| Analysis of Effects of Irradiation on the Crystal Size of Daemonorops Margaritae with X-Ray Diffractometry |
| WANG You-hong1，2, LIU Xing-e3, JIANG Ze-hui3*, FEI Ben-hua3, REN Hai-qing2 |
1. School of Forestry & Garden, Anhui Agricultural University, Hefei 230036, China
2. Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing 100091, China
3. International Centre for Bamboo and Rattan, Beijing 100102, China |
|
|
|
|
Abstract In order to find the relationships between the crystal size and the physical & mechanical properties, and to improve the levels of high value-added processing and utilizing for Chinese rattan resources, the daemonorops margaritae, Chinese unique rattan, was chosen as the research material, then the crystal size was measured and analyzed through the X-ray diffraction method before and after γ-ray irradiation. The results show that the crystal width is in the range between 1.901 and 3.019 nm, and the average width is 2.403 nm. The crystal length is in the range between 4.118 and 28.824 nm with an average length of 10.907 nm. After irradiation, the width of daemonorops margaritae is in the range between 2.139 and 3.540 nm, and the average width is 2.569 nm, and the crystal length dramatically changes in the range between 5.765 and 38.432 nm with a mean of 15.530 nm. Both of the scope and the mean value of the crystal width and length increase after irradiation.
|
|
Received: 2009-10-09
Accepted: 2010-01-08
|
|
|
|
Corresponding Authors:
WANG You-hong
E-mail: jiangzehui@icbr.ac.cn
|
|
[1] JIANG Ze-hui(江泽慧). Bamboo and Rattan in the Wood(世界竹藤). Shenyang: Liaoning Science and Technology Publishing House(沈阳: 辽宁科学技术出版社), 2002.
[2] XU Huang-can, YIN Guang-tian, ZENG Bing-shang, et al(许煌灿, 尹光天, 曾炳山, 等). Forest Pesearch(林业科学研究), 1994, 7(1): 20.
[3] ZHAO Xia, HUANG Shi-neng, XIAN Guang-yong, et al(赵 霞, 黄世能, 冼光勇, 等). Economic Forest Research(经济林研究), 2007, 25(1): 46.
[4] Evans T D, Sengdala K. Economic Botany, 2002, 56(2): 147.
[5] YIN Guang-tian, YANG Jin-chang, SUN Bing, et al(尹光天, 杨锦昌, 孙 冰, 等). Journal of Central South Forestry University(中南林学院学报), 2005, 25(6): 74.
[6] Abasolo W P, Yoshida M, Yamamoto H. World Bamboo and Rattan(世界竹藤通讯). Translated by ZHOU Ting(周 婷，译)，2003, 1(4): 32.
[7] XU You-ming(徐有明). Wood Science(木材学). Beijing: China Forestry Publishing House(北京: 中国林业出版社), 2006.
[8] Jiang Zehui. IAWA Bulletin, 1990, 11(2): 126.
[9] YANG Xin-ping(杨新萍). Journal of Shanxi Normal University(Natural Science Edition)(山西师范大学学报·自然科学版), 2007, 21(1): 72.
[10] CONG Qiu-zi(丛秋滋). Polycrystalline Two-Dimensional X-Ray Diffraction(多晶二维X射线衍射). Beijing: Science Press(北京: 科学出版社), 1997.
[11] LI Chong-gui, TIAN Wei, YANG Yong, et al(李崇桂, 田 伟, 杨 勇, 等). Transactions of Materials and Heat Treatment(材料热处理学报), 2007, 28(增刊): 228.
[12] CHEN Si-shun, CHEN Xin-hua, DING Ming-jie, et al(陈思顺, 陈新华, 丁明洁, 等). Shanghai Chemical Industry(上海化工), 2005, 30(11): 19.
