Study of Photoluminesence Property of CdS/PAMAM Nanocomposites
JIN Yu-juan1, LUO Yun-jun2*, XU Guo-zhi1, YANG Biao1
1. Material and Mechanic Engineering Department, Beijing Technology and Business University, Beijing 100048, China 2. Material Department, Beijing Institute of Technology, Beijing 100081, China
Abstract:The photoluminescence property of CdS/PAMAM nanocomposites in water at different ratio of Cd2+ to PAMAM(r) was studied by fluorescence emission spectrum, and the according mechanism was explored. The results indicate that in the irradiation of UV light at the wavelength of 330 nm, two peaks were shown in the fluorescence emission spectrum of CdS/PAMAM nanocomposites. One peak was attributed to PAMAM dendrimers, and the another came from CdS QDs. The strength of the frontier fluorescence emission peak became weaker and weaker, and at last disappeared with the enhancement of the ratio of Cd2+ to PAMAM;the strength of the latter fluorescence emission peak became stronger, which indicates that the electron at valence band of N atom in amines of dendrimers was transferred to CdS QDs. Oil latent finger marks deposited on transparent adhesive tapes surface treated with pure PAMAM solution with blue photoluminescence was not clear enough because of the blue light emitted from the impurity in adhesive tapes; Latent finger marks emitted strong yellow light and were successfully detected with good resolving rate with CdS/dendrimer solution with r of 10, which shows good reference value for detecting finger marks on surfaces with impurities emitting different photoluminescence colors.
靳玉娟1,罗运军2*,许国志1,杨 彪1 . CdS/PAMAM树形分子纳米复合材料的荧光性能研究[J]. 光谱学与光谱分析, 2011, 31(12): 3311-3314.
JIN Yu-juan1, LUO Yun-jun2*, XU Guo-zhi1, YANG Biao1 . Study of Photoluminesence Property of CdS/PAMAM Nanocomposites . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(12): 3311-3314.
[1] Jagadeeswari S, Jhonsi M A, Kathiravan A, et al. Journal of Luminescence, 2011, 131(4): 597. [2] Jin S K, Kwang J C, Thanh H T, et al. Journal of Colloid and Interface Science, 2011, 353(2): 363. [3] Xue M, Wang X, Wang H, et al. Talanta, 2011, 83(5): 1680. [4] Menzel E R, Savoy S M, Ulvick S J, et al. Journal of Forensic Science, 2000, 45(3): 545. [5] Menzel E R, Takatsu M, Murdock R H, et al. Journal of Forensic Science, 2000, 45(4): 770. [6] Bouldin K K, Menzel E R, Takatsu M, et al. Journal of Forensic Science, 2000, 45(6): 1239. [7] Jin Yujuan, Luo Yunjun, Li Guoping, et al. Forensic Science International, 2008, 179(1): 34. [8] Jessirie D, Hilton K, Amanda V E. Forensic Science International, 2009, 187: 97. [9] Lemon B I, Crooks R M. Journal of American Chemistry Society, 2000, 122: 12886. [10] JIN Yu-juan, LUO Yun-jun, LI Guo-ping, et al(靳玉娟, 罗运军, 李国平, 等). Transactions of Beijing Institute of Technology(北京理工大学学报), 2010, 30(7): 97. [11] LU Wen-ting, LI Guo-ping, LUO Yun-jun, et al(卢文婷, 李国平, 罗运军, 等). Chemical Journal of Chinese University(高等学校化学学报), 2009, 30(7): 1459. [12] Auten B J, Lang H F, Chandler B D. Applied Catalysis B: Environmental, 2008, 81(3-4): 225. [13] Takeshi E, Tomokazu Y, Kunio E. Journal of Colloid and Interface Science, 2005, 286(2): 602. [14] LI Guo-ping, LUO Yun-jun, TAN Hui-min(李国平, 罗运军, 谭惠民). Acta Chimica Sinica(化学学报), 2004, 62(12): 1158. [15] JIN Yu-juan, LUO Yun-jun, LI Guo-ping, et al(靳玉娟, 罗运军, 李国平, 等). Imaging Science and Photochemistry(影像科学与光化学), 2010, 28(2): 111. [16] Wang D J, Imae T. Journal of American Chemistry Society, 2004, 126: 13204. [17] Wang D J, Imae T, Miki M. Journal of Colloid Interface Science, 2007, 306: 222. [18] Suarez I J, Rosal R, Rodriguez A, et al. Trends in Analytical Chemsitry, 2011, 30(3): 492. [19] Hedden R C, Bauer B J, Smith A P, et al. Polymer. 2002, 43: 5473.