The Microstructure and Phase Composition of Metal Melting Marks Caused by Different Fire |
WANG Hai-rong, LIU Jian-yong, YAO Hao-wei, LIANG Dong* |
1. College of Engineering, Sun Yat-sen University, Guangzhou 510275, China 2. Key Laboratory of Fire Science and Technology of Guangdong Province, Guangzhou 510006, China |
|
|
Abstract Four different types of molten metal fire marks were studied through X-ray diffraction (XRD) and 3D image processing software (Image-pro). As a result, the microstructure, average grain size, phase composition and its distribution was obtained. The results showed that on the surface of molten metal fire marks there mainly existed cubic crystal of Cu2O, cellular crystals of Cu and columnar crystals of Cu. And in four different modes of fire, the microstructure and composition of molten metal marks was of significant difference, that is: (1) the average grain size of molten marks by a short circuit fire was about 3~5 μm, and its Cu2O was the lowest; melt marks by circuit overload had an average grain size similar to short-circuit, but their Cu2O content was about 30%; (2) melt marks by secondary short-circuit contained a certain number of larger diameter micro-hole, and their average grain size was about 30 μm; broadening and splitting provision of the diffraction peaks of Cu and Cu2O showed that their ablation was the deepest; (3) melting marks by fire showed the equiaxed maximum intensity of Cu2O diffraction peaks, and there was almost no micro-holes.
|
Received: 2011-11-29
Accepted: 2012-02-21
|
|
Corresponding Authors:
LIANG Dong
E-mail: gzliangd@163.com
|
|
[1] Chen C Y, Ling Y C, Wang J T, et al. Applied Surface, 2003, 203-204: 779. [2] Lee Eul-Pyeong, Ohtani Hideo, Seki Tsutomu, et al. Journal of Applied Fire Science, 2000, 9(4): 361. [3] Huang L M, Wang H T, Wang H T, et al. Chem. Master, 2002, 14: 876. [4] Kim Y G, Oh S K, Crooks R M. Chem. Master, 2004, 16: 167. [5] Chen Z, Shi E, Zheng Y, et al . Crystal Growth, 2003, 249: 294. [6] ZHANG Xin, LIU Jing, LI Guang-qiang(张 鑫,刘 静,李光强). North Master(南方金属),2006, 150: 15. [7] CAO Jun, DING Yu-tian, LU Zhen-hua(曹 军, 丁雨田, 卢振华). Transactions of Materials and Heat Treatment(材料热处理学报), 2011, 32(12): 147. [8] Feng Z,Marks C R,Barkatt A. Oxidation of Metals,2003,60(5/6): 393.
|
[1] |
LI Zong-xiang1, 2, ZHANG Ming-qian1*, YANG Zhi-bin1, DING Cong1, LIU Yu1, HUANG Ge1. Application of FTIR and XRD in Coal Structural Analysis of Fault
Tectonic[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 657-664. |
[2] |
OUYANG Ai-guo, YU Bin, HU Jun, LIN Tong-zheng, LIU Yan-de. Grade Evaluation of Grain Size in High-Speed Railway Wheel Steel Based on Laser-Induced Breakdown Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3428-3434. |
[3] |
HE Xiong-fei1, 2, HUANG Wei3, TANG Gang3, ZHANG Hao3*. Mechanism Investigation of Cement-Based Permeable Crystalline Waterproof Material Based on Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(12): 3909-3914. |
[4] |
Samy M. El-Megharbel*,Moamen S. Refat. In First Time: Synthesis and Spectroscopic Interpretations of Manganese(Ⅱ), Nickel(Ⅱ) and Mercury(Ⅱ) Clidinium Bromide Drug Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(10): 3316-3320. |
[5] |
Samy M. El-Megharbel*, Moamen S. Refat. Preparations and Spectroscopic Studies on the Three New Strontium(Ⅱ), Barium(Ⅱ), and Lead(Ⅱ) Carbocysteine Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(09): 2975-2979. |
[6] |
WANG Yi1, 2, LI Chang-rong1, 2*, ZHUANG Chang-ling1, 2. Study on Alumina/Lanthanum Oxide X-Ray Diffraction and Raman Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(08): 2480-2483. |
[7] |
LI Huan-tong1, 2, CAO Dai-yong3*, ZHANG Wei-guo1, 2, WANG Lu4. XRD and Raman Spectroscopy Characterization of Graphitization Trajectories of High-Rank Coal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(08): 2491-2498. |
[8] |
YE Xu1, QIU Zhi-li1, 2*, CHEN Chao-yang3, ZHANG Yue-feng1. Nondestructive Identification of Mineral Inclusions by Raman Mapping: Micro-Magnetite Inclusions in Iridescent Scapolite as Example[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(07): 2105-2109. |
[9] |
SUN Feng1, 2, YAN Qing-qing1, WANG Lu1, SUN Zhen-fei1. Study on the Conditions of Hydrothermal Synthesis of Chinese Purple BaCuSi2O6 and the Analysis of Its Products[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(07): 2284-2287. |
[10] |
Khaled Althubeiti. Synthesis and Structural Characterizations of Ternary Iron(Ⅱ) Mixed Ligand Complex: Low Cost Materialsas a Precursor for Preparation of Nanometric Fe2O3 Oxide[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1988-1992. |
[11] |
ZHANG Zhi-dan1, ZHAO Min-shuang1, ZHANG Li-na1, LIU Hang1, LI Rui1, SHENG Qian-nan1, GUO Dan1, ZHAO Xiao-yi2, ZHANG Jin-jing1*, ZHONG Shuang-ling1*. Application of Synchrotron Radiation X-Ray Diffraction Spectroscopy in the Study of Clay Minerals in Zonal Forest Soils[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(02): 529-534. |
[12] |
GE Tao1, 2, LI Yang1, Wang Meng2, CHEN Ping3, MIN Fan-fei1, ZHANG Ming-xu1. Spectroscopic Characterization of Carbon Structure in High Sulfur Fat Coal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(01): 45-51. |
[13] |
Sattam Al-Otaibi*. Eco-Friendly Fabrication of Selenium Nanoparticles by Solidstate Thermal Decomposition of SeCl4-L-Glutamine Precursor: Spectroscopic Characterizations[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(11): 3644-3648. |
[14] |
Abeer A El-Habeeb. Chelation Assignments of GaⅢ, GeⅣ and SiⅣ Metal Ions With Pipemidic Acid Antibiotic Drug: Synthesis, Spectroscopic Characterizations and Biological Studies[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3303-3308. |
[15] |
ZHANG Hai-yang1, GAO Bai1, 2*, FAN Hua3 , SHEN Wei1, LIN Cong-ye1. Mechanism of Fluoride and Arsenic Removal by Ce/γ-Al2O3 Based on XRD and FTIR[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2869-2874. |
|
|
|
|