Hydrothermal Synthesis and Luminescence of One-Dimensional Mn2+-Doped CdS Nanocrystals
YUAN Qiu-li1,ZHAO Jin-tao1,NIE Qiu-lin1,2
1. Institute of Materials Physics, Hangzhou Dianzi University, Hangzhou 310037, China 2. Department of Chemistry, Zhejiang University, Hangzhou 310027, China
Abstract:One-dimensional Mn2+-doped CdS nanocrystals were synthesized by the hydrothermal route. The products were characterized by SEM, EDS, XRD, TEM, HRTEM and PL, respectively. The results revealed that dopant Mn2+ completely substitutes Cd2+ in CdS nanocrystals, and the product was of good crystallite. Further more, a complete suppression of the emission from surface states at room temperature when doping with ions Mn2+ has been observed.
[1] Papp J, Soled S, Dwight K, et al. Chem. Mater., 1994, 6: 496. [2] Jonker B T, Liu X, Chou W C, et al. J. Appl. Phys. 1991, 69: 6098. [3] Liu S, Liu F Q, Guo H Q. Solid State Comm., 2000, 115: 615. [4] Sooklal K, Cullum B S, Angel S M. J. Phys. Chem., 1996, 100: 4551. [5] Counio G, Gacoin T, Boilot J P. J. Phys. Chem. B, 1998, 102: 5227 [6] Pileni M P. Catal. Today, 2000, 58: 151. [7] Norris D J, Yao N, Charnock F T. Nano Lett., 2001, 1: 3. [8] XIE Ping-bo, ZHAO Fu-li, LI Ya-dong, et al(谢平波,赵福利,李亚栋,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2005,25(6):848. [9] YUAN Qiu-li, NIE Qiu-lin, CHEN Wei-xiang, et al(袁求理,聂秋林,陈卫祥,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2005,25(6):971. [10] Dai H,Wong E W,Lieber C M,et al. Nature, 1995, 375: 769. [11] Yang P D. Lieber C M. Science, 1996, 273: 1836. [12] Brus L E. Appl. Phys. A, 1991, 53: 465. [13] Vaslltsova O V, Parmon V N. Kinetics and Catalysis, 1999, 40: 62. [14] Heske C, Winkler U, Neureiter H, et al. Appl. Phys. Lett., 1997, 70: 1022. [15] Cao H Q, Hu Y, Hong J M, et al. Adv. Mater., 2001, 13: 1393. [16] Routkevitch D, Bigioni T, Moskovits M, et al. J. Phys. Chem., 1996, 100: 14037. [17] Ge X W, Lee S M, Kang N J, et al. J. Am. Chem. Soc., 2001, 123: 5150. [18] Li Y D, Liao H W, Ding Y, et al. Inorg. Chem., 1999, 38: 1382. [19] Yang J, Zeng J H, Yu S H, et al. Chem. Mater., 2000, 12: 3259. [20] Nie Q L, Yuan Q L, Chen W X, et al. Journal of Crystal Growth,2004, 265(3-4): 420. [21] YUAN Qiu-li, NIE Qiu-lin(袁求理, 聂秋林). Journal of Inorganic Materials(无机材料学报), 2007, 1: 49. [22] Langer D W, Richter H. J. Phys. Rev., 1996, 146: 554. [23] Bawendi M G, Carroll P, Wilson W L. J. Chem. Phys., 1992, 96: 946. [24] Nada K K, Sahu S N. Solid State Comm., 1999, 114: 176. [25] Chamarro M A, Voliotis V, Grousson R. J. Cryst. Growth, 1996, 159: 853. [26] Levy L, Hopechepied J F, Pileni M P. J. Phys. Chem., 1996, 100: 18322.