Preparation and Optical Properties of MgAl2O4/Ce∶YAG Transparent Ceramics |
HE Long-fei1, FAN Guang-han1*, LEI Mu-yun2, LOU Zai-liang2, CHEN Zhi-wu1, XIAO Yao1, ZHENG Shu-wen1, ZHANG Tao1 |
1. Institute of Opto-electronic Materials and Technology, South China Normal University, Guangzhou 510631, China2. Bright Crystals Technology Ltd., Beijing 100018, China |
|
|
Abstract High-purity ultrafine MgAl2O4 powder was synthesized by metal-alkoxide method and calcining for 2~4 h.And then MgAl2O4/Ce∶YAG tra nsparent ceramics were fabricated by hot-pressed sintering and hot isostatic pressed sintering technique with YAG∶Ce powder and MgAl2O4 powder. The tra nsparent ceramics were characterized by XRD, SEM, EDS and fluorescence spectrometer, respectively. The results show that the crystal phase of the tra nsparent ceramic was composed of MgAl2O4 and YAG,and the YAG phase dispersed well in the matrix of MgAl2O4. The excitation spectra had a weak band at 345 nm and a strong band at 475 nm. The broad emission peaks at about 533 nm were attributed to 5d→4f tra nsition of Ce3+ io ns. Decay curves for the fluorescence of MgAl2O4/Ce∶YAG tra nsparent ceramic test show that the lifetime of the Ce∶YAG glass ceramic was 59.74 ns. All results show that MgAl2O4/Ce∶YAG tra nsparent ceramic may be a promising fluorescent material for white LED applicatio ns.
|
Received: 2012-10-03
Accepted: 2013-01-16
|
|
Corresponding Authors:
FAN Guang-han
E-mail: gfan@scnu.edu.cn
|
|
[1] Geusic J E, Marcos H M, Van Uitert L G. Appl. Phys. Lett., 1964, 4(10): 182. [2] Steranka F M, Bhat J, Collins D, et al. Phys. Status Solidi A, 2002, 194(2): 380. [3] Zych E, Brecher C. J. Lumi., 2000, 90(3/4): 89. [4] Yanagida T, Takahashi H, Ito T, et al. IEEE T. Nucl. Sci., 2005, 52(5): 1836. [5] SHI Yun, PAN Yu-bai, FENG Xi-qi, et al(石 云, 潘裕柏, 冯锡淇, 等). Chinese J. Inorg. Mater.(无机材料学报), 2010, 25(2): 125. [6] Nishiura S, Tanabe S, Fujioka K, et al. Opt. Mater., 2011, 33(5): 688. [7] Owen J F, Dorain P B, Kobayasi T. J. Appl. Phys., 1981, 52(3): 1216. [8] Zych E, Brecher C. J. Alloys Compd., 2000, 300: 495. [9] Zych E, Brecher C, Glodo J. J. Phys.: Condens. Matter, 2000, 12(8): 1947. [10] Weber M J. Solid State Commun., 1973, 12(7): 741. [11] Raukas M, Basun S A, Schaik W V, et al. Appl. Phys. Lett., 1996, 69(22): 3300. [12] Blasse G, Grabmaier B C. Luminescent Materials. Berlin: Springer-Verlag,1994. 45. [13] YANG Jie-hui, XU You(杨杰慧, 徐 游). Acta Phys. Sin.(物理学报), 1997, 49(1): 170. [14] Blasse G, Bril A. Appl. Phys. Lett., 1967, 11(2): 53. [15] Lakshminarasimhan N, Varadaraju U V. J. Electrochem. Soc., 2005, 152(9): 152. [16] ZHANG Kai, LIU He-zhou, WU Ya-ting, et al(张 凯, 刘河洲, 仵亚婷, 等). Chinese J. Inorg. Mater.(无机材料学报), 2008, 23(5): 1045. [17] YANG Xin-bo, PAN Yu-bai, XU Jun, et al(杨新波, 潘裕柏, 徐 军). Acta Phys. Sin.(物理学报), 2009, 58(11): 8050. [18] Pang R, Li C Y, Shi L L, et al. J. Phys. Chem. Solids, 2009, 70(2): 303. [19] Zhang K, Liu Q, Liu Q, et al. J. Comb. Chem., 2010, 12(4): 453. [20] Furman J D, Gundiah G, Page K, et al. Chem. Phys. Lett., 2008,465(1/3): 67. |
[1] |
LI Bo-chao1, 2, ZHUO Ning-ze2*, LI Wen-quan2,3, HE Qing-yang1, 2, HUANG Ru-xi2, LIU Guang-xi2, YE En-gan1, 2, WANG Hai-bo2*. The Preparation and Properties Study of High CRI White LED Based on Remote Phosphor Technology [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 728-732. |
