Abstract:The composition and structure evolution of carbon nanotube (CNT)/silica xerogel composites during the process of laser irradiation was traced by infrared (IR) spectra, Raman spectra, transmission electronic microscope (TEM) and pore structure analysis. The results of IR and Raman spectra show that during the process of laser irradiation the compositions of the composites do not make any noteworthy changes, while the matrix silica network becomes perfect and the doped CNTs become more graphitized. TEM images and pore structure analysis show that the SiO2 granules and the corresponding pore size increase after laser irradiation.
[1] Iijima S. Nature, 1991, 354: 56. [2] Tanaka K, Yamabe T, Fukui K. The Science and Technology of Carbon Nanotubes. Elsevier, Amsterdam, 1999. [3] Thostenson T E, Ren Z F, Chou T W. Composites Science and Technonlgy, 2001, 61: 1899. [4] CHENG Hui-ming(成会明). Preparation, Structure, Property and Application of Carbon Nanotubes(纳米碳管制备、结构、物性及应用). Beijing: Chemical Industry Publishing Company(北京:化学工业出版社), 2002. [5] Ebbesen T W, Lezec H J, Hiura H, et al. Nature, 1996, 382(6586): 54. [6] Collins P G, Bradley K, Ishigami M. Science, 2000, 287: 1801. [7] WU Xiao-li, YUE Tao, LU Rong-rong, et al(吴小利,岳 涛,陆荣荣,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2005,25(10):1595. [8] Wan Xianggan, Dong Jinming. Physical Review B, 1998, 58(11): 6756. [9] Milosevic I, Vukovic T, Dmitrovic S, et al. Physica E, 2002, 12: 745. [10] Sun X, Yu R Q, Xu G Q, et al. Applied Physics Letters, 1998, 73(25): 3636. [11] Vivien L, Anglarel E, Riehl D, et al. Chemical Physics Letter, 1999, 312: 317. [12] Zhan Hongbin, Chen Wenzhe, Wang Minquan, et al. Chemical Physics Letter, 2003, 382(3-4): 313. [13] Venkateswara Bao A, Wagh P B, Haranath D, et al. Ceramics International, 1999, 25: 505. [14] WANG Yu-fang, CAO Xun-wei, LAN Guo-xiang(王玉芳,曹学伟,蓝国祥). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2000,20(2): 180.