Abstract：The preparation of P(o-MAABA) via ATRP and the composite of P(o-MAABA)/ZnO nanoparticles were described. 1H NMR, IR, TA and TEM were utilized to confirm the results. 1H NMR indicates that the structure of the P(o-MAABA) was definite, and the molecule weight of P(o-MAABA) was 7 900. IR shows that ZnO nanoparticles were introduced to P(o-MAABA) and were interacted with the reactive groups of polymer. TA shows that the heat stability of P(o-MAABA))/ZnO composite increased greatly. TEM photo demonstrates that the composite was spherical and the surface was smooth. The P(o-MAABA)/ZnO composite exhibits particular fluorescence property, and the emission spectrum of the P(o-MAABA)/ZnO composite red shifts 25 nm compared to the polymer. In addition, the composite features good solubility and film formability, and may become a new optical material.
[1] ZHANG Li-de, MOU Ji-mei(张立德, 牟季美). Science of Nanophase Materials(纳米材料科学). Shenyang: Liaoning Scientific and Technical Press(沈阳: 辽宁科技出版社), 1994. [2] LIU Chao-feng, SUN Yu-qing, ZU Yong(刘超锋, 孙玉晴, 祖 庸). New Material of Chemical Industry(化工新型材料), 1995, 23(11): 13. [3] ZU Yong, LEI Yan-ying, WANG Xun(祖 庸, 雷闫盈, 王 训). New Material of Chemical Industry(化工新型材料), 1999, 27(3): 14. [4] YU Hai-yin, DU Jun, GU Jia-shan, et al(宇海银, 杜 俊, 顾家山, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2004, 24(2): 177. [5] Liu Y, Wang L X, Pan C Y. Macromolecules, 1999, 32: 8301. [6] Cheng G, Simon P F W, Hartenstein M, et al. Macromol Rapid Commun, 2000, 21: 846. [7] Viktor K, Bogdan Z, Lgor L. Polymer Preprints, 2002, 44(1): 538.