[2] |
FENG Ying, TONG Yi-ping*, LI Wen-wei . A Study on Synthesis of CaAl12O19∶xMn4+ Red Phosphor with Combustion Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3211-3214. |
[3] |
LIU Shi1, CHEN Yong-jian1, CUI Hai-ning1*, SUN Sheng-nan1, WANG Zi-han1, WANG Hai-shui2. Native Defect Luminescence of Zinc Oxide Films and Its Potential Application as White Light Sources[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(05): 1604-1614. |
[4] |
CAO Jin2, ZHOU Jie1, XIE Jing-wei1, CHEN An-ping1, ZHANG Xue1, YIN Lu-qiao2, ZHANG Jian-hua2 . Research on the Highly Stable White LED with CdSe/ZnS Quantum Dot as Light Conversion Layer [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(02): 349-354. |
[5] |
FU Yue, CONG Yan*, YANG Yang, XIAO Yu, HE Yang-yang, WANG Li-mei, DONG Bin* . Spectroscopic Properties of CeO2∶Eu3+ for White LEDs [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(11): 3032-3035. |
[6] |
YU Chun-yu1, JIN Peng2, ZHOU Qi-feng3 . Optimizing Color Rendering for Mixed-Color White Light LED [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(05): 1316-1319. |
[7] |
KUANG Qing-liang, LI Yong-jin*, QIU Jian-bei, YIN Zhao-yi, YANG Zheng-wen, SONG Zhi-guo*, WAN Rong-hua, LIU Qun, ZHOU Yu-ting. Synthesis and Luminescence Properties of BiOCl∶Dy3+ Phosphors for NUV Excited White Light-Emitting Diodes [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(04): 889-893. |
[8] |
LI Zhao1, ZHAO Xi-cheng2*, CHEN Li-jun3, JIANGYuan-ru3, LUO Lei2 . Contrastive Research of the Y3Al5O12: Ce3+ Yellow Phosphors Prepared by Different Methods[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(03): 695-699. |
[9] |
XIAO Yao1, FAN Guang-han1, 2, PI Hui1, XU Yi-qin2, CHEN Zhi-wu1, HE Long-fei2, YU Xiao-peng1, ZHANG Li1, ZHENG Shu-wen1*, ZHANG Tao1*. Preparation and Luminescent Properties of Light Scattering Fluorescent Resin[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(12): 3178-3182. |
[10] |
LI Zhao1, ZHAO Xi-cheng2, JIANG Yuan-ru3 . Preparation and Photoluminescent Property of Sphere Y2.96Al5O12∶ 0.04Ce3+ Phosphor for White Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(11): 2918-2922. |
[11] |
XU Guo-tang, LIANG Pei*, WANG Le*, DONG Qian-min, LIU Yang, LI Xiao-yan . Progress in the Research on Silicon-Nitrogen Based Phosphor for White LED [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2907-2912. |
[12] |
TONG Yi-ping, CHEN Teng . The Synthesis and Luminescence Measurement of YAG∶Ce3+ Phosphors by High Temperature Solid Phase Method [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2930-2934. |
[13] |
XU Yan-fang, ZHANG Guo-sheng*, LI Lu-hai, DING Ying-kun . A Method for Measuring Emission Spectrum of YAG Phosphor Used in LED White Light under Practical Conditions [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1834-1838. |
[14] |
WANG Lei1,3, ZHANG Jia-hua2, CUI Cai-e1,3, HUANG Ping1,3* . Effect of PbO on Emission Properties of YAG∶Ce3+ Phosphor [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(05): 1185-1188. |
[15] |
XU Guo-tang1, LIANG Pei1*, HUANG Jie1, WANG Le1, DONG Qian-min1, LIU Yang1, HUA You-jie2 . Study on Sr3LiMgV3O12∶Eu3+ Single-Phase Phosphor for White LED [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(04): 945-948. |
|
|
|
|