Abstract:The nanocrystalline of Y2O3:Eu3+ red phosphor has been studied. The result shows that the maximum excitation spectrum of Y2O3:Eu3+ peaks at λex=252.6 nm, while the maximum emission spectrum peaks at λem=613.4 nm under 254 nm excitation. The luminescence intensity increases with the growth of agglomerate size, adding assistant melting agent and increasing the sintering temperature. The hanging-bonds and the defects on the surface of nanocrystalline Y2O3:Eu3+ particle were removed and its luminescence intensity was increased by the coating process.
[1] WEI Kun(魏 坤). Chinese Rare Earths(稀土),2001,22:37. [2] LI Qiang, GAO Lian, YAN Dong-sheng(李 强,高 濂,严东生). J. Inorg. Mater.(无机材料学报),1997,12(2):237. [3] SHI Chun-shan(石春山). Chinese Rare Earths(稀土), 1984, 5(1): 65. [4] GUO Feng-yu, LIU Nian-hong(郭凤瑜,刘念红). Acta Sientiarum Naturalium Universitatis Pekinensis(北京大学学报),1990,26(2):191. [5] 吉林物理研究所,中国科技大学编. 固体发光. 1976,61. [6] LI Qiang, GAO Lian, YAN Dong-sheng(李 强,高 濂,严东生). J. Inorg. Mater.(无机材料学报),1999,14(1):150.