Effect of Mixed Interface on the Performance of Solution-Processed Phosphorescent OLEDs |
SONG Dan-dan, ZHAO Su-ling*, XU Zheng, ZHANG Fu-jun, LU Li-fang, ZHANG Yan-fei, KONG Chao, YAN Guang |
Key Laboratory of Luminescence and Optical Information (Beijing Jiaotong University), Ministry of Education,Beijing 100044,China |
|
|
Abstract In the present work, in order to improve electron injection and transport at the interface of the hole blocking layer (HBL) and the electron transport layer (ETL) in the hole-domain solution processed phosphorescent organic light emitting devices (PhOLEDs), the mixed interface layer (MIL) was fabricated by partially co-doping hole blocking material 2,9-dimethyl-4,7-diphenyl-1,10-phenanthroline (BCP) and electron transport material tris(8-quinolinolato) aluminum (Alq3) between HBL/ETL. The MIL thickness was kept at 10nm, while the doping ratio of these two materials varied. Under a given electric field, the devices with the MIL at any mixed ratios all show much higher luminance and current density than those with a typical interface. For example, the luminance power and current density at 10 V for a typical device are 1.03 μW and 5.13 mA·cm-2, while in case of mixed interface are 3.64 μW and 18.1 mA·cm-2, respectively. From data results and theoretical analysis, the possible derivation of these improvements is considered to be the reduced electron accumulation at the interface resulting from the reduced electron injection energy barrier and lowered transport mobility by BCP material, which leads to an increase in electron amount in the emission layer and therefore the higher luminance and current density.
|
Received: 2010-11-10
Accepted: 2011-01-20
|
|
Corresponding Authors:
ZHAO Su-ling
E-mail: slzhao@center.njtu.edu.cn
|
|
[1] Reineke S, Lindner F, Schwartz G, et al. Nature(London), 459(2009) 234. [2] Gu G, Burrows P E, Venkatesh S, et al. Thompson, Optics Letters, 1997, 22: 172. [3] Baldo M A, O’Brien D F, You Y, et al. Nature(London), 1998, 395: 151. [4] O’Brien D F, Baldo M A, Thompson M E, et al. Appl. Phys. Lett., 1999, 74: 442. [5] Cleave V, Yahioglu G, Le Barny P, et al. Adv. Mater., 1999, 11: 285. [6] He G, Pfeiffer M, Leo K, et al. Appl. Phys. Lett., 2004, 85: 3911. [7] Tao Y, Wang Q, Yang C, et al. Adv. Funct. Mater., 2010, 20: 2923. [8] Lee C H, Lee K B, Kim J J. Appl. Phys. Lett., 2000, 77: 2280. [9] Vaeth K M, Tang C W. J. Appl. Phys., 2002, 92: 3447. [10] Liu D A, Fina M, Chen Z Y, et al. Appl. Phys. Lett., 2007, 91: 093514. [11] Liu D A, Fina M, Guo J H, et al. Appl. Phys. Lett., 2009, 94: 013110. [12] Vaynzof Y, Dennes T J, Schwartz J, et al. Appl. Phys. Lett., 2008, 93: 103305. [13] Lee J Y, Kwon J H. Appl. Phys. Lett., 2006, 88: 183502. [14] Wang Y, Hua Y L, Wu X M, et al. Appl. Phys. Lett., 2008, 93: 113302. [15] Lee C B, Uddin A, Andersson T G. Solid State Communications, 2007, 142: 206. [16] Pope M, Swenberg C E. Electronic Processes in Organic Crystals, Clarendon: Oxford, 1982. [17] Fung M K, Xie Z, Lee S T, et al. Adv. Mater. Weinheim, Ger., 2002, 14: 1317. [18] Park H, Shin D S, Yu H S, et al. Chae, Appl. Phys. Lett., 2007, 90: 202103.
|
[1] |
XU Yong-long, XU Yu, KONG Wei-li, ZOU Wen-sheng*. Purely Organic Room Temperature Phosphorescence Activated by Heavy Atom Effect for Photodynamic Antibacteria[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(09): 2910-2915. |
[2] |
ZHU Hong-wei1, CHENG You-fa1, CHEN Shu-xiang2*, FAN Chun-li1, LI Ting1, LIU Hai-bin1, ZHAO Xiao-xue1SHAN Guang-qi1, LI Jian-jun1. Spectroscopic Characteristics of a Natural Diamond Suspected of Synthetic Diamond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1690-1696. |
[3] |
LI Ying-ying1, ZHANG Zhi-qing1*, WU Xiao-hong2, Andy Hsitien Shen1*. Photoluminescence in Indonesian Fossil Resins[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(03): 814-820. |
[4] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
[5] |
SUN Qin-jun*, SHI Xiao-lei, GAO Li-yan, ZHOU Shao-long, WU Jun, HAO Yu-ying*. Research on Efficiency Improvement of Inverted PTB7∶PC70BM Solar Cells Using ZnO Nanofibers Prepared by Electrospinning as Electron Transport Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(11): 3368-3373. |
[6] |
LI Jian-jun1,2, FAN Cheng-xing3, CHENG You-fa1, CHEN Shu-xiang4, LI Gui-hua1, TIAN Min-min5. Direct Evidence of Charge Transfer at Boron Acceptors Being Linked to Phosphorescence in Diamond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(06): 1714-1717. |
[7] |
CHENG Xue-li. Density Functional Theory Investigations on the Absorption and Emission Spectra of β-Benzylacetophenone[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(05): 1514-1518. |
[8] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
[9] |
DU Bao-an, LIU Cheng, CAO Yu-hong, CHEN Li-na . Study of the Mn-Doped ZnS Quantum Dots as the Phosphorescence Probes to Detect the Micro-Quantity Hg2+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(04): 1070-1074. |
[10] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326. |
[11] |
LI Li-qing1, 2, CHENG Xue-li1, 3*, ZHAO Yan-yun1, HE Guo-fang1, LI Feng4 . Density Functional Theory Investigations of the Spectroscopic Characteristics and Luminescent Mechanisms of Dipterex and Dichlorvos[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(01): 122-127. |
[12] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Properties of Phosphorescent Organic Light-Emitting Diodes with Different Doping Order on Light Emitting Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1763-1766. |
[13] |
HUANG Jin, ZHANG Fang-hui* . Influence of BCP on Efficiency of Red Phosphorescent Electroluminescent Device [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1767-1770. |
[14] |
LIU Sheng-qiang1, YU Jun-sheng1*, ZENG Yan-bo1, ZHAO Juan1, DU Chun-lei2 . Spectral Characteristics of White Organic Light-Emitting Devices Based on Phosphorescent System of Three Iridium Chelates [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(03): 636-641. |
[15] |
LIU En-zhou1, FAN Jun1*, HU Xiao-yun2, YE Yan-xi2, HOU Wen-qian1 . Upconversion Properties of Sodium and Aluminum Fluorides Coated BaF2 Material [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(01): 61-64. |
|
|
|
|