Abstract:Chiral isotropy material should be obtained in order to manufacture chiral optical waveguide. In the present paper, a chiral crystal of NaClO3 was grown from water solution by standard rocking techniques. Crystal incising and optical polishing were done and a transparent 10.9 mm× 8.2 mm× 4.7 mm crystal NaClO3 was obtained. Along the six directions perpendicular to the surface of the crystal NaClO3, its circular dichroism and UV spectra were collected, and at the same time its optical rotatory dispersion was measured by a self-fabricated ORD apparatus. It was approved by our experiment that the CD, UV spectrum and the optical rotatory dispersion of the crystal NaClO3 were isotropic, which is not the same as those of quartz.
陶卫东1,3, 章 慧2, 方雪明2, 王 芳2, 张子方2, 白贵儒1 . 氯酸钠晶体的CD光谱及ORD特性研究[J]. 光谱学与光谱分析, 2006, 26(01): 134-136.
TAO Wei-dong1,3, ZHANG Hui2, FANG Xue-ming2, WANG Fang2, ZHANG Zi-fang2, BAI Gui-ru1 . Study on the CD and ORD of the Crystal NaClO3. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(01): 134-136.
[1] Cory H. J. Electromagn. Wave Appl., 1995, 9(5-6): 805. [2] Viitanen A J. IEEE Trans. Microwave Theory Tech., 2000, 48(6): 1077. [3] Mazur J, Mrozowski M, Okoniewski M. J. Electromagn. Wave Appl., 1992, 6(5/6): 641. [4] Qiu R C, Lu I T, IEE Pro. Optoelectron, 1998, 145(3): 155. [5] Zhang K, Xiao J. Int. J. Infrared Millim. Waves, 1998, 19(10): 1439. [6] Tao Wei-dong, Xia Hai-ping, Dong Jian-feng, et al. Chinese Physics, 2003, 12(6): 639. [7] TAO Wei-dong, DONG Jian-feng, XIA Hai-ping, et al.(陶卫东, 董建峰, 夏海平, 等). Acta Phys. Sin.,(物理学报), 2004, 53(3): 891. [8] Simon H J, Bloembergen N. Physical Review, 1968, 171(3): 1104.