Abstract：After nano-particles (ZnO) had been encapsulated by a kind of water-soluble cellulose Hydoxyl-Propyl-Methyl Cellulose(HPMC), then methyl methacrylate was grafted onto the surface of them. Thus the surface of nano-ZnO had been successfully modified. FTIR, DTA and TEM were utilized to confirm the results. FTIR shows that HPMC was adsorbed onto the surface of ZnO, and PMMA was also grafted onto its surface, DTA says that the heat stability of HPMC，HPMC-g-PMMA and ZnO/HPMC-g-PMMA increased greatly, TEM photo demonstrates that polymer adhered onto the surface of nano-ZnO which was encapsulated by a layer of film-like polymer.
宇海银，杜 俊，顾家山，关明云，吴正翠，凌 青，孙益民 . 纳米ZnO的表面化学修饰及其分析表征 [J]. 光谱学与光谱分析, 2004, 24(02): 177-179.
YU Hai-yin, DU Jun, GU Jia-shan, GUAN Ming-yun, WU Zheng-cui, LING Qing, SUN Yi-min . Chemical Modification on the Surface of Nano-Particles of ZnO and Its Characterization . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(02): 177-179.