Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2
1. Yunnan Olightek Opto-Electronic Technology Co., Ltd., Kunming 650223, China 2. Kunming Institute of Physics, Kunming 650223, China
Abstract：The top emission organic light-emitting devices were fabricated on the multi-layers metal anode with co-doping method in single host system. In experiment, the multilayer Al/Mo/MoO3 anode on silicon are deposited, systematically analyzed the effect MoO3 thickness on the reflectance and found the mechanism of the MoO3 thickness variation to the reflectivity of Al/Mo/MoO3 on silicon. Experimental results showed that the luminous intensity of blue, green and red appear to change according to the current density increase, and compared with the red intensity, the luminous intensity of blue and green gradually increased. The emission in this host-guest co-doping system is considered to usually involve two emission mechanisms, energy transfer and carrier trapping, and the energy transfer and carrier trapping between the host-guest should be responsible for chromaticity coordinates shift of organic white emitting light devices. In addition, through further study, it is proved the electroluminescence intensity of dopant linearly decrease with the driving voltage applied to the device by theoretical and experimental results.
王光华1,2，赵惠琼1,2，邓荣斌1，段 瑜1，2，孙 浩1，张筱丹1,2，周 琴1，钱金梅1，万锐敏1,2，季华夏1，姬荣斌2 . 顶发射白光OLED器件制备及其色坐标漂移机制研究 [J]. 光谱学与光谱分析, 2016, 36(11): 3758-3763.
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763.
[1] Tang C W, Vanslyke S A. Appl. Phys. Lett., 1987, 51(12): 913. [2] Kido J, Kimura M, Nagai K. Science, 1995, 267：1332. [3] Wang Fengxia, Qiao Xianfeng, Xiong Tao, et al. Organic Electronics, 2008, (9): 985. [4] Zhao Fangchao, Zhang Zhiqiang, Liu Yipeng, et al. Organic Electronics, 2012，(13): 1049. [5] Jou Jwo-Huei, Chen Po-Wei, Chen Yu-Lin, et al. Organic Electronics, 2013，(14): 47. [6] Du Xiaoyang, Huang Yun, Tao Silu, et al. Dyes and Pigments, 2015，(115): 149. [7] Lee Jonghee, Lee Joo-Won, Cho Nam Sung, et al. Current Applied Physics, 2014, (14): 84. [8] Kim Nam Ho, Kim You-Hyun, Yoon Ju-An, et al. Journal of Luminescence, 2013, (143)：723.