Preparation and Luminescent Properties of Light Scattering Fluorescent Resin |
XIAO Yao1, FAN Guang-han1, 2, PI Hui1, XU Yi-qin2, CHEN Zhi-wu1, HE Long-fei2, YU Xiao-peng1, ZHANG Li1, ZHENG Shu-wen1*, ZHANG Tao1* |
1. Laboratory of Nanophotonic Functional Materials and Devices, Institute of Opto-electronic Materials and Technology, South China Normal University, Guangzhou 510631, China 2. Guangdong General Research Institute for Industrial Technology, Guangzhou 510650, China |
|
|
Abstract With the methods of compound-melting and high-temperature molding, PC/YAG∶Ce fluorescent resin pieces were prepared. The transmittance of the prepared PC/YAG∶Ce fluorescent resin in 500~800 nm reaches approximately 65% (0.71 mm thick, double sides polished). The fluorescent resin was characterized by XRD, SEM and PL. The X-ray diffraction (XRD) patterns demonstrated that the fluorescent resin was pure Y3Al5O12 phase. The scanning electron microscopy (SEM) images showed that YAG phosphor was distributed evenly in the fluorescent resin. The excitation spectra had a weak peak at 342 nm and a strong band at 448 nm. The broad emission peaks at about 532 nm can be attributed to 5d→4f transition of Ce3+ ions. Decay curves for the fluorescence of PC/YAG∶Ce fluorescent resin show that the lifetime of the fluorescent resin was 61.5 ns. The luminous efficacy of the white LED packaged by the fluorescent resin and blue LED chip was 81.12 lm·W-1 at 100 mA. All results above of PC/YAG∶Ce fluorescent resin indicate a promising fluorescent material for white LEDs.
|
Received: 2013-09-23
Accepted: 2013-12-20
|
|
Corresponding Authors:
ZHENG Shu-wen, ZHANG Tao
E-mail: hszhangtao@163.com
|
|
[1] Nakamura S, Mukai T. Senoh. Appl. Phys. Lett., 1994, 64: 1687. [2] LIU Xing-ren(刘行仁). Chinese Journal of Luminescence(发光学报),2007, 28(3): 291. [3] HE Long-fei, FAN Guang-han, LEI Mu-yun(贺龙飞,范广涵,雷牧云). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2013, 33(5): 1175. [4] Kim Jong Kyu, Luo Hong,Eric Fred SCHUBERT. Japanese Journal of Applied Physics, 2005,44(21): 649. [5] LIAO Jian-guo, LI Yu-bao(廖建国,李玉宝). Acta Materiae Compositae Sinica(复合材料学报),2008, 25(3): 63. [6] DU Feng, SONG Jian-bin(杜 峰,宋剑斌). Journal of Nanjing University of Technology(南京工业大学学报),2010, 32(4):23. [7] OUYANG Xing, CHEN Da-zhu, TANG Jiao-ning(欧阳星,陈大柱,汤皎宁). China Synthetic Resin and Plastics(合成树脂及塑料),2012, 29(4):21. [8] JIANG Ji-feng, ZHOU Shao-hua(蒋继峰, 周少华). Rare Metal Materials and Engineering(稀有金属材料与工程),2008, 37(2): 426. [9] YANG Jun, YAN Wei-ping, LI Ming-wei(杨 隽,闫卫平, 李明伟). Journal of the Chinese Rare Earth Society(中国稀土学报),2005,23: 27. [10] SONG Guo-hua, MIAO Jian-wen, XU Shu-wu(宋国华, 缪建文, 徐淑武). Journal of Optoelectronics·Laser(光电子·激光),2010, 21(12): 1785. [11] YANG Xin-bo, SHI Yun, LI Hong-jun(杨新波, 石 云, 李红军). Acta Physica Sinica(物理学报),2009, 58(11): 8050. [12] SHI Yun, PAN Yu-bai, FENG Xi-qi(石 云, 潘裕柏, 冯锡淇). Chinese Journal of Inorganic Materials(无机材料学报),2010, 25(2): 125. [13] Pang R, Li C Y, Shi L L. J. Phys. Chem. Solids, 2009, 70(2): 303. [14] Furman J D, Gundiah G, Page K. Chem. Phys. Lett., 2008, 465(1/3): 67. |
[1] |
LI Zhao, WANG Ya-nan, XU Yi-pu, CAO Jing, WANG Yong-feng, WU Kun-yao, DENG Lu. Synthesis and Photoluminescence of Blue-Emitting Phosphor
YVO4∶Tm3+ for White Light Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 623-628. |
[2] |