[13] LIU Jin-hong, WANG Li, XUE Ping-ping, et al (刘锦宏, 王 丽, 薛萍萍, 等). Journal of Lanzhou University(Natural Science Edition)(兰州大学学报·自然科学版), 2005, 41(1): 78～81.
|
| [1] |
FAN Qing-jie, SONG Yan, LAI Shi-quan*, YUE Li, ZHU Ya-ming, ZHAO Xue-fei. XRD Structural Analysis of Raw Material Used as Coal-Based Needle Coke in the Coking Process[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(06): 1979-1984. |
| [2] |
PAN Qiu-li1, SHAO Jin-fa1, LI Rong-wu2, CHENG Lin1*, WANG Rong1. Non-Destructive Analysis of Red and Green Porcelain in Qing Dynasty[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(03): 732-736. |
| [3] |
WANG Yi1, 2, LI Chang-rong1, 2*, ZENG Ze-yun1, 2，XI Zuo-bing1, 2, ZHUANG Chang-ling1, 2. Study on Alumina/Cerium Oxide X-Ray Diffraction and Raman Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1841-1845. |
| [4] |
HUANG Wei-bo, CHEN Jia-yun, HUANG Fang, HUANG Li-shan, OUYANG Jian-ming*. Effects of Different Molecular Weight of Gracilaria Lemaneiformis Polysaccharide on Calcium Oxalate Crystal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(04): 1163-1170. |
| [5] |
DONG Pei-jie1, ZHANG Wen-bo1*, LU Wei2. A NIR Study on Hydrogen Bonds of Bamboo-Based Cellulose Ⅱ[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(04): 1260-1264. |
| [6] |
ZHANG Feng1, LIU Shan1, PU Mei-fang1, TANG Qi-qi1, WU Bin-bin1, LI Lin2, HU Qi-wei3, XIA Yuan-hua3, FANG Lei-ming3, LEI Li1*. Pressure and Temperature Dependence of Raman Spectroscopy of Solid Ionic Crystal β-K0.294Ga1.969O3[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(03): 807-812. |
| [7] |
KU Ya-lun1, YANG Ming-xing1, 2*. Study on Spectral Characteristics of Turquoise With Blue “Water Ripple” From Shiyan, Hubei Province[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(02): 636-642. |
| [8] |
SONG Chen, ZHANG Zhi-jie*, BIAN Bao-lin*. The Hypothesis of Medicinal Gypsum Cooling Material[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(06): 1716-1721. |
| [9] |
WANG You-hong1, ZHANG Fei-fei1，2, XUE Xia1, JI Bi-chao1, LI Dan1, ZHANG Li-ping1. Application of X-Ray in the Study of Cell Wall Structure of Rattan Fibers[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(05): 1442-1446. |
| [10] |
XU Lai-wu1, WANG Yong2, YANG Cheng-da1, ZHU Yi-fan1, HUANG Qiao1, QIN Ying1*. Spectral Analysis of Surface Corrosion Products of Two Embedded Gold or Silver Bronze in Ancient China[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(05): 1457-1460. |
| [11] |
ZHANG Hao1,2, GAO Qing1, HAN Xiang-xiang1, RUAN Gao-yang1, LIU Xiu-yu1. Mechanism Analysis of Formaldehyde Degradation by Hot Braised Slag Modified Activated Carbon Based on XRF and XRD[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(05): 1447-1451. |
| [12] |
XU Lei1,3, YUAN Hui-min1,3*, JIANG Rong-feng1,3, WANG Yan-feng2, WU Liang2, WANG Sheng-feng2. Advances in X-Ray Diffraction for the Determination of Clay Minerals in Soil[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1227-1231. |
| [13] |
WANG Guo-qiang1, 2, 3, 4, CAO Jian-jin1, 2, 3, 4*, DENG Yong-kang1, 2, 3, 4, LIU Xiang1, 2, 3, 4. XRD and NIR Analysis on Minerals of Fault Sections from Dabaoshan Polymetallic Deposit, Guangdong[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(02): 610-615. |
| [14] |
SUN Hai-yan1, 2, JIA Ru1, 2, WU Yan-hua2, ZHOU Liang3, LIU Sheng-quan3, WANG Yu-rong1, 2*. Rapid Detection of Microstructural Characteristics of Heartwood and Sapwood of Chinese Fir Clones[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 184-188. |
| [15] |
WANG Hao1, 2, JIN Bao-sheng1*, WANG Xiao-jia1, YU Bo2, CAO Jun1. Spectroscopical Analysis and Coking Mechanisim of Char Layer in Ascension Pipe of Coke Oven[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(10): 3148-3153. |
|
|
|
|