1. Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan 030024, China 2. The College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China 3. The College of Science, Taiyuan University of Technology, Taiyuan 030024, China
Abstract:A Schiff base organic metal complex,Bis(salicylidene)-1,2-phenylenediam-ine Zinc(Ⅱ) with high purity, was synthesized and purified by vacuum sublimation. Its structure, thermal stability and energy band structure were investigated by element analysis, FTIR spectra, TG-DTA curve, UV-Vis absorption spectra, fluorescece emission spectra and PL spectra. Experimental results showed that the complex is a thermally stable, polycrystalline material, with glass temperature and decomposition temperature being 183 and 449 ℃, respectively. In its infrared spectrum, a high intensity band was at about 1 385 cm-1. This band was typical of the conjugated CN stretching vibration, which shifted to higher frequency in relation to the free ligand of salicylaldehyde with 1,2-phenylenediamine. The new bnd at 529 cm-1 was assigned to Zn—O stretching vibration. Its UV absorption bands were at about 297 and 406 nm, and its tetrahydrofuran solution emitted intensive blue-green fluorescence at the peak wavelength of 508 nm. The absorption band at about 406 nm can be assigned to the intrinsic absorption of CN. Its optical gap was about 2.62 eV,which was determined by the intrinsic absorption band edge of the complex in tetrahydrofuran solution. Under UV excitation at 365 nm, the complex in film emitted yellow-green fluorescence with the maximum emission peak at 562 nm and a full-width at half-maximum of 48.5 nm in PL spectra. Finally, yellow organic light-emitting devices using this complex as the emissive layer were fabricated and investigated.
Key words:Schiff base;Electroluminescence;Thermal stability;Energy band structure
[1] YANG Yu-hui, ZHAN Yi-qiang, DING Huan-jun, et al(杨玉惠,詹义强,丁焕军,徐 健,等). Chin J. Lumin.(发光学报), 2003, 24(6): 583. [2] LI Jie, ZHOU He-feng, HAO Yu-ying, et al(李 洁,周禾丰,郝玉英,等). Spectroscopy and SpectralAnalysis(光谱学与光谱分析), 2006, 26(2): 235. [3] Tang C W, Van Slyke S A. Appl. Phys. Lett., 1987, 51(12): 913. [4] Yuji Hamada, Takeshi Sano, Masayuki Fujita, et al. Japanese Journal Applied Physics,part 2-letters, 1993, 32(4A): L511. [5] YU Gui, LIU Yun-qi, SONG Ya-ru, et al. Synthetic Metals, 2001, 117(1-3): 211. [6] HAO Yu-ying, GAO Zhi-xiang, WANG Hua, et al(郝玉英,高志翔,王 华,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(3): 491. [7] HAO Yu-ying, LI Jie, GAO Zhi-xiang, et al(郝玉英,李 洁,高志翔,等). Chinese Journal of Luminescence(发光学报), 2006, 27: 254. [8] FANG Rong-chuan(方容川). Solid State Spectroscopy(固体光谱学). Hefei: University of Science and Technology of China Press(合肥:中国科技大学出版社), 2001. 58. [9] HAO Yu-ying, HAO Hai-tao, WANG Hua, et al(郝玉英,郝海涛,王 华,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2004, 24(12): 1524.