LI Zhao, WU Kun-yao, WANG Ya-nan, CAO Jing, WANG Yong-feng, LU Yuan-yuan. Synthesis and Luminescence Properties of Yellow-Emitting Phosphor Y2.93Al5O12∶0.07Ce3+ Under Blue Light Excitation[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(02): 381-385. |
[3] |
CAO Li, ZHENG Zi-shan, ZHANG Hong*, LIANG Pei, ZHU Qiang-qiang, WANG Le*. Phosphor-Converted White Light-Emitting Diodes for Plant Lighting[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(04): 1060-1065. |
[4] |
LI Zhao, WANG Yong-feng, CAO Jing, WU Kun-yao, WANG Ya-nan. Preparation and Performance of Red Phosphor ScVO4∶Eu3+ for White LEDs[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3077-3080. |
[5] |
FENG Ai-ming1, WANG Fu-qiang1, ZHANG Hong1*, AN Peng2, LI Yang-hui1, 3, WANG Le1*. Significantly Improved Luminescence Properties of YAG Phosphor via Localized Surface Plasmon Resonance of Nanotitania[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3081-3085. |
[6] |
ZHANG Hong1, WANG Le1*, LUO Dong1, ZHENG Zi-shan1, LI Yang-hui1, 2, PAN Gui-ming1. Structural and Luminescence Properties of Eu2+ Doped CaAlSiN3 Silicon Nitride Red Emitting Phosphor[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 59-64. |
[7] |
ZHUO Ning-ze1, 2, 3, ZHANG Na1, 2, CHEN Yong-hao4, JIANG Peng4, CHENG Shao-wen5, ZHU Yue-hua1, 2, WANG Hai-bo2*. Preparation and Spectral Properties of White Light Emitting LED Based on Layered Remote Phosphor Film[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(08): 2337-2343. |
[8] |
LI Bo-chao1, 2, ZHUO Ning-ze2*, LI Wen-quan2,3, HE Qing-yang1, 2, HUANG Ru-xi2, LIU Guang-xi2, YE En-gan1, 2, WANG Hai-bo2*. The Preparation and Properties Study of High CRI White LED Based on Remote Phosphor Technology [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 728-732. |
[9] |
FENG Ying, TONG Yi-ping*, LI Wen-wei . A Study on Synthesis of CaAl12O19∶xMn4+ Red Phosphor with Combustion Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3211-3214. |
[10] |
LIU Shi1, CHEN Yong-jian1, CUI Hai-ning1*, SUN Sheng-nan1, WANG Zi-han1, WANG Hai-shui2. Native Defect Luminescence of Zinc Oxide Films and Its Potential Application as White Light Sources[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(05): 1604-1614. |
[11] |
CAO Jin2, ZHOU Jie1, XIE Jing-wei1, CHEN An-ping1, ZHANG Xue1, YIN Lu-qiao2, ZHANG Jian-hua2 . Research on the Highly Stable White LED with CdSe/ZnS Quantum Dot as Light Conversion Layer [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(02): 349-354. |
[12] |
FU Yue, CONG Yan*, YANG Yang, XIAO Yu, HE Yang-yang, WANG Li-mei, DONG Bin* . Spectroscopic Properties of CeO2∶Eu3+ for White LEDs [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(11): 3032-3035. |
[13] |
YU Chun-yu1, JIN Peng2, ZHOU Qi-feng3 . Optimizing Color Rendering for Mixed-Color White Light LED [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(05): 1316-1319. |
[14] |
KUANG Qing-liang, LI Yong-jin*, QIU Jian-bei, YIN Zhao-yi, YANG Zheng-wen, SONG Zhi-guo*, WAN Rong-hua, LIU Qun, ZHOU Yu-ting. Synthesis and Luminescence Properties of BiOCl∶Dy3+ Phosphors for NUV Excited White Light-Emitting Diodes [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(04): 889-893. |
[15] |
LI Zhao1, ZHAO Xi-cheng2*, CHEN Li-jun3, JIANGYuan-ru3, LUO Lei2 . Contrastive Research of the Y3Al5O12: Ce3+ Yellow Phosphors Prepared by Different Methods[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(03): 695-699. |
|
|
|
|