高氯酸消解-ICP-OES测定炭复合磷酸铁锂中的锂、铁、磷

doi:10.3964/j.issn.1000-0593(2021)09-2703-07

Abstract
References
Related Citation (6)

Download: PDF (1561 KB)
Export: BibTeX | EndNote (RIS)

Abstract Lithium iron phosphate is one of the main industrial raw materials for the lithium-ion polymer battery industry. Compared with traditional raw material lithium cobalt oxides, lithium iron phosphate has significant advantages in specific energy, battery life, cost and environmental compatibility. Lithium iron phosphate, which is carbon composite cathode material for lithium-ion batteries, is selected as the research object. The content of lithium, iron and phosphorus was determined simultaneously by inductively coupled plasma optical emission spectrometry (ICP-OES). Sample digestion, analytical wavelength, parameters of instrument, solvent effect, background interference for analytical wavelength, accuracy and precision of the method had been discussed. Carbon composite lithium iron phosphate contains about 5% carbon. 0.100 g Sample was digested with 5 mL perchloric acid, heated the digestion solution to clarify visual, and continued heated the solution to smoke and repeated the operation twice as the sample could be digested completely. The sample digestion was checked by the three-dimensional (3D) video microscope. The visual clarify solution was checked by 30 magnification times. It showed that there still had an insoluble matter in the solution. After repeated the operation of added water and continue heated to smoke twice, checked digestion solution by 30 magnification times again; it showed that the sample had been digested completely. The digestion solution was transferred to a 100 mL volumetric flask, diluted to volume and mixed. The analytical solution was prepared as followed: diluted the constant volume digestion solution with the rate of 10∶100 to a 100 mL volumetric flask. The best parameters of ICP-OES for this method were: High-frequency power, 1.1 kW. Atomizer flow: 0.8 L·min^-1. Analytical wavelength, observe direction & observe height: Li610.365 nm-axial，Fe259.940 nm-radial/12 mm，P178.222 nm-axial，P213.618 nm-radial/12mm. Calibration solutions were prepared according to matrix matching with regent blank prepared with sample simultaneously, the preparation of calibration solution can minimize the solvent effect. For Li 610.365 nm, fast, automated curve-fitting (FACT) was used to eliminate background interference of Ar 610.564 nm. Under the optimal conditions, the analytical ranges were: Li, 1%~9%, Fe, 20%~40%, P, 10%~30%. The coefficient of the calibration curve, r＞0.999 0. The relative standard deviation (RSD, n=7) was 0.35 %~1.01 %. The standard recovery rate was 91.2%~112%. Internal round robins (IRR) result was evaluated by F, t-test, the result showed no obvious difference between the test results of two operators. The method has promotional value for application in the lithium-ion polymer battery industry.

Key words：Lithium iron phosphate; Inductively coupled plasma optical emission spectrometry (ICP-OES); Perchloric acid; Lithium Ion battery；Cathode material

Received: 2020-08-28 Accepted: 2020-12-19

ZTFLH:

O657.3

Cite this article:

URL:

https://www.gpxygpfx.com/EN/10.3964/j.issn.1000-0593(2021)09-2703-07 OR https://www.gpxygpfx.com/EN/Y2021/V41/I09/2703

[1] BAI Xiao-yan, MA Xiao-li, ZHANG Chao, et al(白晓艳, 马小利, 张超, 等). Chinese J. of Power Sources(电源技术), 2015, 39(8): 1641.
[2] GB/T 30835—2014, Lithium Iron Phosphate-Cabon Composite Cathod Materials for Lithium Ion Battery(锂离子电池用炭复合磷酸铁锂正极材料). National Standards of the People’s Republic of China(中华人民共和国国家标准).
[3] GB/T 33822-2017, Nano Lithium Iron Phosphate(纳米磷酸铁锂). National Standards of the People’s Republic of China(中华人民共和国国家标准).
[4] YS/T 1028.1—2015, Methods for Chemical Analysis of Lithium Iron Phosphate—Part 1：Determination of Total Iron Content-Titannium Trichloride Reduction Potassium Dichromate Titration Methods(磷酸铁锂化学分析方法第1部分：总铁量的测定三氯化钛还原重铬酸钾滴定法). Non-Ferrous Metals Industry Standards of the People’s Republic of China(中华人民共和国有色金属行业标准).
[5] YS/T 1028.2—2015, Methods for Chemical Analysis of Lithium Iron Phosphate-Part 2：Determination of Lithium Content-Flame Photometry(磷酸铁锂化学分析方法第2部分：锂量的测定火焰光度法). Non-Ferrous Metals Industry Standards of the People’s Republic of China(中华人民共和国有色金属行业标准).
[6] YS/T 1028.3—2015, Methods for Chemical Analysis of Lith Iron Phosphate-Part 3：Determination of Phosphor Content-Quinoline Phosphomolybdate Gravimetry(磷酸铁锂化学分析方法第3部分：磷量的测定磷钼酸喹啉称量法). Non-Ferrous Metals Industry Standards of the People’s Republic of China(中华人民共和国有色金属行业标准).
[7] MA Xiao-li, BAI Xiao-yan, LIU Mei-zi, et al(马小利, 白晓艳, 刘美子, 等). Metallurgical Analysis(冶金分析), 2014, 34(10): 21.
[8] WANG Xiao-yan, WANG Xing，WANG Yu-feng(王晓艳, 王星, 王玉锋). Chinese J. of Power Sources(电源技术), 2006, 30(9): 764.
[9] LIU Ping, FAN Yong-li, PEI Jin-hai(刘平, 樊勇利, 裴金海). Chinese J. of Power Sources(电源技术), 2014, 38(4): 627.
[10] YAN Zi-xin, QU Jing-kui, YU Zhi-hui, et al(严子心, 曲景奎, 余志辉, 等). Chinese J. Anal. Chem.(分析化学)，2019, 47(3): 423.
[11] LIU Jia, LIU Bing-bing, HAN Mei, et al(刘佳, 刘冰冰, 韩梅, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2018, 38(6): 1880.