Abstract：Green light-emitting Ca3Mg3Si4O14∶Eu2+ phosphors were prepared by solid-state reaction using CaCO3, MgO, SiO2 and Eu2O3 as raw materials. The effects of Eu-doping concentration and fluxes (NH4Cl, BaF2) on the crystal structure, luminescence property, and thermal stability of phosphor were studied, which were characterizes by X-ray diffraction (XRD), and photoluminescence (PL) spectra, respectively. The XRD results show that the crystal structure of Ca3Mg3Si4O14∶Eu2+ is consistent with the calculated patterns, which investigated the crystal structure of the compound Ca3Mg3Si4O14∶Eu2+. The phosphor has strong excitation around 360～450 nm and exhibits a broad emission band with a maximum at 530 nm under 440 nm excitation. With the increase of Eu2+ concentration, the phosphor shows a red-shift and the quenching concentration of Eu2+ is about 6%. With the introduction of NH4Cl and BaF2 as fluxes, the luminous intensity of Ca3Mg3Si4O14∶Eu2+ phosphor has been improved. Compared with the luminescence intensity of Ca3Mg3Si4O14∶Eu2+phosphor without flux, the photoluminescence intensity increased by 70% when adding NH4Cl as flux. Furthermore, the emission intensity reduced by only 7.6% and 14% at 150 ℃ for Ca3Mg3Si4O14∶Eu2+ phosphor and commercial green phosphor. The Ca3Mg3Si4O14∶Eu2+ phosphor also possesses high thermal stability, and these luminescnce properties indicate that Ca3Mg3Si4O14∶Eu2+ phosphor is a promising green phosphor for use in solid-state white lighting.
基金资助: National Natural Science Foundation of China (61405183, 61575182), National Key R&D Plan (2017YFB0403105), Natural Science Foundation of Zhejiang Province (LY16F050004), Application Research Program of Commonweal Technology of Zhejiang Province (2015C31102)
通讯作者:
王 乐
E-mail: calla@cjlu.edu.cn
作者简介: PAN Hua-yan, (1992—), female, graduate student of China Jiliang University e-mail:
1443515959@qq.com
引用本文:
潘桦滟，王 乐，李旸晖，吴 拓，罗 东. 一种新型Ca3Mg3Si4O14∶Eu2+绿色荧光粉的制备及其性能研究[J]. 光谱学与光谱分析, 2017, 37(08): 2627-2631.
PAN Hua-yan, WANG Le, LI Yang-hui, WU Tuo, LUO Dong. Preparation and Luminescence Properties of a New Green Emitting Ca3Mg3Si4O14∶Eu2+ Phosphor. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(08): 2627-2631.
[1] Wang L, Zhang H, Wang X J, et al. Physical Chemistry Chemical Physics, 2015, 17(24).
[2] Guanghao L, Jingjing C, Zhiyong M, et al. Ceramics International, 2016, 42: 1756.
[3] Jin Zhouwei, Wu Yuyu, Wu Zhen, et al. Optics Communications, 2014, 322: 224.
[4] Yu X, Zhang L, Xu X, et al. Journal of luminescence, 2014, 145: 114.
[5] He Zhen, Huang Xuefei, Zhou Rendi, et al. Journal of Alloys and Compounds，2016, 658: 36.
[6] Li Xucheng, Zhang Rongfen, Cui Ruirui, et al. Journal of Alloys and Compounds 2015, 650: 470.
[7] Zhang Mei, He Xin, Luo Jianyi, et al. Materials Chemistry and Physics 2014, 147: 968.
[8] Li C, Chen H, Xu S. Optik-International Journal for Light and Electron Optics, 2015, 126(5): 499.
[9] Zhu Yanan, Pang Zengyuan, Wang Jian, et al. Journal of Rare Earths, 2016, 34(5): 483.
[10] Yoon S, Bierwagen J, Trottmann M, et al. Journal of Luminescence, 2015, 167(1): 126.
[11] Wang L, Zhang H, Wang X J, et al. Physical Chemistry Chemical Physics, 2015, 17(24).
[12] Van Uitert L. J. Electrochem. Soc., 1967，114(10)： 1048.
[13] He Z, Huang X, Zhou R, et al. Journal of Alloys & Compounds, 2015, 658: 36.
[14] Khanna A, Dutta P S. Optical Materials 2014, 17: 646.