Abstract:Transparent γ-CuⅠ crystal with size about 9 mm×9 mm×1 mm was grown by using optimized solvent evaporation method with γ-CuⅠ powders as raw material and acetonitrile as solvent. The results of Rutherford backscattering spectrometry (RBS) showed that the proportions of copper and iodine in as-grown γ-CuⅠ crystal were 53.1 and 46.9mol%, respectively. By iodine doping into growth solution, the proportions of copper and iodine were adjusted to 50.4 and 49.6 mol%, respectively. Photoluminescence (PL) showed that the as-grown γ-CuⅠ crystal had an emission at 410 nm and an emission band around 720 nm. After iodine doping, the emission band around 720 nm was suppressed while other two weak emissions at 424 and 474 nm appeared. X-ray excited luminescence (XEL) showed that the as-grown γ-CuⅠ crystal had an emission at 435 nm and an emission band around 720 nm. After iodine doping, the emission band around 720 nm was suppressed. Comparing the emission spectra before and after iodine doping, it is clear that red luminescence in γ-CuⅠ crystal could be suppressed by iodine doping. The effect originated from the reduction of iodine vacancy in the crystal, but not from the iodine adsorbtion on the surface.
Key words:γ-CuⅠ;Crystal growth;Iodine content;Suppression of red luminescence
蔡祖旭,顾 牡*,刘小林,刘 波,黄世明,倪 晨 . γ-CuⅠ晶体生长和红光发射的抑制机理 [J]. 光谱学与光谱分析, 2013, 33(02): 293-296.
CAI Zu-xu, GU Mu*, LIU Xiao-lin, LIU Bo, HUANG Shi-ming, NI Chen . Growth and Red Luminescence Suppression of γ-CuⅠ Single Crystal . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(02): 293-296.
[1] Lewonczuk S, Ringeissen J. Physical Review B, 1994, 49: 2344. [2] Tanka I, Kim D, Nakayama M, et al. Journal of Luminescence, 2000, 87, 257. [3] Boyce J B, Hayes T M, Mikkelsen J C. Jr. Physical Review B, 1981, 23: 2876. [4] Derenzo S E, Weber M J, Klintenberg M K. Nuclear Instrument and Method in Physics Research A, 2002, 486: 214. [5] Gu M, Gao P, Liu X L, et al. Materials Research Bulletin, 2010, 45: 636. [6] CUI Yu-jie,PAN Jian-guo,YANG Shu-ying,et al(崔玉杰,潘建国,杨书颖,等). Journal of Synthetic Crystals(人工晶体学报), 2010, 39(5): 1109. [7] Chen D G, Wang Y J, Zhang L, et al. Crystal Growth & Design, 2010, 10: 2057. [8] Gao P, Gu M, Liu X L, et al. Applied Physics Letter, 2009, 95: 221904. [9] Zhang Y, Sun W, Santos A M, et al. Catalysis Letters, 2005, 101: 35. [10] Yang Y, Gao Q. Langmuir, 2005, 21: 6866. [11] Oggioni R, Spinolo G. Physical Review, 1963, 131(1): 1114.