Using PAA Template to Fabricate SERS Substrate and the SERS Detection of Melamine
LI Jun-mei1, XU Xiao-xuan1,2*, WANG Yu-fang1, WANG Bin1,2, SUN Jia-ming1,2,ZHANG Cun-zhou1,2
1. Institute of Physics, Nankai University, Tianjin 300071, China 2. The Key Laboratory of Weak Light Nonlinear Photonics, Ministry of Education, Nankai University, Tianjin 300457, China
Abstract:The authors have got silver film with orderly arranged nanoparticles as the surface-enhanced Raman spectra (SERS) substrates using porous anodic alumina templates (PAA). A silver film (99.99%) with the thickness of several millimeters was thermally evaporated onto the PAA templates and the SERS substrate was got after removing the PAA templates in hydrochloric acid. SERS spectra of pyridine (0.01 mol·L-1) were measured on Renishaw 2000 Ramanscope with a He-Ne (632.8 nm) laser as an excitation source in backscattering geometry, and the average enhancement factors were more than 105. The authors compared SERS spectra of pyridine from the SERS substrates and from Ag film evaporated directly on glass slide, and the former was 30 times stronger than the latter. The authors got different SERS spectra of pyridine while changing the excitation laser power. It was found that the relationship between the peak intensity of SERS spectra and the excitation laser power was linear as the normal Raman spectrum. We used the substrates to detect melamine, 2.5 mg·L-1 melamine solution could be recognized although excitation laser power was below 1mW.
李俊梅1,徐晓轩1,2*,王玉芳1,王 斌1,2,孙甲明1,张存洲1,2 . 以PAA为模板制备SERS基底及对三聚氰胺的检测 [J]. 光谱学与光谱分析, 2010, 30(10): 2663-2666.
LI Jun-mei1, XU Xiao-xuan1,2*, WANG Yu-fang1, WANG Bin1,2, SUN Jia-ming1,2,ZHANG Cun-zhou1,2. Using PAA Template to Fabricate SERS Substrate and the SERS Detection of Melamine . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(10): 2663-2666.
[1] Fleischmann M, Hendra P J, McQuillan A. J. Chem. Soc. Chem. Commun., 1973, (3): 80. [2] Fleischmann M, Hendra P J, McQuillan A. Chem. Phys. Lett., 1974, 26: 163. [3] CHEN Wei-wei, FENG Shang-yuan, LIN Wen-shuo, et al(陈伟炜,冯尚源,林文硕,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2009, 29(9), 2450. [4] Jeanmaire D L,Van Duyne R P. J. Electroanal. Chem.,1977,84:1. [5] Kerker M, Wang D S, Chew H. Appl. Opt., 1980, 19: 3373. [6] Gersten J,Nitzan A. J. Chem. Phys., 1980, 73: 3023. [7] García-Vidal F J,Pendry J B. Phys. Rev. Lett., 1996, 77: 1163. [8] Gunnarsson L, Bjerneld E J, Xu H, et al. Appl. Phys. Lett.,2001, 78:802. [9] Liu Y J, Zhang Z Y, Zhao Q, et al. Appl. Phys. Lett., 2008, 93: 173106. [10] Masuda Hideki, Satoh Masahiro. Jpn. J. Appl. Phys., 1996, 35: L126. [11] Lombardi I, Cavallotti P L, Carraro C, et al. Sens. Actuators B, 2007, 125: 353. [12] LING Li, XU Min-min, GU Ren-ao(凌 丽,徐敏敏,顾仁敖). Acta Chimica Sinica(化学学报),2007, 65(9): 779. [13] Lu Zhicheng, Ruan Weidong, Yang Jingxiu, et al. J. Raman Spectrosc.,2009, 40:112. [14] Sun Mengtao, Liu Shasha, Chen Maodu, et al. J. Raman Spectrosc., 2009, 40: 137. [15] Meier R J,Maple J R,Hwang M J,et al. J. Phys. Chem.,1995,99:5445. [16] He Lili, Liu Yang, Lin Mengshi, et al. Sens. & Instrumen. Food Qual.,2008,2: 66.