Color Mechanism Analysis During Blended Spinning of Viscose Fibers Based on Spectral Characteristics
CUI Xiang-yu1, 3, CHENG Lu1, 2, 3*, YANG Yue-ru1, WU Yan-feng1, XIA Xin1, 3, LI Yong-gui2
1. College of Textiles and Fashion, Xinjiang University, Urumqi 830017, China
2. Fujian Key Laboratory of Novel Functional Textile Fibers and Materials, Minjiang University, Fuzhou 350108, China
3. College of Textiles, Donghua University, Shanghai 201620, China
Abstract：Aiming at the ambiguity in explaining the color mechanism of fiber aggregates by the existing color-spinning color matching models, the color change mechanism of dope dyed viscose fiber aggregates during spinning was explored. In the experiment, 36 groups of sliver andyarn samples with different color mixing ratios were spun, and the Euclidean distance and spectral angular distance were used to quantify the spectral amplitude difference and shape difference between the fiber aggregates of different states in each group. The chromatic aberration, which was calculated based on the CMC(2∶1) formula was evaluated as a control, and the quantified spectral difference and chromatic aberration were compared horizontally based on the discrepancy criterion based on the category separable ratio (CSR) formula. Among them, between the raw sliver and the drawn sliver, the mean values of CSRED and CSREcmc of the samples were 2.87 and 2.17, the dED of the sample is similar to the performance of ΔEcmc, and the spectral radiation difference is more stable than the color difference. Between the sliver and the yarn, the dED and Ecmc have the same trend of greater changes, and all the samples CSRED and CSREcmc are greater than 1; in the above process, the shape difference of the sample spectrum keeps a small scale, before and after drawing and spinning, there are 20 and 22 samples corresponding to CSRSAD>1, and their mean values are 1.69 and 1.60, respectively, which did not change significantly with processing. It can be concluded that during the spinning process, due to the remodeling of fiber arrangement and aggregation state, the amount of reflected light(brightness) tends to decrease, and the spinning stage is the main stage of change, while the light quality(hue) not significantly changed during this process. Further, according to the light reflection theory of the fiber, that is, the amount of the reflected light of the fiber is mainly affected by the externally reflected light, and the chromaticity is mainly affected by the internally reflected light. It can be concluded that the spinning process mainly affects the external reflected light of the fiber. However, it has little explanatory power for internally reflected light. On the other hand, it also verified the ability of the SAD-ED formula, which integrates spectral amplitude and shape features, to characterize the color difference of colored yarns. CSRSAD-ED can distinguish 31 groups of sliver and drawn sliver samples and can distinguish all drawn sliver and yarn samples, this formula shows more sensitive and stable than the CMC(2∶1) formula, which is the color difference. This scheme also provides a new idea for the color evaluation of colored yarns.
Key words：Color spinning; Process chromatic aberration; Spectral characteristics; European distance; Spectral angular distance
崔翔宇，程 璐，杨月茹，吴艳丰，夏 鑫，李永贵. 基于光谱特征的粘胶纤维混色纺纱过程呈色机理分析[J]. 光谱学与光谱分析, 2023, 43(12): 3916-3923.
CUI Xiang-yu, CHENG Lu, YANG Yue-ru, WU Yan-feng, XIA Xin, LI Yong-gui. Color Mechanism Analysis During Blended Spinning of Viscose Fibers Based on Spectral Characteristics. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3916-3923.
[1] Yang R H, Pan B, Zhang K L, et al. Cellulose, 2021, 28(15): 10039.
[2] Zhang G, Pan R R, Zhou J, et al. Textile Research Journal, 2022, 92(15-16): 2569.
[3] Yang R H, Zhang K L, Wang Z. Fiber Polym, 2022, 23(4): 1018.
[4] Zhang G, Zhou J, Pan R R, et al. Fiber Polym, 2021, 22(2): 412.
[5] Zhu W J, Li Q Z, Zhang F Y, et al. Journal of Fiber Science and Technology, 2020, 76(10): 335.
[6] WANG Yu-juan，WANG Jun（王玉娟，汪 军）. Journal of Textile Research（纺织学报）, 2021, 42(2): 156.
[7] YUAN Li, XIONG Ying, GU Qian, et al（袁 理，熊 莹，谷 迁，等）. Journal of Textile Research（纺织学报）, 2021, 42(5): 122.
[8] YUAN Li, WANG Dan-shu, GU Qian, et al（袁 理，王丹书，谷 迁，等）. Journal of Textile Research（纺织学报）, 2019, 40(2): 30.
[9] YU Wei-dong, CHU Cai-yuan（于伟东，储才元）. Textile Physics（纺织物理）. Shanghai: Donghua University Press（上海：东华大学出版社）, 2009. 169.
[10] LI Dong-gao, JIANG Hui-jun（李栋高，蒋蕙钧）. Journal of Textile Research（纺织学报）, 1980，(3): 1.
[11] CUI Xiang-yu, XIA Xin, YANG Yue-ru, et al（崔翔宇，夏 鑫，杨月茹，等）. Cotton Textile Technology（棉纺织技术）, 2020, 48(11): 78.
[12] GAO Xiao-jie, JIAN Ji, DAI Xiao-ai, et al（高孝杰，简 季，戴晓爱，等）. Geomatics and Information Science of Wuhan University[武汉大学学报（信息科学版）], 2016, 41(3): 408.
[13] PENG Qing-qing, CHEN Song-chao, ZHOU Ming-hua, et al（彭青青，陈颂超，周明华，等）. Spectroscopy and Spectral Analysis（光谱学与光谱分析）, 2022, 42(5): 1614.
[14] ZHAO Chun-hua, TIAN Ming-hua, LI Jia-wei（赵春晖，田明华，李佳伟）. Journal of Harbin Engineering University（哈尔滨工程大学学报）, 2017, 38(8): 1179.
[15] SUN Yan-li, ZHANG Xia, SHUAI Tong, et al（孙艳丽，张 霞，帅 通，等）. Journal of Remote Sensing（遥感学报）, 2015, 19(4): 618.
[16] ZHAO Heng-qian, ZHAO Xue-sheng, CEN Yi, et al（赵恒谦，赵学胜，岑 奕，等）. Spectroscopy and Spectral Analysis（光谱学与光谱分析）, 2017, 37(3): 869.