Raman Spectra Analysis of Calcium Metaphosphate Glass-Ceramics
LIANG Xiao-feng1，2, YIN Guang-fu1*，YANG Shi-yuan2, MA Guo-hua2, WANG Jun-xia2
1. School of Materials Science and Engineering of Sichuan University, Chengdu 610065，China 2. Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621010，China
Abstract：In the present paper, calcium metaphosphate glass with molar ratio of Ca/P=0.45 was prepared and Ca(PO3)2 glass-ceramics were obtained by reheating the glass at 300-700 ℃. The Raman spectra of samples were measured. The bands of these Raman spectra were assigned and analyzed. The length of P—O bonds was calculated by using Raman wavenumbers. The results show that the crystal phase in glass was obtained when preserved at 300 ℃ for 3 h;Along with temperature increase, νs(PO2) and νs(POP) bands are stable in frequency, the bands intensity increases and fine structure appears in the Raman spectra fingerprint. The crystallization degree of glass-ceramics surface is higher than the inner. The length of P—O bonds changes during the heating process and crystallization. The length of O—P—O chain bonds changes to 158.27 pm from 159.96 pm, and terminal P—O changes to 149.02 pm from 147.92 pm, when Ca(PO3)2 glass becomes β-Ca(PO3)2 crystal.
[1] Rezwan K, Chen Q Z, Blaker J J. Biomaterials，2006，27：3413. [2] Eui Kyun Park, Yoang Eud Lee, Je-Yong Choi, et al. Biomaterials, 2004，25：3403. [3] Yoshio Ota, Tetsushi Iwashia, Toshihiro Kasuga, et al. Journal of Materails Science: Materials in Medicine，2002，13：895. [4] Toshihiro Kasuga, Yoshio Ota, Kenji Tsuji, et al. J. Am. Ceram. Soc., 1996，79：1821. [5] Yoshihiro Abe, Toshihiro Kasuga, Hideo Hosono, et al. Journal of American Ceramic Society, 1984, 67(7)c: 142. [6] Lee Jinn-shing, Hsu Chung-king. Thermochimica Acta, 1999，339：103. [7] Wang Kai, Christian Russel, Liu Changsheng. Materials Chemistry and Physics, 2008，111：106. [8] Yuanzheng Yue, Ralf Keding, Christian Russel. Journal of Materials Research，1999，14：3983. [9] Boolchand P, Jin Mingji, Novita D I, et al. Journal of Raman Spectroscopy，2007，38：660. [10] ZHAO Si-jie, YOU Jing-lin, CHEN Hui, et al(赵思杰，尤静林，陈 辉，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2009，29(7)：188. [11] Rothammel W，Burzlaff H，Specht R. Acta Cryst., 1989，C45：551, 4. [12] Bertoluzza A, Caccari S, Tinti A, et al. Journal of Materails Science: Materials in Medicine, 1995，6：76. [13] Prokupkova P, Mosner P, Koudelka L, et al. Journal of Materials Science, 1998，33：743. [14] Popovic L, de Waal D, Boeyens J C A. Journal of Raman Spectroscopy，2005，36：2.