L, Baldinozzi G, Simon P, et al. Journal of Raman Spectroscopy, 2012, 43: 455. [3] Allen G C, Holmes N R. Applied Spectroscopy, 1994, 48: 525. [4] Zhu Yubao, Hansen W N, Ward J. Applied Spectroscopy, 1989, 43: 113. [5] Allen G C, Crofts J A, Griffiths A J. Journal of Nuclear Materials, 1976, 62: 273. [6] Manara D, Renker B. Journal of Nuclear Materials, 2003, 321: 233. [7] He Heming, Shoesmith D W. Physical Chemistry Chemistry Physics, 2010, 12: 8108. [8] He Heming, Qin Z, Shoesmith D W. Electrochimica Acta, 2010, 56: 53. [9] Rousseau G, Desgranges L, Charlot F, et al. Journal of Nuclear Materials, 2006, 355: 10. [10] Sarsfield M J, Taylor R J, Puxley C, et al. Journal of Nuclear Materials, 2012, 427: 333. [11] Livneh T, Sterer E. Physical Review B, 2006, 73: 085118. [12] Jégou C, Caraballo R, Peuget S, et al. Journal of Nuclear Materials, 2010, 405: 235. [13] Senanayake S D, Rousseau R, Colegrave D et al. Journal of Nuclear Materials, 2005, 342: 179. [14] Goel P, Choudhury N, Chaplot S L. Journal of Nuclear Materials, 2008, 377: 438. [15] Desgranges L, Baldinozzi G, Siméone D, et al. Inorganic Chemistry, 2011, 50: 6146.